Unlock instant, AI-driven research and patent intelligence for your innovation.

Self adhesive and high molecule self adhesive water-proof coil and producing process

A self-adhesive waterproof membrane and manufacturing process technology, applied in the directions of adhesives, adhesive types, asphalt material adhesives, etc., can solve the problems of complex process, large shrinkage of the carcass, difficult to dissolve, etc., and achieve a simple compounding process. , Easy to mix and modify, enhance the effect of adsorption

Inactive Publication Date: 2012-05-02
珠海华兴防水科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] (1) The preparation of this kind of self-adhesive requires a high temperature of 180 ° C to 200 ° C, which can cause some plasticizers to overheat and oxidize; when the asphalt is 190 ° C to 200 ° C, a large amount of asphalt fume will pollute the environment, and the cost of asphalt fume treatment is high. , long preparation time and high energy consumption
[0010] (2) Since thermoplastic elastomers are difficult to dissolve in asphalt, they need to be ground by a colloid mill to achieve the purpose of blending. Generally, they need to be stirred and ground for about 3.5 hours, and the energy consumption is too large
[0011] (3) The molding temperature is high, the carcass shrinks greatly (about 1%), the process is complicated, and the energy consumption is high
[0012] (4) When polymer materials are used as the main material layer, this process cannot be used for manufacturing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Self adhesive and high molecule self adhesive water-proof coil and producing process
  • Self adhesive and high molecule self adhesive water-proof coil and producing process
  • Self adhesive and high molecule self adhesive water-proof coil and producing process

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0061] Specific embodiment 1: self-adhesive glue, this self-adhesive glue is made up of asphalt, SBS rubber, tackifier, SIS rubber, maleic anhydride, aluminum chloride, thiuram, magnesium oxide, calcium silicate. The selected materials are as follows:

[0062] Select No. 90 high-quality heavy traffic asphalt produced by Maoming Petrochemical Company, SBS 792 produced by Yueyang Petrochemical Company Rubber Factory, Kraton SIS 1105, tackifier produced by Maoming Petrochemical Plant, maleic anhydride, aluminum trichloride, thiuram, oxidized Magnesium, calcium silicate. Put it into the mixing tank successively, and grind it fully for later use.

[0063] The proportioning examples of each component by weight ratio are as follows:

[0064]

[0065]

[0066] The self-adhesive adhesive obtained by using the ratio method 4, the ratio method 5 and the ratio method 6 has better performance.

[0067] Such as figure 1 As shown, a polymer self-adhesive waterproof membrane is mad...

specific Embodiment 2

[0076] Specific embodiment 2: as figure 2 As shown, a polymer self-adhesive waterproof roll material, which is made of the self-adhesive of specific embodiment 1, consists of a main material layer 1, two self-adhesive layers 3 made of self-adhesive, two isolation layers 4 composition. Two layers of self-adhesive layers are respectively compounded on the upper and lower surfaces of the main material layer, and two layers of isolation layers are respectively compounded on the outer surfaces of the two self-adhesive layers; the main material layer is composed of a synthetic resin sheet with a reinforcing material layer or a The fiber reinforced material layer consists of synthetic rubber sheets. Both outer surfaces of the body material layer have layers of fiber reinforcement material 2 .

[0077] Such as Figure 4 As shown, the main body material layer can also be made of a synthetic resin sheet or a synthetic rubber sheet, and the surface of the synthetic resin sheet or the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The self adhesive consists of cross-linked asphalt, SBS rubber and tackifier, as well as SIS rubber, maleic anhydride, aluminum trichloride, thiram, magnesium chloride and calcium silicate. The self adhesive is cpddd with chemically modified cross-linked asphalt as main material at 150-170 deg.c, and has less pollution and low power consumption. It may be adhered to plasma modified polymer material and wet concrete. The present invention also discloses one kind of self adhering waterproof polymer coil made with the self adhesive and its production process, and the self adhering waterproof polymer coil has high adhesion strength between the adhesive and the main material layer.

Description

technical field [0001] The present invention relates to a self-adhesive, and also relates to a polymer self-adhesive waterproof roll made of the self-adhesive, and a manufacturing process thereof. Background technique [0002] Synthetic polymer waterproof membranes (including synthetic resin sheets and synthetic rubber membranes) have good physical properties, but because their surfaces are not easily bonded, they cannot achieve the ideal application effect. Therefore, the market share of such waterproofing membranes has been very small. Some people try to cold-coat a layer of double-sided self-adhesive membrane on the surface of the polymer membrane, but it is easily peeled off; The surface of the surface is difficult to bond, and the test did not take measures to treat the surface of the polymer coil. In addition, the self-adhesive does not match, so the effect is almost the same as the former. It can be seen that the technology of attempting to coat one deck of self-adh...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09K3/18C09J7/02C09J195/00
Inventor 秦雪辰
Owner 珠海华兴防水科技有限公司