Production art work of cellular catalyst carrier using natural zeolite as principal raw material

The invention relates to a honeycomb catalyst and a manufacturing process technology, which is used in the chemical production of inorganic and solid materials, and the production process of high-efficiency honeycomb catalyst carriers, and can solve the problems affecting the use effect and life, the alumina coating is easy to peel off, and the production cost is high. , to achieve the effect of improving catalytic conversion rate, large specific surface area of ​​finished products, and high specific surface area

Inactive Publication Date: 2007-02-28
胡琳
View PDF2 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The cordierite (Mg 2 Al 4 Si 5 o 18 ) to make a honeycomb catalyst carrier, both of which are two-step production methods. Not only the process is

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0020] Example 1

[0021] Take 30kg of 200 mesh zeolite powder treated with dilute hydrochloric acid with a molar concentration of 2.5mol / L, put it into the mixer, start the mixer and add 15kg clay, 4kg mixed rare earth oxide, 2kg methylcellulose and 2kg water in sequence, and mix thoroughly Evenly. The mixture is put into a vacuum kneader, kneaded repeatedly and then put into a mold and extruded into a honeycomb shape. Put the formed honeycomb body into an activation furnace, raise the temperature to 100°C at a heating rate of 5°C / min and keep the furnace temperature for 3 hours. After it is baked and dry, the furnace temperature is slowly increased to 600°C and kept at a constant temperature for 4 hours , And then cooled to room temperature to obtain a yellowish honeycomb carrier. Measure the various indexes of the product, and the external dimension is 50×50×50mm 3 , The hole diameter is 1.5mm, and the hole density is 27 pcs / cm 2 , The pore wall thickness is 0.35~0.40mm, the fr...

Example Embodiment

[0022] Example 2 /

[0023] The same operation as in Example 1 was used, except that the baking temperature was controlled at 200°C for 2 hours. Finally, the various indicators of the product are measured, and the data parameters obtained are within the control range.

Example Embodiment

[0024] Example 3

[0025] The same operation as in Example 1 was used, except that the ratio of each component was adjusted. Take 40 kg of 200 mesh zeolite powder treated with dilute hydrochloric acid, 10 kg of pottery clay, 3 kg of mixed rare earth oxides, 2 kg of methyl cellulose and water each. Finally, the various indicators of the product are measured, and the data parameters obtained are within the control range.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Specific surface areaaaaaaaaaaa
Thermal expansion coefficientaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparing craft of high-effective honeycomb catalyst carrier, which comprises the following steps: grinding natural zeolite into powder bulk, injecting in the dilute hydrochloric acid to stir evenly, stewing, bleaching the zeolite to neutral through water, adding pottery clay, composite rare earth oxide and cellulose methyl in the zeolite powder, blending evenly in the vacuum pitching machine, squeezing to obtain the honeycomb semi-conductor, placing the honeycomb semi-conductor in the activated furnace, drying at low temperature, heating to 500-600deg.c, cooling to obtain the product.

Description

technical field [0001] The invention relates to a manufacturing process of a high-efficiency honeycomb catalyst carrier, in particular to a manufacturing process of a honeycomb catalyst carrier with natural zeolite as the main raw material, and belongs to the technical field of manufacturing inorganic and solid material chemistry. Background technique [0002] The catalyst carrier is the support of the catalyst material. The catalyst material is coated on its surface and together with the catalyst to form various catalytic devices, which are widely used in chemical industry, environmental protection, thermal power generation and other industries, such as automobile exhaust purifier. In order to improve the performance of the catalyst, the specific surface area of ​​the carrier must be enlarged, usually made into a honeycomb shape. [0003] At present, most of the honeycomb catalyst supports commonly used in the market are based on cordierite (Mg 2 Al 4 Si 5 o 18 ) as the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J29/06B01J35/04
Inventor 胡琳胡珺
Owner 胡琳
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products