Preparing method of coated aluminium powder pigment

A coating type, aluminum powder technology, applied in the direction of fibrous filler, dyed organosilicon compound treatment, etc., can solve the problems of aluminum powder pigment failure, protective layer falling off, protective effect, etc., to achieve good metallic luster, good resistance The effect of acid-base and water resistance, good compatibility

Inactive Publication Date: 2007-06-27
SOUTH CHINA UNIV OF TECH
View PDF0 Cites 77 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing coating technology is difficult to form a dense protective layer on the surface of the aluminum powder pigment or the protective layer is easy to fall off from the surface of the aluminum powder pigment, which does not have a good protective effect on the aluminum powder pigment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] In the first step, in parts by mass, 2 parts of aluminum powder pigment and 50 parts of solvent methanol are added to the reaction vessel, and stirred at room temperature for 0.5 hours;

[0029] In the second step, add 1 part of aminopropyltriethoxysilane, 4 parts of water, and 2 parts of acidic catalyst hydrochloric acid into the reaction vessel described in the first step, heat in a water bath, and react for 2 hours under stirring. The reaction temperature is 30 ° C. The pH value is 5, and the aluminum powder pigment initially coated with organosiloxane is obtained;

[0030] The third step is to raise the temperature of the reaction system described in the second step to 65°C, add 3 parts of styrene, 0.01 part of initiator azobisisobutyronitrile, and react for 2 hours under stirring to obtain organosiloxane and polymer coating Aluminum powder pigment;

[0031] The fourth step is to cool the aluminum powder pigment suspension obtained in the third step to room tempera...

Embodiment 2

[0033] In the first step, in parts by mass, 6 parts of aluminum powder pigment and 70 parts of solvent ethanol are added to the reaction vessel, and stirred at room temperature for 1 hour;

[0034] In the second step, add 5.5 parts of tetraethoxysilane, 9.5 parts of water, and 5 parts of acid catalyst sulfuric acid into the reaction vessel described in the first step, heat it in a water bath, and react for 6 hours under stirring. The reaction temperature is 45 °C and the pH value is 4. Obtain the aluminum powder pigment initially coated with organosiloxane;

[0035] In the third step, the temperature of the reaction system described in the second step is raised to 92.5°C, 5 parts of styrene, 6.5 parts of divinylbenzene, and 4.005 parts of initiator potassium persulfate are added, and the reaction is carried out under stirring for 6 hours to obtain organosiloxane and Polymer-coated aluminum powder pigments;

[0036] The fourth step is to cool the aluminum powder pigment suspen...

Embodiment 3

[0038] In the first step, in parts by mass, 10 parts of aluminum powder pigment and 90 parts of solvent propanol are added to the reaction vessel, and stirred at room temperature for 2 hours;

[0039] In the second step, add 6 parts of epoxytrimethoxysilane, 10 parts of water, and 8 parts of acidic catalyst hydrofluoric acid into the reaction vessel described in the first step, heat in a water bath, and react for 10 hours under stirring, and the reaction temperature is 60°C , the pH value is 6, and the aluminum powder pigment initially coated with organosiloxane is obtained;

[0040] In the third step, the temperature of the reaction system described in the second step is raised to 120°C, 5 parts of methyl methacrylate, 5 parts of butyl methacrylate and 10 parts of methyl acrylate, and 8 parts of initiator ammonium persulfate are added, and stirred React for 10 hours to obtain the aluminum powder pigment coated with organosiloxane and polymer;

[0041] The fourth step is to coo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention is coated aluminum powder pigment and its preparation process. The coated aluminum powder pigment is prepared through the following steps: mixing aluminum powder pigment with alcohol solvent; adding organosiloxane, water and acid catalyst, and heating in water bath to react to obtain organosiloxane coated aluminum powder pigment; heating the reaction system to 65-120 deg.c, adding polymer monomer and initiator to react to obtain organosiloxane and polymer coated aluminum powder pigment; and cooling, filtering, washing and drying to obtain the coated aluminum powder pigment product. The coated aluminum powder pigment with two coating layers has excellent metal luster and high acid and alkali resistance, and is suitable for water paint.

Description

technical field [0001] The invention relates to the technical field of surface treatment of metal pigments, in particular to a method for preparing coated aluminum powder pigments. Background technique [0002] Aluminum powder pigment is one of the important metal pigments, the main application areas are industrial coatings, automotive coatings, printing inks and plastic processing industry. The reason why aluminum powder pigments have many application fields is that they have characteristics different from other pigments: (1) "angle-dependent" effect or "two-color" effect. That is, when the coating containing aluminum powder is observed from different angles, the color of the coating will change with the angle. The coating color is very bright when viewed from the front and darkens when viewed from the side. Aluminum powder pigments are widely used in decorative paints because of this effect. (2) Aluminum powder pigments have good ability to reflect light and reflect hea...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09C1/64C09C3/12
Inventor 皮丕辉李利君文秀芳程江杨卓如
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com