High-temperature-resisting conveyer belt

A conveyor belt and high-temperature-resistant technology, which is applied in the field of cement clinker operation transportation, high-temperature sintered ore, and high-temperature-resistant conveyor belts, can solve the problems of low-efficiency high-temperature material transportation, achieve excellent wear resistance, excellent heat resistance, The effect of delaying cracking

Active Publication Date: 2007-09-05
WUXI BOTON CONVEYOR SOLUTION CO LTD
View PDF0 Cites 66 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to overcome the above disadvantages, thereby providing a high temperature resistant conveyor belt, which has excellent heat aging resistance, excellent crack aging resistance, excellent wear resistance, and can significantly improve the use of high temperature belts. Long life and avoid environmental pollution caused by the conveyor belt on the job site, meet the transportation requirements of high-temperature materials in the steel, cement and other industries, and solve the big problem of low-efficiency high-temperature material transportation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-temperature-resisting conveyer belt

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Embodiment 1: The production process of the high temperature resistant conveyor belt of the present invention is as follows:

[0028] The high-temperature-resistant conveyor belt of the present invention adopts a canvas with a core tensile body between the covering rubber of the working surface and the covering rubber of the non-working surface, and they are firmly combined into a whole through molding and vulcanization processes.

[0029] Its composition and proportioning of the working face covering glue described in the embodiments of the present invention are in parts:

[0030] 1. Rubber mixing process:

[0031] a. One stage mixing process:

[0032] Add 100 parts of binary ethylene propylene rubber to the internal mixer for pre-compression mixing, mixing time: 28-32 seconds; add fine materials: thermal conductive agent, 10 parts of zinc oxide, anti-aging agent 1: RD, scientific name: 2,2 , 4-trimethyl-1,2-dihydroquinoline polymer: 2 parts, anti-aging agent 2: 1010...

Embodiment 2

[0045] Its composition and proportioning of the working face covering glue described in the embodiments of the present invention are in parts:

[0046] The present invention gets binary ethylene propylene glue: 90 parts;

[0047] EPDM rubber: 10 parts;

[0048] Cross-linking agent, DCP-40: 7 parts;

[0049] Auxiliary cross-linking agent, TAIC: 2.0 parts;

[0050] Heat conduction agent zinc oxide: 15 parts;

[0051] Reinforcing agent 1, N330: 30 parts;

[0052] Reinforcing agent 2, N550: 30 parts;

[0053] Softener 1, paraffin oil, SUNPAR2280: 30 parts;

[0054] Softener 2, liquid ethylene propylene rubber: 10 parts;

[0055] Aramid staple fiber: 6.5 parts;

[0056] Antiaging agent 1, RD: 2 parts;

[0057] Antiager 2, 1010: 2 parts.

[0058] The above formula is made into the working surface covering rubber according to the process steps in the first implementation, and a tensile canvas with a core is provided between the working surface covering rubber and the non-wor...

Embodiment 3

[0060] Its composition and proportioning of the working face covering glue described in the embodiments of the present invention are in parts:

[0061] Binary ethylene propylene rubber: 80 parts;

[0062] EPDM rubber: 20 parts;

[0063] Cross-linking agent, DCP-40: 6.6 parts;

[0064] Auxiliary cross-linking agent, TAIC: 2.0 parts;

[0065] Heat conduction agent zinc oxide: 22 parts;

[0066] Reinforcing agent 1, N330: 35 parts;

[0067] Reinforcing agent 2, N550: 25 parts;

[0068] Softener 1, SUNPAR2280: 20 parts;

[0069] Softener 2, liquid ethylene propylene rubber: 16 parts;

[0070] Aramid staple fiber: 8 parts;

[0071] Antiaging agent 1, RD: 2 parts;

[0072] Antiager 2, 1010: 2 parts.

[0073] The above formula is made into the working surface covering glue according to the process steps in the first implementation, and a tensile canvas with a core is provided between the working surface covering glue and the non-working surface covering glue, and they are fi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

A refractory conveying belt is prepared from the dibasic ethylene propylene rubber, or dibasic ethylene propylene rubber and ternary ethylene propylene rubber through pre-pugging, adding heat conducting agent and anti-ageing agent, pugging, adding reinforcing agent, softening agent and short aramid fibers, pugging, adding cross-linking agent and cross-linking aid, heating, calendering to become sheet, attaching it onto tension-resistant canvas, rolling and sulfurizing.

Description

technical field [0001] The invention relates to a high-temperature-resistant conveyor belt, which is specifically used in industries such as iron and steel, cement, and high-temperature sintered ore and cement clinker for operation and transportation, and belongs to the technical field of rubber products. Background technique [0002] At present, in the iron and steel, cement and other industries, the operation and transportation of high-temperature sintered ore and cement clinker are completed through high-temperature resistant conveyor belts. The high-temperature-resistant conveyor belt working surface covering rubber is mainly gradually added in batches on the internal mixer by using EPDM rubber, halogenated butyl rubber, styrene-butadiene rubber and cross-linking agent, reinforcing agent, softener and anti-aging agent. Through one-stage and two-stage mixing, it is processed into two-stage compound rubber (or final compound rubber), and the final compound rubber is formed...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B65G15/30B29D29/00B29B7/00B29C70/02C08L23/16C08K5/3437C08K5/14C08K3/22C08K3/04C08K5/21
Inventor 陶小明包志方
Owner WUXI BOTON CONVEYOR SOLUTION CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap