Method of preparing thin crystal composite layer on magnesium alloy surface

A magnesium alloy and composite layer technology, applied in metal processing equipment, manufacturing tools, welding equipment, etc., can solve the problems of magnesium alloy surface oxidation, high energy consumption, complex process, etc., to refine grains and improve wear resistance. , the effect of simple process

Inactive Publication Date: 2007-10-24
LANZHOU UNIVERSITY OF TECHNOLOGY
View PDF1 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantage of this technology is that the energy consumption is large, the process is relatively complicated, and it is easy to oxidize the surface of the magnesium alloy.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method of preparing thin crystal composite layer on magnesium alloy surface
  • Method of preparing thin crystal composite layer on magnesium alloy surface

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0007] The invention relates to a method for preparing a fine-grained composite layer on the surface of a magnesium alloy. A magnesium alloy formed by casting or a semi-solid formed magnesium alloy is used. First, the surface of the magnesium alloy is polished, and grooves are opened on the surface of the magnesium alloy. The grooves are filled with powdered Al+SiC, and then friction stir processing is performed to form a fine-grained composite structure on the surface of the magnesium alloy.

[0008] The AZ91D magnesium alloy obtained by metal mold casting is firstly polished on the surface of the magnesium alloy, and a friction stirring head with a shaft shoulder diameter of 18 mm, a stirring pin diameter of 6 mm, and a height of 4 mm is selected. Dig 4.2mm deep, 1mm wide, and 5mm-spaced grooves on the surface of the magnesium alloy, and evenly fill them with Al+SiC powder. Install it on the friction stir welding machine and process it under specific welding parameters. The ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparing method of composite fine-grained layer on the surface of magnesium alloy, which is characterized by the following: adopting casting shaping magnesium alloy or semi-solid pattern as raw material; sanding the surface of magnesium alloy; opening groove on the surface of magnesium alloy; filling powder-shaped Al+SiC in the groove; stirring the surface; forming the fine-grained layer with high antirusting and anti-abrasion resistance.

Description

technical field [0001] The invention belongs to the technical field of surface modification, and relates to surface refinement and improvement of surface corrosion resistance and wear resistance. Background technique [0002] The invention patent "SiC+Al surfacing method on magnesium alloy surface" (application number 200410089271.5) discloses a SiC+Al surfacing method on magnesium alloy surface. The surface of the magnesium alloy workpiece is polished with sandpaper to remove oxides, and then rinsed with alcohol. Dry in the air; mix SiC and Al powder according to particle size and volume ratio SiC / Al, add binder, stir evenly, and make coating material; apply the prepared coating material evenly on the magnesium alloy workpiece surface, and then dry the coated magnesium alloy workpiece; carry out inert gas shielded tungsten arc surfacing remelting treatment on the surface of the coated magnesium alloy workpiece, adjust the welding current, welding speed and welding torch ang...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23C24/02B23K20/12
Inventor 陈体军朱战民郝远马颖
Owner LANZHOU UNIVERSITY OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap