Method for raising common steel antibiotic and rust resisting performance

A technology of anti-rust performance and common steel, applied in the field of improving the anti-bacterial and anti-rust performance of common steel and surface treatment, it can solve the problems of weak bonding force between the protective film and the substrate, unable to improve the anti-bacterial property of common steel, easy to fall off, etc., to achieve adhesion Good, strong environmental protection, high bonding strength effect

Inactive Publication Date: 2007-11-07
SHANGHAI JIAO TONG UNIV
View PDF2 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the defects of the above-mentioned patents are: the general spraying or dipping process is adopted, so the bonding force between the formed protective film and the substrate is weak, easy to fall off, easy to wear; at the same time, the product of this invention cannot improve the antibacterial properties of ordinary steel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] This embodiment 1 is implemented under the following conditions of implementation and technical requirements:

[0026] The sample is ordinary steel, and the surface of the sample is ground and mirror polished. Before ion plating, the surface of the sample is cleaned with deionized water and absolute ethanol, and dried to deposit a layer of 1.5-1.8 μm Cr-Ni film on the surface of ordinary carbon steel. Afterwards, metal ions were implanted on the surface of ordinary carbon steel on the ion implantation composite coating equipment (authorized announcement number: CN 1206386C) using the metal rod as the target source.

[0027] First, the ion plating parameters are as follows:

[0028] Element: Ni-Cr; working pressure: 5×10 -8 ×10 -2 Pa; Negative bias voltage: 150-180V; Arc current: 100-110A;

[0029] Second, the ion implantation parameters are as follows:

[0030] Implantation element: Cu; Vacuum degree: 1×10 -3 ×10 -3 Pa; accelerating voltage: 30-35kV; injection do...

Embodiment 2

[0033] This embodiment 2 is implemented under the following conditions of implementation and technical requirements:

[0034] Take ordinary steel products, the surface is ground and mirror polished. Before ion plating, the surface of the product is cleaned with deionized water and acetone, and dried at low temperature to deposit a layer of 2.5-3.0 μm Cr-Ni film on the surface of ordinary carbon steel. Afterwards, metal ions were implanted on the surface of ordinary carbon steel on the ion implantation composite coating equipment (authorized announcement number: CN 1206386C) using the metal rod as the target source.

[0035] First, the ion plating parameters are as follows:

[0036] Element: Ni-Cr; working pressure: 1×10 -1 ~2×10 -1 Pa; Negative bias voltage: 180~200V; Arc current: 110~120A;

[0037] Second, the ion implantation parameters are as follows:

[0038] Implantation element: Cu; Vacuum degree: 8×10 -4 ~1×10 -3 Pa; accelerating voltage: 45 ~ 50kV; injection dos...

Embodiment 3

[0041] This embodiment 3 is implemented under the following conditions of implementation and technical requirements:

[0042]Take ordinary steel, the surface is ground, and mirror polished. Before ion plating, the surface is cleaned with deionized water and absolute ethanol, and dried, and a layer of 2.0-2.5 μm Cr-Ni film is deposited on the surface of ordinary carbon steel. Afterwards, metal ions were implanted on the surface of ordinary carbon steel on the ion implantation composite coating equipment (authorized announcement number: CN1206386C) using the metal rod as the target source.

[0043] First, the ion plating parameters are as follows:

[0044] Element: Ni-Cr; working pressure: 1×10 -1 ~2×10 -1 Pa; Negative bias voltage: 160~180V; Arc current: 110~120A;

[0045] Second, the ion implantation parameters are as follows:

[0046] Implantation element: Ag; Vacuum degree: 1×10 -3 ~3×10 -3 Pa; accelerating voltage: 35 ~ 40kV; injection dose: 3×10 17 ~5×10 17 ions / c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The process of raising antibiotic and antirust performance of common steel product belongs to the field of material surface treating technology. The process includes: grinding and polishing the surface of steel product to mirror finishing, ion plating to deposit Ni-Cr film, and implanting Cu or Ag ion. The ion plating and the ion implanting make the common steel product possess both antibiotic performance and antirust performance. Thus treated steel may be used in door handle, kitchenware, household appliance, etc.

Description

technical field [0001] The invention relates to a surface treatment method in the technical field of metal materials, in particular to a method for improving the antibacterial and antirust properties of ordinary steel. Background technique [0002] Ordinary steel is widely used in many fields such as machinery manufacturing and construction, and is the largest and most important metal material in engineering. However, ordinary steel is easy to corrode during practical application, and the corrosion continues to expand, even forming holes and causing fractures. This is one of the main problems to be solved urgently in the application of ordinary carbon steel. In addition, ordinary carbon steel is in a certain acid-alkaline environment, and it is easy to form micro-batteries on its surface, resulting in electrochemical corrosion. In short, the corrosion of ordinary carbon steel has always been one of the bottlenecks restricting its application. At present, in many fields, st...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C14/22C23C14/32C23C14/48C23C14/54C23C14/14
Inventor 蔡珣安全长沈耀徐放
Owner SHANGHAI JIAO TONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com