High glazing and high liquidity glass fiber-reinforced nylon 6 composite material and preparation method thereof

A glass fiber and composite material technology, applied in the field of high gloss, can solve the problems of loss of material mechanical properties and thermal properties, unmentioned material molding flow properties, rising product cost, etc., to achieve improved mechanical properties, good surface gloss, improved The effect of processability

Active Publication Date: 2008-01-16
CHONGQNG PRET NEW MATERIAL +2
View PDF2 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

They either propose many special requirements to the raw materials for preparing these glass fiber reinforced composite materials, such as the microfine glass fibers of special fineness mentioned in USP.0035984, JP.6021947, USP.6191207; as mentioned in USP.5804313 Special surface coating treatment; such as the rare earth mineral components mentioned in USP.4528304, etc., which will obviously lead to a substantial increase in product costs; or they are at the expense of the excellent mechanical and ther

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0046] Example 1

[0047] The weight ratio of PA6 resin is 84.5%, the weight ratio of glass fiber is 10%, the weight ratio of MAPP is 3%, the weight ratio of KH550 is 0.2%, the weight ratio of 1010 / 168 is 0.1 / 0.2%, and the weight ratio of high gloss masterbatch A is 2%. , Mix the above components in a high-speed mixer at room temperature, and use the TE-35 (L / D=48) twin-screw extruder produced by Nanjing Keya Company. The processing temperature (from the feed port to the die The head) are: 170°C, 200°C, 215°C, 220°C, 225°C, and the main engine speed is 30 Hz. The test results are listed in Table 1.

Example Embodiment

[0048] Example 2

[0049] The weight ratio of PA6 resin is 74.3%, the weight ratio of glass fiber is 20%, the weight ratio of MAPP is 3%, the weight ratio of KH550 is 0.4%, the weight ratio of 1010 / 168 is 0.1 / 0.2%, and the weight ratio of high gloss masterbatch A is 2%. , Mix the above components in a high-speed mixer at room temperature, and use the TE-35 (L / D=48) twin-screw extruder produced by Nanjing Keya Company. The processing temperature (from the feed port to the die The head) are: 180°C, 210°C, 215°C, 220°C, 230°C, and the main engine speed is 30 Hz. The test results are listed in Table 1.

Example Embodiment

[0050] Example 3

[0051] The weight ratio of PA6 resin is 62.1%, the weight ratio of glass fiber is 30%, the weight ratio of MAPP is 4%, the weight ratio of KH550 is 0.6%, the weight ratio of 1010 / 168 is 0.1 / 0.2%, and the weight ratio of high gloss masterbatch A is 3%. , Mix the above components in a high-speed mixer at room temperature, and use the TE-35 (L / D=48) twin-screw extruder produced by Nanjing Keya Company. The processing temperature (from the feed port to the die The head) are: 180°C, 220°C, 225°C, 230°C, 240°C, and the main engine speed is 30 Hz. The test results are listed in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a glass-fiber reinforced nylon 6 composite material with high gloss and high fluidity and a preparation method of the glass-fiber reinforced nylon 6 composite material. The glass-fiber reinforced nylon 6 composite material comprises the following components by weight: nylon 6 resin 40 to 88 percent, compatilizer 1 to 20 percent, glass fiber 10 to 50 percent, master batches with high gloss 0.5 to 5 percent, the other additives 0.5 to 4 percent. The master batches with high gloss are made into granulates with organic fatty acid ester, ethylene copolymer and nylon copolymer by being extruded by twin screw. The specific steps of the method are as follow: all the materials except the glass fiber are weighed to be mixed in a mixer for 3 to 5 minutes, and then the mixed material is put into a twin screw extruder with the glass fiber being added from a first exhaust port. The temperatures from a material feeding port to an extrusion die head respectively are: 160 to 180 DEG C, 190 to 220 DEG C, 210 to 240 DEG C, 220 to 250 DEG C and 210 to 240 DEG C, the engine speed is 20 to 50 Hz. Then the material is made into sample with a plastic injection modeling machine. The composite material has the advantages of fine gloss on the surface, good performance and easy process.

Description

technical field [0001] The invention belongs to the field of polymer composite materials, and in particular relates to a high-gloss, high-flow glass fiber reinforced nylon 6 composite material and a preparation method thereof. Background technique [0002] Glass fiber reinforced nylon has good properties such as high strength, high heat resistance, high fatigue resistance, and low molding shrinkage, so it is widely used in automobiles, machinery, home appliances, aviation and military components and other fields. Traditional application fields usually only have high requirements on the above-mentioned physical and mechanical properties of materials, but do not have high requirements on other characteristics of parts, such as surface gloss. Therefore, in such traditional application fields, when people prepare glass fiber reinforced nylon composite materials, the problem of surface luster caused by the material is usually not considered much. However, with the further expans...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L77/02C08K7/14C08J5/08B29C47/40B29C48/40
CPCB29C2947/92704B29C2948/92704B29C48/40
Inventor 刘正军张祥福周文
Owner CHONGQNG PRET NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap