Method for manufacturing positive electrode aluminum foil of electrolytic capacitor

A technology of electrolytic capacitors and anode aluminum foil, applied in the direction of electrolytic capacitors, capacitor manufacturing, capacitors, etc., can solve the problems of unstable product quality, weakened dissolution, etc., and achieve the effect of high specific volume and good bending

Inactive Publication Date: 2008-01-23
DONGGUAN HEC CONDENSER CO LTD
View PDF0 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The organic acid in the second process adopts a straight-chain saturated dicarboxylic acid or a trans straight-chain unsaturated dicarboxylic acid with an odd number of carbon atoms, or an organic acid with an aromatic ring and a c

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for manufacturing positive electrode aluminum foil of electrolytic capacitor

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0016] Example one

[0017] The high-pressure corrosion foil with a purity of 99.99% is used, treated in pure water above 98°C for 12 minutes, and then in an aqueous solution of 0.04wt% fumaric acid at 75°C for 2.5 minutes. After cleaning with pure water, the treatment time is 0.5 First-stage formation in wt%, 75℃ phosphate, current density 20mA.cm -2 After reaching the predetermined voltage of 200V, it will be kept constant for 8 minutes; then in a mixed solution of 5wt% boric acid, 0.3wt% ammonium borate (or sodium) aqueous solution, 0.5wt% citric acid at 85℃, the current density is 20mA .cm -2 When the voltage reaches 400V, the voltage is constant for 10 minutes; then the third-stage formation is performed in a mixed solution of 5wt% boric acid, 0.15wt% ammonium borate (or sodium) aqueous solution, and 0.1wt% citric acid at 85℃, and the voltage reaches 520V. Press for 15 minutes; then in a mixed solution of 5wt% boric acid, 0.08wt% ammonium borate (or sodium) aqueous solution, ...

Example Embodiment

[0019] Example two

[0020] A high-pressure corrosion foil with a purity of 99.99% was used and treated in pure water above 98°C for 10 minutes, followed by an aqueous solution of maleic acid 0.03% by weight and 75°C for 4 minutes. After cleaning with pure water, the treatment time was 1% by weight. %, 85℃ in phosphate, the first-stage formation, the current density is 30mA.cm -2 After reaching the predetermined voltage of 180V, it is constant for 8 minutes; then the second-stage chemical conversion is carried out in a mixed solution of 3wt% boric acid, 1.0wt% ammonium borate (or sodium) aqueous solution, and 0.20wt% gluconic acid, with a current density of 20mA.cm -2 , Constant voltage for 8 minutes when the voltage reaches 350V; then in the mixed solution of 3wt% boric acid, 0.50wt% ammonium borate (or sodium) aqueous solution, 0.10wt% gluconic acid at 85℃, the third stage formation, the voltage reaches 480V constant Press for 12 minutes; then in a mixed solution of 3wt% boric a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to a method for producing high voltage anode aluminum foil in electrolytic capacitor, which relates to a reduction technology about the method for producing high voltage anode aluminum foil in electrolytic capacitor. The invention mainly comprises a number of procedures comprising pure water boiling, pre-processing, four-stage reduction, heat treatment, phosphoric acid treatment, depolarization treatment and after-treatment. After the treatment of pure water boiling, the aluminum foil will be treatment with a plurality of unsaturated organic acids, then undergone first-state reduction in phosphoric acid and salt, then undergone the second-stage, third-stage and fourth-stage reduction and depolarization in boric acid, boric acid ammonium (or natrium) or minim organic acid solution. Therefore, the produced anode aluminum foil has the advantages of high specific volume and excellent bending performance.

Description

[0001] Field [0002] The invention belongs to a method for manufacturing medium and high voltage anode aluminum foils of electrolytic capacitors. Background technique: [0003] At present, the manufacture of medium and high voltage anode foils for aluminum electrolytic capacitors mainly uses boric acid and ammonium borate or borax for chemical formation, including immersing the corroded foil in high-temperature pure water for a period of time as the first process; The aqueous solution of acid and at least one of these organic acid salts is the second step, and finally, the above-mentioned aluminum foil is subjected to a generation treatment in an electrolytic solution. The organic acid in the second process adopts a straight-chain saturated dicarboxylic acid or a trans straight-chain unsaturated dicarboxylic acid with an odd number of carbon atoms, or an organic acid with an aromatic ring and a carboxyl group, so that the dissolution of the oxide film weakened, the bonding e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01G9/055H01G13/00C25D11/16C25D11/04C25D11/12C25D11/08C25D11/10
Inventor 何凤荣
Owner DONGGUAN HEC CONDENSER CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap