Light-sensitive polymer composition not easy to change color and application thereof
A technology of photosensitive resin and composition, applied in the field of photosensitive resin composition, can solve the problems of poor printing resistance, poor organic solvent resistance, etc., and achieve the effects of superior water resistance, superior water resistance and solvent resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0022] Example 1
[0023] Acrylic acid ester copolymer emulsion [POLYACE AC-120A1 made by Daisei Kayaku Co., Ltd. with a solid content of 35% by weight] 43 parts and polyvinyl alcohol with a degree of polymerization of 1700 and a degree of alkalinity of 88 mol% [manufactured by Nippon Gosei Co., Ltd. PVA-210] 40 parts of 12% by weight aqueous solution were mixed together and then 10 parts of block isocyanate (CORONATE 2513 manufactured by Japan Polyurethane Industry) and photopolymerization initiator diethylthioxanthene [Nippon Kayaku Co., Ltd. ) Manufactured by KAYACURE BP-100] 0.2 part and polymerization accelerator amine compound [KAYACURE-EPA manufactured by Nippon Kayaku Co., Ltd.] 0.1 part of dissolved and mixed acrylic monomer [manufactured by Shinnakamura Chemical Co., Ltd. A-TMM-3] After 10 parts is emulsified, 1 part of the photocuring agent P-diazo diphenylamine sulfate paraformaldehyde condensate is mixed together to form a photosensitive resin composition. Then, a cir...
Example Embodiment
[0024] Example 2
[0025] Acrylic acid ester copolymer emulsion [POLYACE AC-120A1 made by Daisei Kayaku Co., Ltd. with a solid content of 35% by weight] 43 parts and polyvinyl alcohol with a degree of polymerization of 1700 and a degree of alkalinity of 88 mol% [manufactured by Nippon Gosei Co., Ltd. PVA-210] added 12% by weight, 1.4mol% of styryl pyridine salt and 40 parts of photosensitive water-soluble polymer in a mixed solution of 10 parts of bulk isocyanate (CORONATE 2513 manufactured by Japan Polyurethane Industry) Dissolved and mixed with 0.2 part of photopolymerization initiator diethylthioxanthene [KAYACURE BP-100 manufactured by Nippon Kayaku Co., Ltd.] and 0.1 part of polymerization accelerator amine compound [KAYCURE-EPA manufactured by Nippon Kayaku Co., Ltd.] Acrylic monomer [A-TMM-3 manufactured by Shinnakamura Chemical Co., Ltd.] was emulsified and combined into a photosensitive resin composition. Then, a circular screen printing plate was produced using the metho...
Example Embodiment
[0029] Example 3
[0030] The water-soluble polyvinyl alcohol with a degree of alkalinity of 60% or more containing styrylpyridyl or styrylquinolinyl can disperse compounds containing more than one vinyl group in the presence of protective colloids. Under the action of a soluble thermal polymerization initiator, a polymerizable emulsion and a compound that can be cured under the action of heat form a photosensitive resin composition, the photosensitive resin composition comprising a water-dispersible polymer 0.1wt% and a water-soluble binder Polymer 50wt%, photocurable compound 0.1wt%, thermosetting compound 40wt%, diazo resin or dichromate 0.1wt%, defoamer 0.2wt%, level measuring agent 0.5wt%, coloring agent 0.5wt%, Preservative 0.1wt%, organic / inorganic filler 5wt%, organic solvent 3.2wt%, plasticizer 0.1wt%, surfactant 0.1wt%.
PUM
Property | Measurement | Unit |
---|---|---|
Thickness | aaaaa | aaaaa |
Alkalinity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap