Modified chlorosulphonated polyethylene rubber paint for steel storage tank and preparation method thereof

A chlorosulfonated polyethylene and rubber coating technology, applied in epoxy resin coatings, coatings, containers, etc., can solve the problem of poor salt spray resistance and light aging resistance, and the coating is prone to pitting corrosion, discoloration and chalking. and other problems, to achieve the effect of improving thixotropy and workability, improving storage stability, and improving solvent resistance

Inactive Publication Date: 2008-10-29
TIANJIN BO XING ENG SCI & TECH LIMITED COMPANY OF CNPC +1
View PDF0 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The outer surface of existing steel storage tanks is coated with synthetic resin coatings. The disadvantages are that the salt spray resistance and light aging resistance are not good, and the coating is prone to pitting and discoloration. The artificial accelerated salt spray test of synthetic resin coating is generally 500h, and the artificial accelerated light aging test is generally 600h

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] The manufacturing process of the modified chlorosulfonated polyethylene rubber coating for steel storage tanks in the present embodiment 1 is: in a stainless steel bucket, 1 part by weight of chlorosulfonated polyethylene rubber is added to 1 part by weight of chlorosulfonated polyethylene rubber Add polyethylene rubber into 3.0 parts by weight of xylene and 1 part by weight of trimethylbenzene mixed solvent, stir evenly at low speed at room temperature, and disperse at high speed for 5 hours, add 0.1 part by weight of titanium dioxide, 0.2 part by weight of titanium dioxide while stirring Part of talcum powder, 0.02 parts by weight of AFCONA-3777 fluorocarbon modified polyacrylate, 0.02 parts by weight of organic bentonite 881, after dispersing for 0.5h, grind for 1h with a sand mill to make the A agent of the coating; Add 3.5 parts by weight of xylene and 0.8 parts by weight of n-butanol in the bisphenol A type epoxy resin of 1 part, mix well, under the situation of hi...

Embodiment 2

[0022] The manufacturing process of the modified chlorosulfonated polyethylene rubber coating for steel storage tanks in the present embodiment 2 is: in a stainless steel bucket, 1 part by weight of chlorosulfonated polyethylene rubber is added to 1 part by weight of chlorosulfonated polyethylene rubber Add polyethylene rubber into 2.5 parts by weight of xylene and 1.5 parts by weight of trimethylbenzene mixed solvent, stir evenly at low speed at room temperature, and disperse at high speed for 5 hours, add 0.2 parts by weight of titanium dioxide, 0.3 parts by weight of titanium dioxide while stirring Parts of talcum powder, 0.01 parts by weight of EFKA-3777 fluorocarbon modified polyacrylate, 0.03 parts by weight of organic bentonite 881, after dispersing for 0.5h, grind for 1h with a sand mill to make the A agent of the coating; Add 3.5 parts by weight of xylene and 0.8 parts by weight of n-butanol in the bisphenol A type epoxy resin of 1 part, mix well, under the situation o...

Embodiment 3

[0025]The manufacturing process of the modified chlorosulfonated polyethylene rubber coating for steel storage tanks in this embodiment 3 is: in a stainless steel bucket, 1 part by weight of chlorosulfonated polyethylene rubber is added to Add polyethylene rubber into 2.0 parts by weight of xylene and 2.1 parts by weight of trimethylbenzene mixed solvent, stir evenly at low speed at room temperature, and disperse at high speed for 5 hours, then add 0.18 parts by weight of titanium dioxide while stirring , 0.25 parts by weight of talcum powder, 0.03 parts by weight of AFCONA-3777 fluorocarbon modified polyacrylate, 0.05 parts by weight of organic bentonite, after dispersing for 0.5h, grind 1h with a sand mill to make the A agent of the coating; Add 3.5 parts by weight of xylene and 0.8 parts by weight of n-butanol to 1 part by weight of bisphenol A epoxy resin, mix well, and add 0.1 parts by weight of diphenylguanidine, 0.1 parts by weight of ethylene thiourea, dispersed for 0....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a modified chlorosulfonated polyethylene rubber coating used for steel storage tanks and a preparation method thereof. The coating comprises a component A and a component B, wherein the component A is composed of chlorosulfonated polyethylene rubber, dimethylbenzene, trimethylbenzene, titanium white powder, talc powder, fluorocarbon-modified polyacrylamide and organic bentonite; and the component B is composed of bisphenol-A epoxy resin, dimethylbenzene, n-butanol, diphenyl guanidine (manufactured by Dongbei Auxiliary general factory, Shenyang) and ethylenethiourea. The component A and the component B are mixed and cured to form a coating film before application. The coating is excellent in physical property, chemical resistance, salt spray resistance and light fastness, and can be used for the surface protection and coating of steel storage tanks in various corrosive environments.

Description

technical field [0001] The invention relates to a modified chlorosulfonated polyethylene rubber coating used for protecting and coating the outer surface of steel storage tanks under various corrosive environments and a preparation method thereof. Background technique [0002] The outer surface of existing steel storage tanks is coated with synthetic resin coatings. The disadvantages are that the salt spray resistance and light aging resistance are not good, and the coating is prone to pitting and discoloration. The artificial accelerated salt spray test of the synthetic resin coating is generally 500h, and the artificial accelerated light aging test is generally 600h. Contents of the invention [0003] The technical problem to be solved by the present invention is to avoid the shortcomings of the above-mentioned prior art and provide a simple and convenient manufacturing method, which can be dried and formed at room temperature, and the coating film has excellent physical...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D123/34B65D90/04C09D133/08C09D163/02
Inventor 贺江张丽萍段绍明李小朋白晶杜建伟梁国珍
Owner TIANJIN BO XING ENG SCI & TECH LIMITED COMPANY OF CNPC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap