Quick-drying amino-stoving varnish and preparation thereof

An amino baking varnish and formula technology, applied in the field of amino baking varnish and its preparation, can solve the problems of long baking time, high baking temperature, waste of energy and the like, and achieve the effects of fast drying speed, high gloss and convenient construction

Inactive Publication Date: 2009-01-14
WUXI HUHUANG PAINT
View PDF0 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the amino baking varnishes on the market either have a long baking time (more than 1h) or a higher baking temperature (above 200°C). energy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] A kind of quick-drying amino stoving varnish, it comprises the component of following parts by weight:

[0042] Alkyd resin 60 parts

[0043] Basic urethane copolymer 1 part

[0044] Titanium dioxide 20 parts

[0045] Anti-settling agent 0.3 part

[0046] 5 parts of polybasic acid ester

[0047] 582-2 resin 18 parts

[0048] Leveling agent 0.3 part

[0049] Xylene 10 parts

[0050] 4 parts n-butanol

[0051] The production method is as follows:

[0052] 1. Put half of the alkyd resin, 582-2 resin, polybasic dibasic acid ester, xylene, n-butanol and titanium dioxide into the dispersion tank. 1200r / min to disperse for 20min;

[0053] 2. Add the dispersed pigment slurry into a sand mill and grind it to a fineness of ≤20μm;

[0054] 3. Add the remaining alkyd resin, basic urethane copolymer, anti-sedimentation agent and leveling agent in the formulated amount into the ground color paste under stirring, and 1000r / min to disperse for 10 minutes.

Embodiment 2

[0056] A kind of quick-drying amino stoving varnish, it comprises the component of following parts by weight:

[0057] Acrylic resin 75 parts

[0058] Polycarboxylic acid polymer and organosiloxane copolymer (weight ratio 1: 1) 1.5 parts

[0059] Titanium dioxide 30 parts

[0060] 0.4 parts of anti-settling agent

[0061] 10 parts of polybasic acid ester

[0062] 582-2 resin 22 parts

[0063] Leveling agent 0.5 parts

[0064] Xylene 12 parts

[0065] 5 parts n-butanol

[0066] The production method is as follows:

[0067] 1. Put half the amount of acrylic resin, 582-2 resin, polybasic acid ester, xylene, n-butanol and titanium dioxide into the dispersion kettle, 1000r / min to disperse for 15 minutes;

[0068] 2. Add the dispersed pigment slurry into a sand mill and grind it to a fineness of ≤20μm;

[0069] 3. Add the remaining acrylic resin, the formulated amount of polycarboxylic acid polymer and organosiloxane copolymer, the formulated amount of anti-settling agent...

Embodiment 3

[0071] A kind of quick-drying amino stoving varnish, it comprises the component of following parts by weight:

[0072] 45 parts acrylic resin

[0073] Unsaturated polycarboxylic acid polymer 0.5 parts

[0074] 3 parts titanium dioxide

[0075] Anti-settling agent 0.2 part

[0076] 3 parts polybasic acid ester

[0077] 582-2 resin 12 parts

[0078] Leveling agent 0.2 parts

[0079] 7 parts xylene

[0080] 2.5 parts of n-butanol

[0081] The production method is as follows:

[0082] 1. Put half the amount of acrylic resin, 582-2 resin, polybasic dibasic acid ester, xylene, n-butanol and titanium dioxide into the dispersion kettle, 1200r / min to disperse for 18min;

[0083] 2. Add the dispersed pigment slurry into a sand mill and grind it to a fineness of ≤20μm;

[0084] 3. Add the remaining acrylic resin, the formulated amount of unsaturated polycarboxylic acid polymer, the formulated amount of anti-sedimentation agent and the formulated amount of leveling agent into the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
water resistanceaaaaaaaaaa
Login to View More

Abstract

The invention discloses a quick-drying amino baking paint, the components of the quick-drying amino baking paint are as follows:alcoholic acid or acrylic acid resin, dispersing agent, pigment, anti-settling agent, polyhydric dibasic ester, 582-2 resin, leveling agent, dimethyl benzene and normal butyl alcohol. The invention also provides a preparation method of the quick-drying amino baking paint. The quick-drying amino baking paint of the invention is mainly applied in the miniature and thinner steel products such as the fan blade, the outer casing of an air-conditioner, the mechanical cover, the steel barrel and the antitheft door and the like. The quick-drying amino baking paint has the advantages that the baking paint is single componet, and after the baking paint being diluted by the thinning agent, the spraying construction can be directly performed, the construction is convenient, and the drying speed is quick; the paint has good decorative property, and can be made into a variety of pigment according to the requirements; the paint has good adhesive force, high gloss and smooth surface; the paint also has good gloss retention and color retention, more than 75 percent of gloss can commonly be retained after the paint is used outside for 3 years to 4 years by the user ; the preparation method is simple and easy to be realized; after being dried,the paint film is flat and bright.

Description

technical field [0001] The invention relates to a coating and a preparation method thereof, in particular to an amino baking varnish with the advantage of quick drying and a preparation method thereof. Background technique [0002] At present, the amino baking varnishes on the market either have a long baking time (more than 1h) or a higher baking temperature (above 200°C). energy. Therefore be badly in need of developing a kind of amino stoving varnish with quick-drying effect. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide an amino baking varnish with the advantage of quick drying. [0004] A technical problem to be solved by the present invention is to provide a preparation method of the above coating. [0005] In order to solve the problems of the technologies described above, the technical scheme adopted in the present invention is as follows: [0006] A kind of quick-drying amino stoving varnish, it co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/00C09D133/00C09D175/00B05D3/02
Inventor 冯申永
Owner WUXI HUHUANG PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com