Poly-pyrrole and metal nanometer particle composite gas sensor and preparation thereof

A technology of metal nanoparticles and gas sensors, applied in the direction of material resistance, etc., can solve problems such as low sensitivity, poor selectivity, and practical limitations, and achieve the effects of increasing body surface area, improving stability, and enhancing action

Inactive Publication Date: 2011-10-26
ZHEJIANG UNIV
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Ammonia is a common toxic gas. The traditional polypyrrole-based ammonia sensor has the disadvantages of low sensitivity and poor selectivity, and its practical application is limited.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Poly-pyrrole and metal nanometer particle composite gas sensor and preparation thereof
  • Poly-pyrrole and metal nanometer particle composite gas sensor and preparation thereof
  • Poly-pyrrole and metal nanometer particle composite gas sensor and preparation thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] 1) Clean the surface photolithography and evaporate the ceramic substrate with interdigitated gold electrodes, and dry it for later use;

[0029] 2) Palladium chloride, sodium polystyrene sulfonate, and polyvinylpyrrolidone are added to deionized water, palladium chloride: sodium styrene sulfonate unit in sodium polystyrene sulfonate: vinylpyrrolidone unit in polyvinylpyrrolidone The molar ratio is 1:1:1, prepare a solution with a palladium chloride concentration of 0.0012mol / L, then add methanol to the solution, the volume ratio of methanol to deionized water is 1:0.5, and react at 50°C for 0.5h, Obtain the precursor solution.

[0030] 3) Add ammonium persulfate with a concentration of 0.005mol / L to the precursor solution prepared in step 2), and use a dipping machine to immerse the ceramic substrate with interdigitated gold electrodes in step 1) in the precursor solution for 0.5min, After being pulled out and dried in the air, it was gas-phase polymerized in saturate...

Embodiment 2

[0032] 1) cleaning the surface photolithography and evaporating the ceramic substrate with interdigitated gold electrodes, and drying for later use;

[0033] 2) Palladium chloride, sodium polystyrene sulfonate, and polyvinylpyrrolidone are added to deionized water, palladium chloride: sodium styrene sulfonate unit in sodium polystyrene sulfonate: vinylpyrrolidone unit in polyvinylpyrrolidone The molar ratio is 1:10:10, prepare a solution with a palladium chloride concentration of 0.0048mol / L, then add methanol to the solution, the volume ratio of methanol to deionized water is 1:4, and react at 80°C for 8h to obtain precursor solution.

[0034] 3) Ammonium persulfate with a concentration of 0.08mol / L was added to the precursor solution prepared in step 2), and the ceramic substrate with interdigitated gold electrodes in step 1) was immersed in the precursor solution for 8 minutes using a dipping machine to extract After being pulled out and dried, it was gas-phase polymerized...

Embodiment 3

[0036] 1) cleaning the surface photolithography and evaporating the ceramic substrate with interdigitated gold electrodes, and drying for later use;

[0037] 2) Palladium chloride, sodium polystyrene sulfonate, and polyvinylpyrrolidone are added to deionized water, palladium chloride: sodium styrene sulfonate unit in sodium polystyrene sulfonate: vinylpyrrolidone unit in polyvinylpyrrolidone The molar ratio is 1:5:2.5, prepare a solution with a palladium chloride concentration of 0.0024mol / L, then add methanol to the solution, the volume ratio of methanol to deionized water is 1:2, and react at 60°C for 4h to obtain precursor solution.

[0038] 3) Add ammonium persulfate with a concentration of 0.02mol / L to the precursor solution prepared in step 2), and use a dipping machine to immerse the ceramic substrate with interdigitated gold electrodes in step 1) in the precursor solution for 4 minutes to improve After being pulled out and dried, it was gas-phase polymerized in satura...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
widthaaaaaaaaaa
interdigital gapaaaaaaaaaa
Login to View More

Abstract

The invention discloses a polypyrrole and metal nano-particle composite gas sensor and a production method thereof. The gas sensor adopts a ceramic matrix with interdigital gold electrode pairs; the surfaces of the ceramic matrix and the gold electrodes are covered with polypyrrole and palladium nano-particle composite gas-sensing films. The invention has simple production technique and low cost,which is particularly suitable for mass production. The prepared element has the advantages of high sensitivity, fast response, good recovery, strong stability, good selectivity and room temperature detection in ammonia detection, and can be widely used for accurate detection and control of ammonia gas in atmospheric environmental monitoring in the industrial and agricultural production processes.

Description

technical field [0001] The invention relates to a polypyrrole and metal nano particle composite gas sensor and a manufacturing method thereof. Background technique [0002] Toxic gas seriously endangers human life and health. Its room temperature detection plays an important role in industrial and agricultural production and environmental monitoring, which provides a broad space for the development of gas sensors. Polymer intrinsically conductive polymer material gas sensors have developed rapidly in recent years. Compared with traditional ceramic material gas sensors, it has the characteristics of room temperature detection, easy integration, miniaturized mass production, and low price. Among them, the polymer resistive gas sensor is well compatible with the current integrated circuit technology, easy to realize integration, and realizes simultaneous detection and control of various gases, and room temperature detection does not require heating and requires low power, espec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G01N27/12
Inventor 李扬洪利杰杨慕杰
Owner ZHEJIANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com