Synthesis technique of beta-calcium orthophosphate

A synthesis method and technology of calcium phosphate, applied in the field of synthesis of β-calcium phosphate materials, to achieve the effects of stable product performance, simple process and strong repeatability

Inactive Publication Date: 2011-03-16
邓旭亮
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The dry method is synthesized by solid-state reaction, which can produce powder with better crystallization, but the grain size is large, and there are often impurities. It is not only time-consuming but also easy to stick to dirt during grinding, so it is rarely used in the field of bioceramics.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Synthesis technique of beta-calcium orthophosphate
  • Synthesis technique of beta-calcium orthophosphate
  • Synthesis technique of beta-calcium orthophosphate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028]

[0029] Example 2:

[0030] Weigh an appropriate amount of PS microspheres, add concentrated sulfuric acid, stir on a magnetic stirrer for 6 hours, disperse by ultrasonic for half an hour, repeat 2-3 times. After being centrifuged and washed with absolute ethanol, it was dried and set aside. Weigh calcium nitrate and diamine hydrogen phosphate to form a saturated solution. The molar ratio of calcium to phosphorus is 1.4:1. At the same time, add vulcanized PS microspheres and surfactant CTAB ammonia water to adjust the pH value of the reaction to about 8.5. Magnetic stirring Stir on the machine, age after the reaction is complete, centrifuge and wash repeatedly with absolute ethanol, dry in an oven at 70°C, and calcined to 700°C, 800°C, and 850°C for 3 hours respectively.

Embodiment 2

[0032] Weigh an appropriate amount of PS microspheres, add concentrated sulfuric acid, stir on a magnetic stirrer for 5 hours, disperse by ultrasonic for half an hour, repeat 2-3 times. After being centrifuged and washed with absolute ethanol, it was dried and set aside. Weigh calcium nitrate and diammonium hydrogen phosphate to form a saturated solution. The molar ratio of calcium to phosphorus is 1.6:1. At the same time, add vulcanized PS microspheres and surfactant CTAB ammonia water to adjust the pH value of the reaction to about 8. Magnetic stirring Stir on the container, age after the reaction is complete, centrifuge and wash repeatedly with absolute ethanol, dry in an oven at 70°C, and calcined to 700°C, 800°C, and 900°C for 3 hours respectively.

Embodiment 3

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a synthesis technique used for a Beta-calcium phosphate material, comprising the steps as follows: quantitative polystyrene microspheres are added into concentrated sulfuric acid, sufficiently mixed and dispersed by ultrasonic, centrifuged, washed and dried, thus gaining vulcanized polystyrene microspheres; calcium nitrate solution is complexed with diammonium phosphate solution so as to lead the molar ratio of calcium and phosphorus in the complexed solution to be 1.4-1.6; the pH value of the solution is adjusted to be 8-10; furthermore, a surfactant (CTAB) and the vulcanized polystyrene microspheres are added in the complex so as to react sufficiently and gain a white substance which is washed, dried and calcined in a heating surface; subsequently, the white substance is heat-preserved for 2-4 hours at the temperature of 700-1000 DEG C and cooled with the furnace to gain the Beta-calcium phosphate powder. The synthesis technique adds the PS microspheres in the chemical reaction process to synthesize the Beta-calcium phosphate with the aperture and high purity, and has the advantages of simple process, strong repeatability, stable performance of the product, and the like.

Description

technical field [0001] The invention belongs to the field of material science, in particular to a method for synthesizing a β-calcium phosphate material. Background technique [0002] Tricalcium Phosphate, referred to as TCP, Ca 3 (PO 4 ) 2 . Since 1980, the research on the biodegradable calcium phosphate material TCP (α-TCP, β-TCP) has attracted extensive attention of many scholars. There are two kinds of high-temperature α-phase and low-temperature β-phase. The composition of TCP is the same as that of HAP, both contain CaO and P 2 o 5 . Among them, β-TCP is the most widely used. The crystal system of the α phase is monoclinic, and the lattice constant The density is 2.86g / cm 3 . The β phase is hexahedral, The density is 3.07g / cm3. The chemical properties of β-TCP are similar to those of hydroxyapatite, and its solubility in water is large. The solubility in aqueous solution and body fluid is 10 to 15 times that of HAP (solubility: 1 μm / year), and it can be...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01B25/32
Inventor 邓旭亮林元华夏春杰马琦胡晓阳
Owner 邓旭亮
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com