Amorphous soft magnetic alloy coatings and preparation method thereof

A soft magnetic alloy, amorphous alloy technology, applied in metal material coating process, coating, magnetic materials and other directions, can solve the problem of inconvenience, without considering the comprehensive performance of amorphous alloy materials with high magnetic permeability and high saturation magnetic induction intensity , the complex preparation process of shielding materials, etc.

Active Publication Date: 2012-07-25
ADVANCED TECHNOLOGY & MATERIALS CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] The current technology of amorphous alloy electromagnetic shielding technology mainly has the following deficiencies: (1) amorphous soft magnetic alloy is mainly used in the form of strips, flakes, fibers or powders, and is compounded with other materials to form composite materials. The preparation process of shielding materials is relatively complicated and inconvenient to use; (2) the comprehensive performance of high magnetic permeability and high saturation magnetic induction of amorphous alloy materials is not considered; (3) there are difficulties in the preparation of large-area amorphous shielding layers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Amorphous soft magnetic alloy coatings and preparation method thereof
  • Amorphous soft magnetic alloy coatings and preparation method thereof
  • Amorphous soft magnetic alloy coatings and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0034] In a preferred embodiment of the preparation method of the present invention, the alloy material smelted in the first step can be pulverized by atomization in a molten state to prepare alloy powder;

[0035] In another preferred embodiment of the preparation method of the present invention, the alloy material smelted in the first step can also be sprayed with alloy strips or scales in a molten state, and then the strips or scales are crushed to prepare alloy powder;

[0036] In a preferred embodiment of the preparation method of the present invention, the coating of the present invention is obtained by plasma spraying;

[0037] In another preferred embodiment of the preparation method of the present invention, the coating of the present invention is obtained by high velocity flame spraying.

[0038] Compared with prior art, the present invention has following advantage:

[0039] 1. Fe-Co based amorphous soft magnetic alloy material is used to prepare the coating, which...

Embodiment

[0043] Ingredient Fe according to No. 1 36 co 36 Si 4 B 20 Nb 4 and No. 2 component [(Fe 0.6 co 0.4 ) 0.75 Si 0.05 B 0.2 〕 96 Nb 4 After batching, the alloy is smelted, and powders are prepared by gas atomization and water atomization processes respectively, and 300-60 mesh powders are obtained after sieving. The coating is prepared by plasma spraying, the substrate is copper, and sandblasting is carried out before spraying. The plasma spraying process parameters are: arc voltage 60V, arc current 500A, main gas (Ar gas) flow: 70-80L / min, hydrogen flow: 15 ~20L / min, spray distance 100~120mm, powder feeding speed 50~70g / min. Table 1 is the implementation process and performance.

[0044] Table 1 embodiment process and performance

[0045] Preface

No Powder

prepare Powder size

(mesh) Spray side

Law high frequency shielding

efficiency

(dB) DC magnetic screen

Masking efficiency

(dB) Micro Vickers Hardness

Degree (HV100...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
electric potential / voltageaaaaaaaaaa
Login to View More

Abstract

The present invention relates to an amorphous soft magnetic alloy coating and the preparation method thereof, particularly relates to Fe-Co base amorphous soft magnetic alloy coating, characterized in that: (1) the sum of atom percentage content of Fe and Co is no less than 70&; (2) basically the coating is in amorphous structure. The invention also relates to the usage of the coating and the preparation method thereof.

Description

technical field [0001] The invention belongs to the field of electromagnetic shielding, and in particular relates to an Fe-Co-based amorphous soft magnetic alloy coating and a preparation method thereof. The coating is used as an electromagnetic shielding coating, an abrasion-resistant coating and a corrosion-resistant coating. Background technique [0002] With the rapid development and wide application of radio, television, communication, navigation, radar, telemetering and remote control, and computers, human beings have created huge material wealth and provided great convenience for life. However, while enjoying the benefits brought by these new technologies, human society is facing new environmental pollution—electromagnetic pollution. Since the progress of these technologies is inseparable from the use of electromagnetic energy, the electromagnetic environment has become increasingly complex, and electromagnetic pollution has become a major public hazard in today's soc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01F1/153C22C45/00C23C4/08H05K9/00C23C4/06C23C4/134
Inventor 赵新彬倪晓俊卢志超吴嘉伟薄希辉郭金花李德仁孙克周少雄
Owner ADVANCED TECHNOLOGY & MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More