Nonlinear optical material of strontium-ammonium boron tartrate tetrahydrate and preparation method and application thereof

A technology of nonlinear optics and tartaric acid, applied in the direction of nonlinear optics, carboxylate preparation, chemical instruments and methods, etc., can solve the problems of high price, low optical damage threshold, difficult to realize optical integration, etc., and achieve simple preparation, growth short cycle effect

Inactive Publication Date: 2009-06-03
XINJIANG TECHN INST OF PHYSICS & CHEM CHINESE ACAD OF SCI
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the crystal growth technology of these materials has become increasingly mature, there are still obvious shortcomings: such as expensive, low optical damage threshold, and can only work with single crystal materials, it is difficult

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nonlinear optical material of strontium-ammonium boron tartrate tetrahydrate and preparation method and application thereof
  • Nonlinear optical material of strontium-ammonium boron tartrate tetrahydrate and preparation method and application thereof
  • Nonlinear optical material of strontium-ammonium boron tartrate tetrahydrate and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0035] Example 1:

[0036] Taking the chemical reaction formula as an example, the specific operation steps are as follows:

[0037] Weigh SrCl 2 ·6H 2 O solid powder is dissolved in a container of 100mL deionized water, and tartaric acid (L(+)-C 4 H 6 O 6 ) And H 3 BO 3 The powder is mixed and dissolved, in which SrCl 2 ·6H 2 O, tartaric acid (L(+)-C 4 H 6 O 6 ) And H 3 BO 3 The molar ratio of the system is 1:1:10, and the incompletely dissolved substances are treated with ultrasonic waves at a temperature of 30°C for 60 minutes to make them fully mixed and dissolved;

[0038] Then take the solution out, cool to room temperature naturally, and then add NH 3 ·H 2 O, slowly drip into the solution, adjust the pH value to 10 and stop the dripping. A large amount of white insoluble matter appears in the solution during the dripping process;

[0039] Seal with plastic wrap, then pierce a number of small holes in the film, place the solution in a clean, pollution-free, air-free environm...

Example Embodiment

[0042] Example 2:

[0043] Taking the chemical reaction formula as an example, the specific operation steps are carried out according to Example 1;

[0044] Weigh SrCl 2 ·6H 2 O solid powder is dissolved in a container of 250mL deionized water, and tartaric acid (L(+)-C 4 H 6 O 6 ) And H 3 BO 3 The powder is mixed and dissolved, in which SrCl 2 ·6H 2 O, tartaric acid (L(+)-C 4 H 6 O 6 ) And H 3 BO 3 The molar ratio of the system is 1:1.5:5, and then the incompletely dissolved substances are treated with ultrasonic waves at a temperature of 35°C for 60 minutes to make them fully mixed and dissolved;

[0045] Then take the solution out, cool to room temperature naturally, and then add NH 3 ·H 2 O slowly drip into the solution, adjust the pH value to 10.5 and stop the dripping. During the dripping process, a large amount of white insoluble matter appears in the solution;

[0046] Place the solution system open in a clean, pollution-free, air-free environment, and let it stand for 50 ...

Example Embodiment

[0049] Example 3:

[0050] Taking the chemical reaction formula as an example, the specific operation steps are carried out according to Example 1;

[0051] Weigh SrCl 2 ·6H 2 O solid powder is dissolved in a 500mL deionized water container, and tartaric acid (L(+)-C 4 H 6 O 6 ) And H 3 BO 3 The powder is mixed and dissolved, in which SrCl 2 ·6H 2 O, tartaric acid (L(+)-C 4 H 6 O 6 ) And H 3 BO 3 The molar ratio of the system is 1:2:8, and then the incompletely dissolved substances are treated with ultrasonic waves at a temperature of 40°C for 60 minutes to make them fully mixed and dissolved;

[0052] Then take the solution out, cool to room temperature naturally, and then add NH 3 ·H 2 O slowly drip into the solution, adjust the pH value to 11 and stop dripping. During the dripping process, the solution appears a lot of white insoluble matter;

[0053] Seal the solution with a plastic wrap, then pierce a number of small holes in the film, place the solution in a clean, pollution...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a nonlinear optical crystal of strontium-ammonium boron tartrate tetrahydrate and a preparation method and application thereof. The molecular formula of the crystal is C4H16BNO12Sr, belongs to triclinic system and has a molecular weight of 368.61. The method comprises: adopting a water solution method, adjusting pH value, slowly volatizing water in 10 to 60 days so as to obtain a plurality of crystals, selecting crystals with better quality as seed crystals and using a program temperature reducing method to obtain the organic-inorganic hybrid nonlinear optical crystal of strontium-ammonium boron tartrate tetrahydrate with larger size. The nonlinear optical effect of the crystal is 1.5 times that of KDP crystal and the ultraviolet-visible transparent wave band ranges from 210nm to 900nm. The crystal has simple operation and low cost; an agent in use is an organic/inorganic material and has the advantages of low toxicity, short growth cycle and stable hysicochemical properties, and the like. The nonlinear optical crystal can be widely applied in nonlinear optical devices, such as frequency doubling converters, optical parametric oscillators, and the like.

Description

technical field [0001] The invention relates to an organic-inorganic hybrid prepared by an aqueous solution method, in particular to a boron ammonium strontium tartrate tetrahydrate nonlinear optical crystal formed by hybridization between an inorganic borate and an organic acid, and a preparation method and use thereof. Background technique [0002] Due to the attractive application prospects of nonlinear optics in modern laser technology, optical communication, data storage, optical information processing, etc., in recent decades, the search for new materials with strong nonlinear optical properties and extremely fast response speed has become a new field of nonlinear optics. One of the main research topics in the field. Early research on nonlinear optical materials mainly focused on inorganic crystals and semiconductor materials, many of which have been applied in practice, such as quartz, KDP, lithium niobate (LN) and so on. my country is in the leading position in the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): G02F1/355C07F5/02C07C59/255C07C51/41
Inventor 潘世烈范晓芸
Owner XINJIANG TECHN INST OF PHYSICS & CHEM CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka