Zincium electrode production method for zinc-nickel battery

A manufacturing method and technology of zinc-nickel batteries, applied in the direction of alkaline battery electrodes, etc., can solve the problems of short charge and discharge cycle life, increased battery internal pressure, difficult battery sealing, etc., and achieve a small difference in polarization potential and electrodeposition efficiency , charging efficiency improvement, and the effect of solving the problem of sealing

Inactive Publication Date: 2009-06-10
GUIZHOU MEILING POWER SUPPLY CO LTD
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] ①The charge and discharge cycle life is short
[0005] ②Battery is not easy to seal
Oxygen will be generated on the nickel electrode during the charging process of the zinc-nickel battery, and hydrogen gas will be generated during the storage process of the battery, which will cause the internal pressure of the battery to rise and cause the battery to be difficult to seal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 2

[0015] Embodiment 2 of the present invention: configure active material by weight, Zn powder: 88 parts, Ca(OH) 2 : 4 parts, In: 0.5 parts, adhesive: 7.5 parts. All the other are with embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for manufacturing a zinc electrode of a zinc-nickel cell. A silver-plated foam nickel conductive framework is coated with 84 to 88 portions of zinc powder, 4 to 7 portions of calcium hydroxide, 0.5 to 1.0 portion of indium and 7 to 9 portions of adhesive which is a pasty active substance, is pressed and molded and is finally dried. The method has obvious function in habiting deformation of the zinc electrode and growth of dendritic crystal; with the method, as the hydrogen precipitation overpotential of silver is high, the hydrogen precipitation is inhibited to improve the charging efficiency of the zinc electrode; each part of the electrode has even density and thickness; the polarization potential and the electrodeposition efficiency have small difference; and the electrode is uneasy to deform so as to well inhibit the problem of rapid increase of the dendritic crystal of specific parts of the zinc electrode, thereby well solving the problems of deformation, the dendritic crystal and short service life of the zinc electrode. The cyclic life of the nickel-zinc cell is increased from 200 cycles to 350 cycles. The method solves the problem of difficult sealing of the zinc-nickel cell.

Description

Technical field: [0001] The invention relates to a method for manufacturing a long-life zinc-nickel battery zinc electrode, belonging to the technical field of the zinc-nickel battery zinc electrode. Background technique: [0002] Zinc-nickel batteries have the superior performance of the extremely high capacity of the zinc anode in the zinc-silver battery and the long life of the nickel electrode in the cadmium-nickel battery. The outstanding advantages of zinc-nickel batteries are: high specific energy, up to 50Wh / kg~80Wh / kg; large specific power, which can exceed 200W / kg; wide working temperature range, which can be normal between -20℃~+60℃ Work. The source of raw material is extensive, the cost is low, and will not cause environmental pollution. [0003] Its main disadvantages are mainly as follows: [0004] ① The charging and discharging cycle life is short. The zinc electrode is easily deformed during the cycle charge and discharge process, and the dendrites cause ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/26
CPCY02E60/124Y02E60/10
Inventor 林甘红韦海张云朋魏俊华曹念荣石斌肖骞王庆杰
Owner GUIZHOU MEILING POWER SUPPLY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products