A transparent ink and gravure technology, applied in ink, household utensils, applications, etc., can solve the problems of low transparency, hinder light penetration, affect the appearance of packaging products, etc., achieve low solvent residue and good visual effect

Active Publication Date: 2009-06-17
HUANGSHAN SHINING INK TECH
View PDF0 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The packaging plastic film adopts multi-layer composite method and composite aluminized material to meet this demand. The ink is to give a picture, text and description on the surface of the package, and it is a coating between various substrates to prevent the ink from damaging the substrate. Corr

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] Preparation:

[0042] a) Dye dilution process: Dilute the dye into a solution with a weight concentration of 20% with an appropriate amount of mixed solvent, and adjust the pH value of the solution to 7.0, leave it to stand and filter, and the mixed solvent is ethyl acetate, Ethanol, isopropanol, propylene glycol methyl ether, the weight ratio is 1:1.8:1:0.4;

[0043] b) Resin dilution process: Dilute the vinyl chloride vinyl acetate copolymer resin to a weight concentration of 20% and the modified chlorinated polypropylene resin to a weight concentration of 50% with the same mixed solvent as the a) operation; this ratio The mixed solvent can fully dissolve the vinyl chloride vinyl acetate copolymer resin under the condition that the amount of the mixed solvent is the least, and reduce the pollution of the solvent to the environment.

[0044] c) Blending process: first stir the remaining mixed solvent in the formula with polyurethane solution, vinyl chloride vinyl acet...

Embodiment 2

[0058] Except that formula is following material and parts by weight, all the other are identical with embodiment 1

[0059] Yellow ink formula (weight ratio)

[0060] Modified polyurethane 33

[0061] Vinyl chloride vinyl acetate copolymer resin 4

[0062] Modified chlorinated polypropylene resin 3

[0063] Dye BL Yellow 10

[0064] Erucamide Wax 0.5

[0065] Defoamer 0.5

[0066] Adhesion Promoter 1

[0067] Propylene glycol methyl ether 3

[0068] Ethyl acetate 15

[0069] Ethanol 17

[0070] Isopropanol13.

Embodiment 3

[0072] Except that formula is following material and parts by weight, all the other are identical with embodiment 1

[0073] Blue ink formula (weight ratio)

[0074] Modified polyurethane 15

[0075] Vinyl chloride vinyl acetate copolymer resin 3

[0076] Modified chlorinated polypropylene resin 2

[0077] Dye BL-06 blue 10

[0078] Erucamide Wax 1

[0079] Defoamer 1

[0080] Adhesion Promoter 1.5

[0081] Propylene glycol methyl ether 5

[0082] Ethyl acetate 5

[0083] Ethanol 15

[0084] Isopropanol 5

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a gravure ink and a preparation method thereof. The ink consists of the following substances of modified polyurethane, a vinyl chloride acetic acid copolymer resin, a modified chlorinatedpolypropylene resin, a dye, an erucidic acid amide wax, an antifoaming agent, an adhesion promoter, propylene glycol methyl ether, acetic ether, ethanol and dimethyl carbinol. The preparation method of the invention includes the following sequential working procedures: a) the dye diluting; b) the resin diluting; c) the blending. Compared with the present technology, the invention is low in solvent residue, and printing products have no version fogs of knife wires with very good adhesion fastness on BOPP and PET and are especially suitable for package printing of PET aluminium-plated products. Metallic lustre of composite packaged products is fully shown, and the visual effect is very good and the adhesion fastness of the ink is equal to or more than 98 percent. The composite sealing strength is 45N per 15mm.

Description

technical field [0001] The invention relates to a gravure ink and a preparation method thereof, in particular to a gravure transparent ink and a preparation method thereof. Background technique [0002] Plastic film packaging products are very common in daily life. Plastic film packaging products include pharmaceutical packaging, food packaging, and daily chemical packaging. [0003] The characteristics of packaging requirements for plastic film packaging are anti-corrosion, anti-leakage, anti-oxidation, better sealing and air tightness, which is more conducive to the protection of packaging. The packaging plastic film adopts multi-layer composite method and composite aluminized material to meet this demand. The ink is to give a picture, text and description on the surface of the package, and it is a coating between various substrates to prevent the ink from damaging the substrate. Corrosiveness, ordinary inks use pigments as colorants, which have a certain covering power,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D11/10C09D11/102
Inventor 汪建中吴土华罗平平汪健方正吴秉祯王宾
Owner HUANGSHAN SHINING INK TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap