Aqueous glass frosting powder chemical composition and preparation method thereof

A technology for frosting powder and composition, which is applied in the field of glass frosting production, water-based glass frosting powder chemical composition and preparation thereof, can solve the problem of physical injury to operators, large changes in frosting process, and high corrosiveness of production equipment. and other problems to achieve the effect of reducing environmental pollution

Inactive Publication Date: 2009-09-16
上海多林玻璃技术有限公司
View PDF3 Cites 40 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since the above patents all use strong acid as the medium, which has strong volatility and corrosiveness, not only the frosting process changes greatly,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] Ammonium bifluoride 30%

[0014] Potassium bifluoride 8%

[0015] Oxalic Acid 20%

[0016] Chloroacetic acid 10%

[0017] Kaolin 8%

[0018] Magnesium Sulfate 22%

[0019] Hydroxyethyl Cellulose 2%

[0020] According to the glass frosting powder composition with water as the medium configured in the above list, when taking the preparation of 10kg frosting powder as an example, the above-mentioned components are weighed in the above-mentioned weight percentage range and placed in a plastic container, and stirred for 10 Minutes, get a white frosting powder mixed uniformly. When using, dissolve 10kg of frosting powder in 6.0kg of tap water at a ratio of 1:0.60. After the frosting powder is mixed with water in a plastic container, the temperature of the mixture drops rapidly to 5°C. Keep stirring at a constant speed for 24 hours to obtain a uniformly mixed frosting solution. Immerse the cleaned glass sheet (thickness 3mm, size 150×200mm) in the frosting solution for...

Embodiment 2

[0026] Ammonium bifluoride 40%

[0027] Sodium fluoborate 10%

[0028] Sodium bifluoride 5%

[0029] Sorbic Acid 15%

[0030] Trichloroacetic acid 5%

[0031] Bentonite 15%

[0032] Magnesium Fluorosilicate 9.5%

[0033] Sodium lignosulfonate 0.5%

[0034] According to the glass frosting powder composition with water as the medium configured according to the above list, when preparing 10kg frosting powder as an example, weigh each of the above components within the above weight percentage range and place them in a plastic container, and stir After 10 minutes, a uniformly mixed frosting powder white powder was obtained. When using, dissolve 10kg of frosting powder in 4.0kg of tap water at a ratio of 1:0.40. After the frosting powder is mixed with water in a plastic container, the temperature of the mixture drops rapidly to 5°C. Keep stirring at a constant speed for 24 hours to obtain a uniformly mixed frosting solution. Immerse the cleaned glass sheet (thickness 3mm, s...

Embodiment 3

[0040] Ammonium bifluoride 80%

[0041] Potassium fluoroborate 4%

[0042] Citric Acid 10%

[0043] Barite powder 2%

[0044] Hydroxyethyl Cellulose 4%

[0045] According to the composition of glass frosting powder with water as the medium configured according to the above list, when preparing 10kg of frosting powder as an example, weigh each of the above components within the above weight percentage range and place them in a plastic container, and stir for 10 minutes , to obtain a uniformly mixed frosting powder white powder. According to the ratio of 1:0.7, dissolve 10kg of frosting powder in 7.0kg of tap water. After the frosting powder is mixed with water in a plastic container, the temperature of the mixture drops rapidly to 5°C. Keep stirring at a constant speed for 24 hours to obtain a uniformly mixed frosting solution. Immerse the cleaned glass sheet (thickness 3mm, size 150×200mm) in the frosting solution for 6 minutes. Take it out and rinse it with water for 1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an aqueous glass frosting powder chemical composition containing a mixed material of an inorganic fluorine compound capable of generating fluorine ions in water, a solid acid compound capable of dissolving in water, an assistant and a filling agent, wherein the mixed material is doped with at least one surfactant; the adding amount of the inorganic fluorine compound is 20 to 90 percent of the total weight percentage of the frosting powder; the adding amount of the solid acid compound is 10 to 60 percent of the total weight percentage of the frosting powder; the adding amount of the filling agent is 1 to 30 percent of the total weight percentage of the frosting powder; the adding amount of the surfactant is 0.1 to 10 percent of the total weight percentage of the frosting powder; and during use, the water is 20 to 100 percent of the total weight percentage of the frosting powder to prepare frosting powder liquid. The technical scheme can avoid acid pollution of the production environment and natural environment because of the inevitable strong acid medium such as sulphuric acid and hydrochloric acid when frosting a glass product by using the prior glass frosting liquid.

Description

technical field [0001] The invention relates to the chemical composition of glass frosting powder, in particular to a water-based chemical composition of glass frosting powder and a preparation method thereof, belonging to the glass frosting production technology category. Background of the invention [0002] Glass frosting can make glass have a hazy and beautiful appearance, and has been widely used in daily life and industrial production. For a long time, the glass frosting processing industry has been using the method of sandblasting and chemical reaction on the glass surface to make glass frosting products. Common chemical glass etching is performed by fluoride ions in solution and silicon atoms in the glass surface structure. Chinese patents ZL96122275.1, ZL00110528.0, and ZL01126383.0 all describe technical methods involving frosting treatment of glass products. The above-mentioned technologies all use hydrofluoric acid or various fluorides as the main means of etchi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C15/00
Inventor 李建辉
Owner 上海多林玻璃技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap