Glass fiber reinforced polyester mineral composite material and preparation method thereof

A technology of glass fiber and composite materials, which is applied in the field of composite materials, can solve the problems that are difficult to improve the dynamic and static performance and thermal stability of machine tools, achieve excellent damping and vibration reduction performance, improve mechanical properties, and improve damping and vibration reduction performance Effect

Inactive Publication Date: 2009-09-16
SHANDONG UNIV
View PDF0 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In recent years, the structure, design and control system of machine tools have developed rapidly, but most of the mechanical basic parts are still mainly ma

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glass fiber reinforced polyester mineral composite material and preparation method thereof
  • Glass fiber reinforced polyester mineral composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0024] The preparation method of the glass fiber reinforced polyester mineral composite material includes the following steps (such as figure 2 ):

[0025] a) Sieving granite particles or sand particles into 6 levels according to the particle size range: 0.1mm~0.6mm, 0.6mm~2mm, 2mm~3.5mm, 3.5mm~5mm, 5mm~7mm, 7mm~10mm , Clean and dry the granular aggregates of different particle size grades, and then weigh them according to a certain mass ratio according to the different particle size grades and mix them evenly; b) Weigh the glass fibers and use the silane coupling agent soaking method to surface treat the glass fibers; c) Weigh the liquid synthetic resin, diluent, toughening agent and curing agent and mix them into a uniform resin system, add the surface-treated glass fiber to the uniformly mixed resin system, and stir to make it evenly distributed; d) mix The uniform solid particle aggregate is added to the homogeneous mixture of the resin system and glass fiber, and continues to...

Embodiment 1

[0027] Aggregate: 8000g natural granite particles, of which:

[0028] 0.1mm~0.6mm: 1040g, accounting for 13%

[0029] 0.6mm~2mm: 1360g, accounting for 17%

[0030] 2mm~3.5mm: 1200g, accounting for 15%

[0031] 3.5mm~5mm: 1120g, accounting for 14%

[0032] 5mm~7mm: 1360g, accounting for 17%

[0033] 7mm~10mm: 1920g, accounting for 24%

[0034] Adhesive base 975g, of which:

[0035] Epoxy resin 660g

[0036] Curing agent ethylene diamine 200g

[0037] Thinner acetone 55g

[0038] Toughening agent dibutyl phthalate 60g

[0039] Glass fiber 25g

[0040] The obtained glass fiber reinforced polyester mineral composite material has a compressive strength of 97.68MPa and a damping ratio of 0.231.

Embodiment 2

[0042] Aggregate: 50kg of natural granite particles, of which:

[0043] 0.1mm~0.6mm: 7kg, accounting for 14%

[0044] 0.6mm~2mm: 8kg, accounting for 16%

[0045] 2mm~3.5mm: 7.5kg, accounting for 15%

[0046] 3.5mm~5mm: 7kg, accounting for 14%

[0047] 5mm~7mm: 9kg, accounting for 18%

[0048] 7mm~10mm: 11.5kg, accounting for 23%

[0049] Adhesive base 7.8kg, of which:

[0050] Epoxy resin 5.5kg

[0051] Curing agent ethylenediamine 1.6kg

[0052] Thinner acetone 0.3kg

[0053] Toughening agent dibutyl phthalate 0.4kg

[0054] Glass fiber 0.2kg

[0055] The obtained glass fiber reinforced polyester mineral composite material has a compressive strength of 103.51MPa and a damping ratio of 0.207.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Compressive strengthaaaaaaaaaa
Compressive strengthaaaaaaaaaa
Compressive strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a glass fiber reinforced polyester mineral composite material and a preparation method thereof, which belong to the technical filed of composite materials. The glass fiber reinforced polyester mineral composite material comprises an adhesive substrate, an aggregate and a glass fiber, and is prepared by the steps of evenly mixing the adhesive substrate, the aggregate and the glass fiber, casting and curing the mixture, and the like, wherein the mass fraction of the adhesive substrate is 9 to 20 percent; the mass fraction of the aggregate is 79 to 90 percent; and the mass fraction of the glass fiber is 0.1 to 1 percent. The composite material has excellent damping property and physical and mechanical properties, improves the compressive strength by 15 to 25 percent compared with a polyester mineral material without reinforced fiber, improves the damping ratio by 9.5 to 23 percent, and can be used as an excellent mechanical basic element material.

Description

Technical field: [0001] The invention relates to a composite material and a preparation method thereof, in particular to a glass fiber reinforced polyester mineral composite material and a preparation method thereof, and belongs to the technical field of composite materials. Background technique: [0002] The development of modern science and technology has increasingly higher requirements for machining efficiency, precision and quality. High speed and high precision have become the two major development trends of modern machining technology. It is required to shorten the processing time and auxiliary time, and increase the metal removal rate and cutting amount. . The increase of cutting amount is easy to cause vibration during processing, so the machine tool system is required to have better dynamic and static performance, thermal stability, high damping and other performance. The main way to solve the vibration problem is to optimize the structure of the machine tool and use ne...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L101/00C08L67/06C08L63/00C08K13/06C08K9/06C08K7/14
Inventor 张建华白文峰
Owner SHANDONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap