Hollow-core rock wool and preparation method and applications thereof

A technology of rock wool and hollow core, applied in glass manufacturing equipment, manufacturing tools, etc., can solve the problems of low heat preservation, short rock wool fibers, poor tensile force, etc., and achieve the effect of cool hand feeling, strong toughness and good tension

Inactive Publication Date: 2009-09-23
鞠加会
View PDF0 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The prepared rock wool fiber is short, the tensile force is poor, the toughness is poor, and the degree of heat preservation is low.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hollow-core rock wool and preparation method and applications thereof
  • Hollow-core rock wool and preparation method and applications thereof
  • Hollow-core rock wool and preparation method and applications thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Take each raw material according to the following weight ratio: basalt 60kg, dolomite 30kg, diabase 6kg, fluorite 4kg;

[0026] Mix the above raw materials evenly and put them into the cupola (purchased from Longhua Complete Equipment Factory of Langfang Longhua Energy Saving Materials Co., Ltd., specification: annual output of 3,000 tons), melt at a high temperature of 900-1000°C, and guide the melt into The rollers of the four-roller high-speed centrifuge (purchased from Nanjing Fiberglass Research Institute, specification: annual output 2000-3000 tons) are formed into fibers. During the fiberization process, the melt is subjected to cooling water in the rollers and a high-pressure fan in contact with the rollers. (Purchased from Harbin High Pressure Fan Factory; specification: 919-2900 rpm, wind pressure: 5008-5697m 3 / n) The resulting cold air is cooled and blown into cotton.

[0027] Wherein, in the preparation process, each specific process parameter preferably a...

Embodiment 2

[0036] Take each raw material according to the following weight ratio: basalt 70kg, dolomite 20kg, diabase 2kg, fluorite 8kg;

[0037] Mix the above raw materials evenly and put them into the cupola (purchased from Longhua Complete Equipment Factory of Langfang Longhua Energy Saving Materials Co., Ltd., specification: annual output of 3,000 tons), melt at a high temperature of 900-1000°C, and guide the melt into The rollers of the four-roller high-speed centrifuge (purchased from Nanjing Fiberglass Research Institute, specification: annual output 2000-3000 tons) are formed into fibers. During the fiberization process, the melt is subjected to cooling water in the rollers and a high-pressure fan in contact with the rollers. (Purchased from Harbin High Pressure Fan Factory; specification: 919-2900 rpm, wind pressure: 5008-5697m 3 / n) The resulting cold air is cooled and blown into cotton.

[0038] Wherein, in the preparation process, each specific process parameter preferably a...

Embodiment 3

[0047] Take each raw material according to the following weight ratio: Heilongjiang Muling mesobasalt 65kg, dolomite 25kg, diabase 4kg, fluorite 6kg;

[0048] Mix the above raw materials evenly and put them into the cupola (purchased from Longhua Complete Equipment Factory of Langfang Longhua Energy Saving Materials Co., Ltd., specification: annual output of 3,000 tons), melt at a high temperature of 900-1000°C, and guide the melt into The rollers of the four-roller high-speed centrifuge (purchased from Nanjing Fiberglass Research Institute, specification: annual output 2000-3000 tons) are formed into fibers. During the fiberization process, the melt is subjected to cooling water in the rollers and a high-pressure fan in contact with the rollers. (Purchased from Harbin High Pressure Fan Factory; specification: 919-2900 rpm, wind pressure: 5008-5697m 3 / n) The resulting cold air is cooled and blown into cotton.

[0049] Wherein, in the preparation process, each specific proces...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a hollow-core rock wool and a preparation method and applications thereof, belonging to the field of temperature-preservation and heat-insulation materials. The hollow-core rock wool consists of the following materials by weight percentage: 60-70% of basalt, 20-30% of dolomite, 2-6% of diabase, and 4-8% of fluorite. After being mixed evenly, the materials are put into a cupola and melted at high temperature of 900-1000 DEG C, and then the hollow-core rock wool is obtained. The rock wool has long fiber, good temperature-preservation and heat-insulation properties, fireproofing capability, good elasticity, strong tensile force and good hand-feel, thus being head and shoulders above the slag cotton. All properties are in full compliance with standards of nation, national defense, industry, aerospace, navigation, construction, petroleum, chemical industry, and agriculture. The hollow-core rock wool can be used for the industries such as electric power, chemical industry, petroleum, construction, metallurgy, textile, shipping, automobile, train, airplane, heating pipe and the like, and is the temperature-preservation and heat-insulation material of industrial equipment such as pipeline storage tanks, boiler flues, heat exchangers, large airports, gyms, large-scale cold storage and the like, and civil building engineering.

Description

technical field [0001] The present invention relates to a heat preservation and heat insulation material, in particular to a hollow rock wool with heat preservation and heat insulation properties which is mainly prepared from basalt ore as a raw material. The invention also relates to the preparation method and The application belongs to the field of thermal insulation and heat insulation materials. Background technique [0002] Rock wool is an inorganic fiber made from natural rocks such as basalt, gabbro, dolomite, iron ore, bauxite, etc., which are melted and fiberized at high temperature. Rock wool product is a kind of heat preservation and heat insulation material, which has the characteristics of light weight, heat preservation, heat insulation, flame retardant, sound insulation, energy saving, corrosion resistance, acid and alkali resistance, etc. Its main chemical components are silicon dioxide, trioxide Magnesium, Magnesium Oxide and Calcium Oxide. Compared with t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C13/06C03B37/00
Inventor 鞠加会
Owner 鞠加会
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com