Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Light heat insulation construction material of solar energy phase transition heat accumulation

A phase change heat storage and building insulation technology, applied in the field of building insulation materials, can solve problems such as economic losses, and achieve the effects of energy saving, simple and fast construction, and high strength

Inactive Publication Date: 2010-02-17
沈阳隆发电热产品制造有限公司
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although benzene panels will burn at a certain temperature, and will release a large amount of toxic and harmful gases during the combustion process, in order to save energy, because benzene panels do not burn at low temperatures, they are used in large quantities under the effect of fluke. So far, there are indeed some fires caused by benzene panels, which have brought huge economic losses to people's lives and production.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0026] First take 100 kg of phase change thermal storage insulation material, 260 kg of 425# ordinary Portland cement, 450 kg of fly ash, 50 kg of light-body expanded vermiculite powder, 89 kg of expanded water-quenched steel slag, and 3 kg of cement reinforcing agent, and add them to the In the mixing tank, mix under stirring at room temperature for 0.5 to 1.5 hours; then, under stirring, add 1 kg of anti-seepage and water repellent, 4 kg of redispersible latex powder as a bonding regulator, and as Anti-cracking agent polypropylene cellulose Fc-055 kg, starch ether 6200 2.5 kg, hexachloro powder or SQ-8 algicide trichloropropyl sulfate 2.5 kg as anti-mold agent, anti-cracking agent added to the mixture In the tank, and after being fully mixed by cyclone separation, the finished product is packaged in bags.

[0027] The above anti-seepage and waterproofing agent is composed of 2 kg of synthetic fatty acid or natural stearic acid, 13 kg of hydroxyethyl cellulose, 21 kg of portl...

example 2

[0031]First take 100 kg of phase change heat storage insulation material, 280 kg of 425# ordinary Portland cement, 482 kg of fly ash, 60 kg of light-body expanded vermiculite powder, 120 kg of expanded water-quenched steel slag, and 2 kg of cement reinforcing agent, and add them to the In the mixing tank, mix under stirring at room temperature for 0.5 to 1.5 hours; then, under stirring, 3 kg of anti-seepage water repellent, 4.5 kg of redispersible latex powder as a bonding regulator, and as 4 kg of polypropylene cellulose Fc-05 anti-cracking agent, 3.5 kg of starch ether 6200, 3 kg of trichloropropyl sulfate as anti-fungal agent, and anti-cracking agent were added to the mixing tank and fully mixed by cyclone separation. After uniformity, the finished product is packaged in bags.

[0032] The above anti-seepage and waterproofing agent is composed of 2 kg of synthetic fatty acid or natural stearic acid, 15 kg of hydroxyethyl cellulose, 20 kg of Portland cement or high alumina c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a light heat insulation construction material of solar energy phase transition heat accumulation, which has the following technical essentials: firstly, respectively adding acertain amount of phase transition heat accumulation and heat insulation material, common portland cement, fly ash, light expanded vermiculite powder, expanded water-hardened steel slag and cement reinforcing agent sequentially into a mixing trough; evenly mixing the materials by stirring at normal temperature; then, adding with stirring, a certain amount of impervious waterproof agent, redispersible latex powder as a bonding regulator, polypropylene cellulose as an antimitotic agent, starch ether and chlordene powder or SQ-8 algicide trichloro-propyl sulfate as an anti-mildew agent; fully mixing the materials evenly by cyclone separation; and packing the mixture to obtain a finished product. The material of the invention has good effects of heat insulation, heat accumulation and energy saving, light volume weight (345-650 kilograms / cubic meter), large density, high strength and small heat transfer coefficient. The fly ash which is a serious public nuisance is fully utilized as a renewable resource to produce the environment-friendly light heat insulation construction material of solar energy phase transition heat accumulation by fully utilizing the characteristics of the fly ash.

Description

technical field [0001] The invention relates to the technical field of building thermal insulation materials, in particular to a solar energy phase change thermal storage light-weight building thermal insulation material. Background technique [0002] As we all know, in the construction process of traditional buildings and one-story houses, a protective layer is applied inside and outside the structural walls, generally using white lime mortar or cement mortar, and then adding paint to the outdoor structural walls according to different needs. layer or decorative brick layer, adding a decorative layer to the interior structural wall. With the continuous development of science and technology and the continuous progress of society, people pay more and more attention to the energy-saving and thermal insulation of residential and office buildings. [0003] In recent years, in order to increase the thermal insulation performance of houses, especially in the process of building c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C09K5/06C04B18/08C04B14/20C04B18/14
CPCC04B2111/28C04B2103/302C04B20/06C04B28/04Y02W30/91C04B14/204C04B18/08C04B18/142C04B24/383C04B32/02C04B40/0028C04B2103/0057C04B2103/0071C04B2103/58C04B2103/65C04B2103/69C04B20/02C04B7/02C04B24/005C04B24/06C04B24/08C04B24/2641C04B7/32C04B24/085C04B24/04C04B24/18
Inventor 袁海波刘磊刘立志
Owner 沈阳隆发电热产品制造有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products