Daily ceramic glaze with high refractive rate and preparation technique thereof

A high-refractive-index, ceramic glaze technology, applied in the field of ceramic manufacturing, can solve the problems that the surface of daily-use ceramic products is not smooth, bright, and old, and achieve the effects of wide firing range, improved elasticity, and reduced expansion coefficient.

Inactive Publication Date: 2010-03-03
GUANGDONG SHUNXIANG PORCELAIN
View PDF0 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the current glaze raw material formula and production process are relatively old, the surface of fired daily ceramic products is not smooth and bright enough

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Embodiment 1, the present embodiment carries out according to the following steps:

[0033] (1) Batching: prepare the following components according to weight percentage:

[0034] Potassium feldspar: 37%; Kaolin: 11%; Barium carbonate: 4.6%; Strontium carbonate: 2.7%; Lanthanum carbonate: 1.3%; Lithium carbonate: 1.7%; Zinc oxide: 5.7%; Quartz: 36%.

[0035] (2) Ball milling: add the above-mentioned ingredients to a ball mill, add water according to the ratio of material: ball stone: water = 1:1.8:1, and ball mill to form a glaze slurry;

[0036] (3) Iron removal: the above-mentioned glaze slurry is removed in an 18000 Gauss iron remover;

[0037] (4) Sieve: sieve the glaze slurry after iron removal, the fineness of the sieve is 250 mesh, and the sieve residue is less than 0.02%;

[0038] (5) Stale: stale the sieved glaze slurry for 25 hours and set aside.

Embodiment 2

[0039] Embodiment 2, the present embodiment carries out according to the following steps:

[0040] (1) Batching: prepare the following components according to weight percentage:

[0041] Potassium feldspar: 38%; Kaolin: 10%; Barium carbonate: 5%; Strontium carbonate: 2.8%; Lanthanum carbonate: 1.3%; Lithium carbonate: 1.8%; Zinc oxide: 6.1%; Quartz: 35%.

[0042] (2) Ball milling: add the above-mentioned ingredients to a ball mill, add water according to the ratio of material: ball stone: water = 1:1.8:1, and ball mill to form a glaze slurry;

[0043] (3) Iron removal: the above-mentioned glaze slurry is removed in an 18000 Gauss iron remover;

[0044] (4) Sieve: sieve the glaze slurry after iron removal, the fineness of the sieve is 250 mesh, and the sieve residue is less than 0.02%;

[0045] (5) Stale: stale the sieved glaze slurry for 26 hours and set aside.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to daily ceramic glaze with a high refractive rate and a preparation technique thereof, which belongs to the field of the preparation of ceramics. The daily ceramic glaze with high refractive rate comprises the following raw materials by weight percent: 36-38% of potash feldspar, 10-12% of kaolin, 4.5-5.5% of barium carbonate, 2.6-2.8% of strontium carbonate, 1.2-1.4% of lanthanum carbonate, 1.6-1.8% of lithium carbonate, 5.5-6.5% of zinc oxide and 34-36% of quartz. The daily ceramic glaze with high refractive rate is prepared by the steps of proportioning, ball milling,iron removing, sieving, aging and the like according to the mixture ratio of the raw materials. By adopting the daily ceramic glaze with high refractive rate and the preparation technique thereof, thefiring range of the glaze is wide, the glaze is free from the influence of a firing atmosphere, a fired porcelain has gorgeous and delicate colour, the glossiness of a glaze layer is as high as 108,and the quality and the grade of a daily ceramic product are greatly enhanced.

Description

technical field [0001] The invention relates to a high-refractive-index daily-use ceramic glaze composition and a manufacturing process thereof, belonging to the field of ceramic manufacturing. Background technique [0002] With the improvement of people's living standards, the quality and grade requirements of daily-use ceramic products are also getting higher and higher, and the brightness of the ceramic glaze layer is a main reason that directly affects the product grade. Because the current glaze raw material formula and production process are relatively old, the surface of fired ceramic products for daily use is not smooth and bright enough. In order to improve the brightness of the surface of daily-use ceramics, meet consumer demand, and occupy the high-end market, the invention improves the raw material ratio and manufacturing process of the glaze to improve the quality and grade of daily-use ceramics. Contents of the invention [0003] The purpose of the present i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C8/02C04B41/86
Inventor 林伟河
Owner GUANGDONG SHUNXIANG PORCELAIN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com