Low-voltage halogen-free retarding two-wall heat-shrinkage tube and preparation method thereof

Abstract

The invention relates to a heat-shrinkage tube, in particular to a low-voltage halogen-free retarding two-wall heat-shrinkage tube and a preparation method thereof. The low-voltage halogen-free retarding two-wall heat-shrinkage tube comprises an outer wall material and an inner wall material, wherein the outer wall material comprises 60 parts by mass of first polyolefin mixed resin, 10 parts by mass of first assistant, 20 parts by mass of fire retardant and 10 parts by mass of auxiliary fire retardant; and the inner wall material comprises 60 parts by mass of second polyolefin mixed resin, 10 parts by mass of second assistant, 20 parts by mass of fire retardant and 10 parts by mass of auxiliary fire retardant. The preparation method comprises the following steps of preparing, extruding, radiating and expanding to form the inner wall material and the outer wall material of the two-wall heat-shrinkage tube. Compared with the traditional heat-shrinkage tube, the invention has the technical characteristics that because the fire retardant and the auxiliary fire retardant are adopted in the raw materials, the low-voltage halogen-free retarding two-wall heat-shrinkage tube has good retarding property, high temperature resistance, better property, no pollution in combustion, cost reduction and remarkable economic and environmental-friendly benefits, and is suitable for massive popularization and application.

Description

1. Technical field: [0001] The invention relates to a heat-shrinkable tube, in particular to a low-pressure halogen-free flame-retardant double-wall heat-shrinkable tube and a preparation method thereof. 2. Background technology [0002] The heat-shrinkable double-walled tube currently on the market has an inner and outer two-layer structure, which is composed of a flame-retardant polymer outer layer with a shape memory function that can shrink radially after heating and an inner rubber layer that can melt and flow at the shrinkage temperature. After heating, the inner adhesive layer melts and flows to fill. It can be widely used in aviation, aerospace, shipbuilding, automobiles, home appliances, communications, petrochemical and other fields. Anti-corrosion, anti-vibration dislocation and other functions. In the formulation of conventional outer layer materials, halogen-containing flame retardants are used, which have the disadvantages of high smoke generation and high tox...

AI Technical Summary

Problems solved by technology

However, in the prior art, there are many disadvantages of low quality, high cost or poor flame retardant effect for double-walled tubes with halogen-free flame retardants.