High-whiteness bamboo-charcoal viscose fiber and manufacturing method thereof

A technology of bamboo charcoal viscose and a manufacturing method, applied in the field of viscose fiber, can solve the problems such as dyeing of bamboo charcoal viscose fiber fabric and limitation of application fields, and achieve the effect of wide application field

Active Publication Date: 2010-05-19
吉林化纤股份有限公司
View PDF0 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But because bamboo charcoal viscose fiber is made of bamboo charcoal powder, the fiber is dark gray, which makes the dyeing and application fields of bamboo charcoal viscose fabrics subject to greater restrictions.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The raw materials used are 70% bamboo chemical pulp and 30% cotton chemical pulp. After the yellowing is finished, add 0.8 micron particle size and 0.5% Naina white crystal pulp with the dissolving solution. A viscose solution is obtained. The viscose solution is filtered through channels I and II, continuously degassed and filtered through channel III to obtain a spun viscose solution, and the spun viscose solution is introduced into an acid bath. The condition is: H 2 SO 4 110g / L, Na 2 SO 4 325g / L, Zn 2 SO 4 10.8g / L, spun in a coagulation bath with a temperature of 50.5°C, and after post-treatment and drying, high-whiteness bamboo charcoal viscose fibers were obtained.

[0026] The whiteness of the obtained high-whiteness bamboo charcoal viscose fiber is 65%, the antibacterial value (adopting JLS L1902 standard) is 3.5, the far-infrared emissivity is 86%, and the negative oxygen ion is 4000 / cubic centimeter.

Embodiment 2

[0028] The raw material that adopts is the bamboo chemical pulp that accounts for 90% by weight and the wood chemical pulp of 10%, adds particle diameter 3.6 microns along with dissolving liquid after yellowing finishes, and accounts for the Naina white crystal slurry of 5.0% of first kind of cellulose weight The viscose solution is obtained, the viscose solution is filtered through I and II channels, continuous defoaming and III channel filtration to obtain the spinning viscose collagen solution, and the spinning viscose collagen solution is introduced into the acid bath condition as follows: H 2 SO 4 116g / L, Na 2 SO 4 328g / L, Zn 2 SO 4 10.8g / L, spun in a coagulation bath with a temperature of 50.5°C, and after post-treatment and drying, high-whiteness bamboo charcoal viscose fibers were obtained.

[0029] The whiteness of the obtained high-whiteness bamboo charcoal viscose fiber is 67%, the bacteriostasis value (using JLS L1902 standard) is 3.8, the far-infrared emissivi...

Embodiment 3

[0031] The raw material that adopts is the bamboo chemical pulp that accounts for 100% by weight, adopts the pre-spinning injection method, before the spinning process starts after the filtration process finishes, uses the syringe to add particle size 5.0 microns to the spinning viscose collagen liquid, accounting for the first fiber 10.0% Naina white crystal slurry by weight, and the spinning viscose collagen solution is introduced into the acid bath condition as: H 2 SO 4 120g / L, Na 2 SO 4 335g / L, Zn 2 SO 4 11.2g / L, spun in a coagulation bath with a temperature of 51.5°C, and after post-treatment and drying, high whiteness bamboo charcoal viscose fibers were obtained.

[0032] The whiteness of the obtained high-whiteness bamboo charcoal viscose fiber is 68%, the bacteriostasis value (using JLS standard) is 4.0, the far-infrared emissivity is 87%, and the negative oxygen ion is 4800 / cubic centimeter.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a manufacturing method of a high-whiteness bamboo-charcoal viscose fiber, which comprises the following steps: soaking the raw materials mainly comprising bamboo chemical fiber pulp, squeezing, pulverizing, aging, sulfidizing, dissolving, degassing, filtering, spinning into yarn, post-processing and drying; and in the course of processing, adding nano white-crystal pulp, wherein the nano white-crystal pulp accounts for 0.5-10% of the alpha cellulose by weight. In the invention, the nano white-crystal pulp is added in the course of manufacturing the bamboo-charcoal viscose fiber to manufacture the high-whiteness bamboo-charcoal viscose fiber. The prior bamboo-charcoal viscose fiber can be only black or grey; however, the high-whiteness bamboo-charcoal viscose fiber has high whiteness which is greater than or equal to 60%. The high-whiteness bamboo-charcoal viscose fiber can be colored with various dyes, and has the functions of bacterial inhibition, far infrared emission and negative oxygen-ions, thereby having wide application range.

Description

technical field [0001] The invention relates to the technical field of viscose fiber, in particular to a high-whiteness bamboo charcoal viscose fiber and a manufacturing method thereof. Background technique [0002] Bamboo charcoal is an environmentally friendly material developed by bamboo resources. It is made of bamboo after a high-temperature drying and carbonization process at 800 ° C to 1200 ° C. Bamboo charcoal has strong adsorption and decomposition ability, can absorb moisture and dry, deodorize and antibacterial, and can generate a large amount of negative ions. [0003] The manufacture of bamboo charcoal viscose fiber is based on nanotechnology. Firstly, the bamboo charcoal is micronized, and then the nano-scale bamboo charcoal micropowder is processed by high-tech technology, and then combined with the chemical fiber preparation process, spinning and forming, the multifunctional bamboo charcoal can be prepared. Viscose fiber. Bamboo charcoal viscose fiber is si...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F2/08
Inventor 宋德武郑书华李振峰薛振军吕彦松张焕志范美欣范小勇
Owner 吉林化纤股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com