Aqueous polyurethane art painting and preparation method thereof

A water-based polyurethane, ethylene oxide polyurethane technology, used in polyurea/polyurethane coatings, art coatings, coatings, etc., can solve the problems of easy dust contamination, hot stickiness and cold brittleness, temperature sensitivity, etc., and achieves flexibility. , Excellent weather resistance, strong adhesion effect

Inactive Publication Date: 2010-06-30
宋健
View PDF0 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, acrylic paint also has obvious defects. When using acrylic paint for painting, the dry picture is prone to stickiness when the temperature is high in summer, easy to be contaminated with dust, and brittle and easy to damage when the temperature is low in winter.
The performance of acrylate copolymer emulsion has led to such defects in the art paint using it as the base material. The structure of acrylate copolymer is generally a chain linear structure, which is a thermoplastic material and is extremely sensitive to temperature. The formed pigment film cannot withstand Climate changes in winter and summer, prone to hot sticky cold brittle phenomenon
After the painter finishes drying the painting, it may be damaged due to the hot stickiness and brittleness of the picture when saving and assembling the frame. Especially for the artwork drawn by the artist, such defects cannot be tolerated

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] The preparation method of embodiment 1 water-based polyurethane art pigment of the present invention adopts the following processing steps:

[0019] The present invention takes 30 kilograms of water-based polyurethane emulsion (containing 35 ± 1%) of solid content, 20 kilograms of modified ethylene oxide polyurethane emulsion (containing 10 ± 1 percent of solid content), ketone phthalocyanine-blue (a kind of in pigment powder) ) 25 kg, calcium carbonate 10 kg, sodium benzoate 0.2 kg, distilled water 20 kg.

[0020] a. Stir the water-based polyurethane emulsion obtained according to the formula at a slow speed of 100 rpm. While stirring, slowly add modified ethylene oxide polyurethane emulsion to thicken until it is in the form of an ointment to make a rubber base material ;

[0021] B, dissolving sodium benzoate in distilled water, then moisten ketone phthalocyanine-blue (a kind of in the pigment powder) and calcium carbonate with the aqueous solution of this sodium be...

Embodiment 2

[0025] The preparation method of embodiment 2 water-based polyurethane art pigments of the present invention adopts the following processing steps:

[0026] The present invention gets 50 kilograms of water-based polyurethane emulsion (containing 30 ± 1%) of solid content, 15 kilograms of modified ethylene oxide polyurethane emulsion (containing 20 ± 1 percent of solid content), CI pigment red (a kind of in pigment powder) 5 kg, 30 kg of calcium carbonate, 0.5 kg of sodium benzoate and 10 kg of distilled water.

[0027] a. Stir the water-based polyurethane emulsion measured according to the formula at a slow speed of 300 r / min, and slowly add modified ethylene oxide polyurethane emulsion to thicken it until it is in the shape of an ointment, and make a glue base material;

[0028] B, dissolving sodium benzoate in distilled water, then moisten ketone phthalocyanine-blue, calcium carbonate (a kind of in the pigment powder) with the distilled aqueous solution of this sodium benzoa...

Embodiment 3

[0032] The preparation method of embodiment 3 waterborne polyurethane art pigments of the present invention adopts the following processing steps:

[0033] The present invention gets 45 kilograms of water-based polyurethane emulsion (containing 30 ± 1%) of solid content, 5 kilograms of modified ethylene oxide polyurethane emulsion (containing 50 ± 1 percent of solid content), 35 kilograms of titanium dioxide (a kind of in pigment powder), Calcium carbonate 10 kg, sodium benzoate 0.25 kg and distilled water 30 kg.

[0034] a. Stir the water-based polyurethane emulsion measured according to the formula at a slow speed of 200 r / min, and slowly add modified ethylene oxide polyurethane emulsion to thicken it until it is in the shape of an ointment, and make a glue base material;

[0035] B, dissolving sodium benzoate in distilled water, then moisten ketone phthalocyanine-blue (a kind of in pigment powder) and calcium carbonate with the distilled aqueous solution of this sodium benz...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an aqueous polyurethane art painting and a preparation method thereof. The art painting includes the following mass parts of components: 30-50 parts of aqueous polyurethane emulsion,5-20 parts of modified epoxyethane polyurethane emulsion, 5-35 parts of painting powder,10-30 parts of calcium carbonate, 0.2-0.5 part of sodium benzoate and 10-30 parts of distilled water. The steps include; firstly, stirring the aqueous polyurethane emulsion, while adding the modified epoxyethane polyurethane emulsion, so that obtaining ointment-like glue substrate material; then, dissolving the sodium benzoate in distilled water, using sodium benzoate aqueous solution to wet the painting powder and the calcium carbonate, and obtaining painting wet material by stirring; and finally, mixing the ointment-like glue substrate material with the painting wet material, and grinding the mixture to obtain aqueous polyurethane art painting product. The art painting of the invention not only has the advantages of convenient usage, strong adhesion, color stability, and simple reconciliation, but also has the excellent resistance and flexibility of picture film without sticking and cold brittleness.

Description

technical field [0001] The invention discloses a water-based polyurethane art paint for painting, and also discloses a preparation method of the water-based polyurethane art paint. Background technique [0002] In the prior art, among the art paints in the past, the art paints belonging to the water-based series include gouache, watercolor, and acrylic paint. Among them, acrylic paint (the art paint with acrylate copolymer emulsion as the base material) is easy to use and has strong adhesion. It is widely used due to its advantages of stable color and stable color. At the same time, the stroke effect and color depth can be easily adjusted with water or dilute glue solution. However, acrylic paint also has obvious defects. When using acrylic paint for painting, the dry picture is prone to stickiness when the temperature is high in summer, easy to be contaminated with dust, and brittle and easy to damage when the temperature is low in winter. The performance of acrylate copol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04C09D7/12C09D5/06
Inventor 宋健
Owner 宋健
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products