Polymer film sound absorbing material and preparation method thereof
A technology of polymer film and sound-absorbing material, applied in the field of polymer film sound-absorbing material and its preparation, to achieve the effects of simple film-forming process, widening sound-absorbing frequency band, and easy source
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0030] Example 1: Preparation of polyaniline film
[0031] The synthesis reaction equation of basic polyaniline:
[0032]
[0033] Preparation of conductive polyaniline: add aniline and hydrochloric acid solution in a three-necked flask in proportion, and slowly drop the hydrochloric acid solution of ammonium persulfate into the solution under high-speed stirring in an ice water bath. After dripping, keep the reaction temperature at 0°C and react for 7-12 hours. Then stand for 12-16 hours, filter and wash to neutrality, and vacuum dry for later use.
[0034] Therefore, take 10 parts of polyaniline, 2 parts of epoxy resin, 1 part of polyamide resin, 60 parts of N-methylpyrrolidone, and 20 parts of methyl ethyl ketone, make a slurry with ultrasonic, and then apply it to nylon cloth and dry it. Film with a thickness of 0.32 mm. The sound absorption coefficient test results are shown in Table 1.
Example Embodiment
[0035] Example 2: Preparation of polyaniline graphite film
[0036] The preparation of conductive polyaniline was the same as in Example 1. Take 10 parts of polyaniline polymer, 2 parts of epoxy resin, 1 part of polyamide resin, 60 parts of N-methylpyrrolidone, and 20 parts of methyl ethyl ketone according to the ratio of polyaniline: nanographite=1:0.2, and make slurry with ultrasonic , And then coated on nylon cloth, dried into a film with a thickness of 0.35 mm. The sound absorption coefficient test results are shown in Table 1.
Example Embodiment
[0037] Example 3: Preparation of polyaniline graphite film
[0038] The preparation of conductive polyaniline was the same as in Example 1. Take 10 parts of polyaniline polymer, 2 parts of epoxy resin, 1 part of polyamide resin, 60 parts of N-methylpyrrolidone and 20 parts of methyl ethyl ketone according to the ratio of polyaniline: nanographite = 1:0.3, and make slurry with ultrasonic , And then coated on nylon cloth, dried into a film with a thickness of 0.43 mm. The sound absorption coefficient test results are shown in Table 1.
PUM
Property | Measurement | Unit |
---|---|---|
Thickness | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap