Baking-free carbon rammed mass and preparation method thereof

A carbonaceous ramming material, no baking technology, applied in the field of refractory materials, can solve the problems of waste of pig iron, long baking cycle, high labor intensity, etc.

Inactive Publication Date: 2010-09-08
景书贤
View PDF0 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] 1. The labor intensity is high (the shortest time for one pouring is 12-8 hours);
[0004] 2. Long baking cycle (96 hours-168

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0039] A kind of baking-free carbonaceous ramming material of the present invention, comprises particle raw material, micropowder raw material, modified binding agent, phenolic resin:

[0040] The weight components of the original particles of the non-baking carbonaceous ramming material are respectively:

[0041] Raw material name Raw material specification (particle size) Weight component

[0042] Electric calcined anthracite 5-8mm 12-16

[0043] Electric calcined anthracite 3-5mm 12-16

[0044] Metallurgical coke 1-3mm 12-16

[0045] Metallurgical coke 0.01-1mm 12-16

[0046] Described micropowder raw material comprises:

[0047] Micropowder raw material name specification (particle size) weight component

[0048] Metallurgical coke powder 0.075mm 10-20

[0049] Anthracite fine powder 0.075mm 5-10

[0050] Phosphor flake graphite powder 0.024mm 4.5-6.5

[0051] Silicon carbide 0.088mm 4.5-6.5

[0052] 13-18 parts by weight of modified binder; 13-18 parts of phenoli...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a baking-free carbon rammed mass and a preparation method thereof, aiming to provide a baking-free carbon rammed mass which has high carbon content, abrasion resistance, corrosion resistance and convenient construction and conforms to requirements on energy conservation and environment protection. The adopted technical scheme of the invention is as follows: the carbon rammed mass comprises particle raw materials, micropowder raw materials, modified bonding agent and phenolic resin; after being applied, the invention is proved that the baking-free rammed mass in the invention has primary ramming time of 15-25min, thus greatly lowering labor strength and saving labor time; baking is not performed, and tapping can be performed after ramming is finished, thus saving baking cost; the benzopyrene content is no more than 0.05%, thus having no environmental pollution; a primary iron flux period is long (50,000-100,000ton), thus improving service life; and the carbon rammed mass has the advantages of high carbon content, abrasion and corrosion resistance, convenient construction and the like, saves energy and protects environment, and is a substitute of iron trough castables.

Description

technical field [0001] The invention relates to the field of refractory materials, and is suitable for ramming materials for iron troughs in front of iron-making blast furnaces, slag shielding materials, ramming parts above the center line of water-cooled pipes at the bottom of blast furnaces, and gaps between blast furnace linings and steel shells. Tamping and ramming of the leveling layer on the bottom sealing plate of the blast furnace. Background technique [0002] In the prior art, it is used for the ramming material for the iron trough in front of the iron-making blast furnace, the slag shielding device material, the ramming material above the center line of the blast furnace bottom water cooling pipe, and the gap between the blast furnace lining and the steel shell. The ramming material and the ramming material of the leveling layer on the bottom sealing plate of the blast furnace have the following technical defects: [0003] 1. The labor intensity is high (the shor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/66
Inventor 景书贤刘伟景文慧刘瑜
Owner 景书贤
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap