Method for preparing nanosilver/nano silicon dioxide-containing antibacterial biological dressing

A technology of nano-silica and biological dressings, applied in the field of preparation of biomedical materials, can solve the problems of high efficiency, large particle size, and wide size distribution that affect antibacterial performance, and achieve the promotion of wound healing, dense and uniform voids, and high porosity Effect

Inactive Publication Date: 2010-12-15
SOUTH CHINA UNIV OF TECH
View PDF4 Cites 35 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, nano-silver materials prepared by traditional methods have large particle sizes and wide size distributions, which affect the high efficiency of their antibacterial properties.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing nanosilver/nano silicon dioxide-containing antibacterial biological dressing
  • Method for preparing nanosilver/nano silicon dioxide-containing antibacterial biological dressing
  • Method for preparing nanosilver/nano silicon dioxide-containing antibacterial biological dressing

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] In 200mL of absolute ethanol, add 1.0g of silicon dioxide dried at 120°C, and stir evenly. Add 1.0 mL of water and 0.054 g of sodium hydroxide, and stir for 24 hours in a constant temperature water bath environment at 25°C. Add 20 mL of 7.6 g / L ethanol solution of silver nitrate dropwise at a constant speed for 30 min, react for 10 min, centrifuge, wash with ethanol, and dry to obtain silver-loaded silica powder.

[0026] 0.05g of chitosan was dissolved in 5% dilute acetic acid aqueous solution by volume to prepare a chitosan solution with a mass fraction of 1.0%. Dissolve 0.05 g of polyvinyl alcohol in boiling water to prepare a polyvinyl alcohol solution with a mass fraction of 1.0%. The above chitosan solution and polyvinyl alcohol solution are mixed at a volume ratio of 1:1 and then fully stirred to obtain a polyvinyl alcohol / chitosan blend. Weigh 20g of polyvinyl alcohol, dissolve it in 200mL of boiling water, cool down to 50°C, add 0.20g of sodium lauryl sulfate...

Embodiment 2

[0030] In 280mL of absolute ethanol, add 0.5g of silicon dioxide dried at 120°C, and stir evenly. Add 2.0 mL of water and 0.054 g of sodium hydroxide, and stir for 24 hours in a constant temperature water bath environment at 25°C. Add 30 mL of 7.6 g / L ethanol solution of silver nitrate dropwise at a constant speed for 40 min, react for 10 min, centrifuge, wash with ethanol, and dry to obtain silver-loaded silica powder.

[0031]Dissolve 0.05g of chitosan in 5% dilute acetic acid aqueous solution to prepare a chitosan solution with a mass fraction of 1.0%. Dissolve 0.05 g of polyvinyl alcohol in 5 ml of boiling water to prepare a 1.0% polyvinyl alcohol solution. The above chitosan solution and polyvinyl alcohol solution are mixed at a volume ratio of 1:1 and then fully stirred to obtain a polyvinyl alcohol / chitosan blend. Weigh 20g of polyvinyl alcohol, dissolve it in 120mL of boiling water, cool down to 35°C, add 0.10g of sodium lauryl sulfate, 20mL of formaldehyde with a ma...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for preparing a nanosilver / nano silicon dioxide-containing antibacterial biological dressing, and relates to the field of antibacterial biological dressings. The nanosilver / nano silicon dioxide-containing antibacterial biological dressing is prepared by adding mixed solution of chitosan and polyvinyl alcohol and silver-carried silicon dioxide powder during the acetalation of the polyvinyl alcohol. The nanosilver / nano silicon dioxide-containing antibacterial biological dressing of the invention can accelerate the wound healing, slowly release the silver nanoparticles and continuously act on reproductive bacteria, has the characteristic of durable and high-efficiency sterilization and does not produce medicament resistance; and through the researches on the toxicity of the material to mouse fibroblast cells, the product does not produce obvious toxicity to the cells but promotes the growth of the cells.

Description

technical field [0001] The invention relates to a preparation technology of biomedical materials, in particular to a preparation method of an antibacterial biological dressing containing nanometer silver / nanometer silicon dioxide, which is suitable for wound treatment. Background technique: [0002] A medical dressing is a protective covering over a wound to help control bleeding, prevent infection, and absorb secretions. Modern medical biological dressings are new types of wound repair and protection materials developed on the basis of the "moist healing" theory of wound repair by Winter and Hinman. Compared with traditional medical dressings (such as absorbent cotton yarn), modern medical biological dressings have accelerated wound healing. Healing, avoiding wound adhesion, promoting tissue repair, antibacterial and anti-inflammatory and other characteristics. In the treatment of burns, the use of antibacterial dressings containing antibacterial drugs is still one of the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A61L15/28A61L15/24A61L15/18A61L15/44C08F16/06C08F8/28C08K9/12
Inventor 魏坤曾晓峰
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap