Method for manufacturing medium and high-voltage anode aluminum foil for aluminum electrolytic capacitor

An aluminum electrolytic capacitor, anode aluminum foil technology, applied in electrolytic capacitors, capacitors, circuits, etc., can solve the problems of thermal expansion and deformation of light foil, affecting the service life of copper rolls, increasing production costs, etc., to prevent thermal deformation, reduce heating, Increase the effect of specific volume

Inactive Publication Date: 2011-01-19
南通华冠电子科技有限公司
View PDF4 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When corroding the pores once, the light foil is sent from the copper roll to the acid tank for DC electrolytic corrosion. The DC current is generally greater than 5000A, so it is easy to cause heat expansion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] The present invention will be further described below in conjunction with the accompanying drawings and embodiments.

[0019] The manufacturing method of the middle and high voltage anode aluminum foil for aluminum electrolytic capacitor of the present invention comprises the following steps successively:

[0020] 1) Provide 65-130um thick light foil, and pre-treat the light foil;

[0021] 2) Put the light foil into the acidic solution with the ratio of chloride ion and sulfate ion at 5-15:1, and apply a current density of 60-100mA / cm 2 The AC current is used to corrode the pores once; then it is put into the acidic solution with the ratio of chloride ion and sulfate ion at 1:9.5~16, and the applied current density is 250~300mA / cm 2 Direct current is used to corrode pores once; among them, the concentration of hydrochloric acid is 2-15%, and the concentration of sulfuric acid is 2-10%;

[0022] 3) Carry out secondary corrosion expansion in an acidic solution after the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for manufacturing a medium and high-voltage anode aluminum foil for an aluminum electrolytic capacitor, which sequentially comprises the following steps of: 1) pretreating an optical foil; 2) putting the optical foil into acid solution in a ratio of chloride ion to sulfate ion of 5-15:1, then applying an alternating current with the current density of 60 to 100mA/cm<2> to the optical foil for primary corroding and hole forming, then putting the optical foil into acid solution in the ratio of the chloride ion to the sulfate ion of 1:9.5-16, and then applying a direct current with the current density of 250 to 300mA/cm<2> to the optical foil for primary corroding and hole forming; 3) after primary cleaning, performing secondary corroding and reaming on the optical foil in the acid solution; 4) after secondary cleaning, drying the optical foil by using a drying furnace to obtain the corroded foil finished product; and 5) performing conversion coating on the corroded foil finished product to obtain the medium and high-voltage anode aluminum foil finished product. In the method for manufacturing the medium and high-voltage anode aluminum foil for the aluminum electrolytic capacitor provided by the invention, the surface dislocation and defect parts of the optical foil are subjected to pitting by the alternating current, and then the optical foil is subjected to primary corroding and hole forming by the direct current, so that heating is reduced, the deformation of the aluminum foil because of heating is prevented, the surface expansion rate of the aluminum foil is increased, and specific volume is improved greatly.

Description

technical field [0001] The invention relates to a method for manufacturing an anode aluminum foil, in particular to a method for manufacturing a medium-high voltage anode aluminum foil for an aluminum electrolytic capacitor. Background technique [0002] With the rapid development of the electronic industry, the application of aluminum electrolytic capacitors is more extensive, and the performance requirements are getting higher and higher. Corrosion formed foil for aluminum electrolytic capacitors is the main electronic material for basic components in the electronic information industry, and the market for aluminum foil for medium and high voltage aluminum electrolytic capacitors is in short supply. As a corroded foil for medium and high voltage electrolytic capacitors with a rated voltage exceeding 200V, the quality requirements are high and the production is difficult. There are only a few manufacturers in China, but the performance cannot meet the user's requirements. T...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01G9/055
Inventor 张方亭
Owner 南通华冠电子科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap