Method for recycling secondary lead by electrolyzing alkaline leaded solution

A technology for regenerating lead and solution, applied in the field of hydrometallurgy, can solve the problems of high DC power consumption, high acid electrolytic corrosion, unacceptable to manufacturers, etc., to reduce energy consumption, avoid secondary pollution, and achieve continuous and fully enclosed industrial production. Effect

Inactive Publication Date: 2011-01-26
BEIJING UNIV OF CHEM TECH
View PDF13 Cites 52 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0013] (2) The DC power consumption of acid electrolysis is relatively high, and the power consumption per ton of recycled lead is as high as 600-1000KWh, which is 550KWh higher than that of the fire method;
[0014] (3) Acidic electrolysis is highly corrosive, making it difficult for manufacturers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for recycling secondary lead by electrolyzing alkaline leaded solution
  • Method for recycling secondary lead by electrolyzing alkaline leaded solution
  • Method for recycling secondary lead by electrolyzing alkaline leaded solution

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0117] Take 10 pieces of 12V, 12Ah waste lead-acid batteries for electric vehicles purchased on the market. The total weight of the battery pack is 45.5 kg. The specific implementation process is as follows:

[0118] 1) After discharging the 10 batteries, they are put into a crusher to be broken, and the water phase is separated by density difference to obtain lead paste, grids, waste sulfuric acid, separators and shells.

[0119] 2) Put the pressure-filtered lead paste into a crusher and a ball mill in turn for smashing, and then use a 60-mesh stainless steel screen for sieving. The larger lead paste particles continue to be transferred to the crusher for crushing until all the lead paste is Through the screen.

[0120] 3) Take 40L of waste sulfuric acid obtained in the process of (1), after supplementing a small amount of concentrated sulfuric acid, adjust it to contain 5mol / L H 2 SO 4 , 0.5mol / L Fe(ClO 4 ) 2 And 0.5mol / L HClO 4 . Take 26 kilograms of lead paste powder and waste ...

Embodiment 2

[0127] Take a 12V, 54Ah lead-acid battery from a used automobile. The total weight of the battery pack is 15.5 kg. The specific recycling process is as follows:

[0128] According to the procedures (1) and (2) of Example 1, the lead paste, grids, spacers and plastics were separated.

[0129] 3) Take 12L of waste sulfuric acid obtained in the above process and adjust its acidity to a mixed solution containing 4.0mol / L sulfuric acid, 1mol / L ferrous perchlorate and 1mol / L perchloric acid. Take 6 kg of lead paste powder and waste sulfuric acid solution obtained by screening in (2), mix the two, and add 4.0mol / L sulfuric acid, 0.8mol / L ferrous perchlorate and 0.8mol / L perchloric acid at the same time The mixed solution was reacted at 85°C for 4 hours. The reaction is stopped when the detection potential drops to 0.25V.

[0130] 4) Lead sulfate obtained after centrifugal separation of the reaction liquid of the process (3), and a mother liquor containing ferrous perchlorate, ferric perch...

Embodiment 3

[0136] Take 2 kilograms of lead-containing waste from the lead-acid battery production workshop of a company in Hebei and pulverize it into powder by a ball mill. It is determined that it is mainly 95% lead oxide (PbO), 3% lead and a small amount of clay. The process of regenerating lead is as follows:

[0137] 1) After ball milling the above-mentioned lead-containing waste powder in an air atmosphere for 3 hours, sieving with a 60-mesh screen to obtain fine powder, then adding 20 L of 29% NaOH solution, and performing leaching reaction at 100°C. In this process, the lead oxide in the waste and a small amount of lead oxidation newly formed lead oxide and NaOH undergo a complex reaction to form Na 2 [Pb(OH) 4 ]. Measured by EDTA chemical titration, Na 2 [Pb(OH) 4 ] Part of the lead content is 99g / L, and about 0.05 kg of clay-like precipitate remains after filtration.

[0138] 2) The lead-containing mother liquor obtained in the process (1) is purified and then enters an electrolyti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for recycling secondary lead by electrolyzing an alkaline leaded solution. Leaded alkaline electrolyte is directly obtained by prepositive catalytic conversion and alkalinity desulfuration leaching processes; and then the leaded alkaline electrolyte is subjected to fractional electrolysis in an ion film electrolyser, thus directly obtaining the high-purity metal lead and byproducts of oxygen gas and sodium sulfate decahydrate. The method in the invention is a novel technology which has the advantages of energy conservation and large-scale industrialization application prospect.

Description

Technical field [0001] The invention relates to a method for recovering regenerated lead by alkaline electrolysis of a lead-containing solution, belonging to the field of hydrometallurgy for recovering lead from lead-containing materials and waste lead-acid batteries. Background technique [0002] Since lead-acid batteries were proposed by French engineer Plante in 1859, lead-acid batteries have been widely used in electric vehicles, automobiles, uninterruptible UPS power supplies, etc., as a cheap and reliable rechargeable battery. In recent years, despite the competition between lithium-ion batteries and nickel-metal hydride batteries, lead-acid batteries have always been at the top of secondary batteries, accounting for nearly 60% of the global output value of secondary batteries. According to statistics from power industry associations, China's lead consumption reached more than 3.5 million tons in 2009, accounting for more than 23% of the world's total lead consumption. The...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C25C1/18
CPCY02E60/12Y02P10/20Y02W30/84
Inventor 潘军青孙艳芝张超
Owner BEIJING UNIV OF CHEM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap