Moxibustion patch and preparation method thereof
A patch, one-sided technology, used in pharmaceutical formulations, other medical devices, medical preparations containing active ingredients, etc., can solve problems such as contaminated clothing, and achieve the effect of restoring health and vitality, dredging meridians, and avoiding volatilization loss.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0025] Example 1
[0026] In parts by weight, weigh 15 parts of fumed silica and 3 parts of mugwort oil, mix them evenly, add 81 parts of polyacrylate emulsion with a mass concentration (g / L) of 40%, and then add 0.01 part of antioxidant vitamin E , Fully disperse and mix, and then add 1 part of FS-20C viscosity modifier produced by Dandong Star Fine Chemical Co., Ltd. to thicken the liquid to a viscosity of 100,000 centipoise to obtain a thick slurry;
[0027] Coat the above thick slurry on one side of the non-woven fabric substrate, the coating amount is about 160g / m2, and hot-air bake at about 60℃ until it is cured and formed into a film to obtain an essential oil sustained-release film. The other side of the cloth substrate is coated with hot-melt pressure-sensitive adhesive, then covered with release paper, and die-cut into pieces to obtain the essential oil sustained-release film;
[0028] Remove the release paper from the essential oil sustained-release film, and then attach ...
Example Embodiment
[0030] Example 2
[0031] In parts by weight, weigh 6.0 parts of polyvinyl alcohol, 70 parts of water, and 1 part of glycerin, mix, and heat to 100°C to dissolve to obtain a mixed solution of polyvinyl alcohol. Add 19 parts of kaolin, 1 part of titanium dioxide, and 1 part of cinnamon oil. Part of the pre-prepared powder is fully dispersed and evenly dispersed, and then 0.1 part of antioxidant di-tert-butyl hydroxytoluene and 2 parts of propylene glycol alginate viscosity modifier are added to adjust the viscosity of the material to 100,000 cps to obtain a thick slurry ;
[0032] Coat the above thick slurry on one side of the non-woven fabric substrate, the coating amount is about 200g / m2, and hot air bake part of the water at about 60°C to solidify and form a film to obtain an essential oil sustained-release film. Coat the other side of the substrate with hot-melt pressure-sensitive adhesive, then cover with release paper, and die-cut into pieces to obtain the essential oil susta...
Example Embodiment
[0034] Example 3
[0035] In parts by weight, weigh 4 parts of sodium polyacrylate, 85 parts of water, 0.6 parts of aluminum hydroxide and 5 parts of glycerin, dissolve to obtain a mixed solution of sodium polyacrylate, add 10 parts of light calcium carbonate, 1 part of titanium dioxide, 2 parts of juniper oil and 0.3 parts of antioxidant butyl hydroxyanisole are pre-prepared powder, which is fully dispersed and evenly distributed to obtain a thick slurry with a viscosity of 100,000 cps;
[0036] Coat the above thick slurry on a non-woven fabric substrate with a coating amount of about 200g / m2. At about 60℃, hot air bake part of the water to solidify and form a film to obtain an essential oil sustained-release film. The other side of the woven fabric substrate is coated with hot-melt pressure-sensitive adhesive, then covered with release paper, and die-cut into pieces to obtain the essential oil sustained-release film;
[0037] Remove the release paper from the essential oil sustain...
PUM
Property | Measurement | Unit |
---|---|---|
Viscosity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap