Preparation method of polyisobutene with medium molecular weight in boron trifluoride initiating system
A technology for initiating system and polyisobutene, applied in the field of preparation of medium molecular weight polyisobutene, can solve the problems of difficult control of isobutene and unstable product quality, and achieve the effects of improved molecular weight distribution, high conversion rate and wide adjustment range
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0011] 500 milliliters of there-necked flasks are equipped with attachments such as stirring and a thermometer, after this there-necked flasks are evacuated and nitrogen replacement is qualified, to wherein adding the mixture of 192 grams (300ml) of isobutylene and hexane, wherein isobutylene concentration is 35wt.%. h 2 0 content is 1.39×10 -3 mol / kg, the methanol content in isobutene is 1.56×10 -3 mol / kg isobutene. Cool the polymerization solution in the three-necked flask to -35°C through a low-temperature bath, start stirring and add 9.07×10 -3 g NH 3 Gas, then add 0.03 g of BF 3 , control the polymerization reaction temperature in the three-necked flask at -35°C to -30°C, after 40 minutes of reaction, terminate and wash with 300ml of water, and introduce the mixture into a separatory funnel to remove the water phase. After the glue solution was filtered, the solvent was distilled off to obtain medium molecular weight polyisobutylene with a viscosity average molecular...
Embodiment 2
[0013] Repeat the method described in Example 1, except that the polymerization temperature in the there-necked flask is controlled at -30°C to -25°C to obtain a medium molecular weight polyisobutylene with a viscosity average molecular weight (Mv) of 84,000mm.
Embodiment 3
[0015] Repeat the method described in Example 1, the difference is to add 0.043 gram of BF 3 , Obtaining a viscosity-average molecular weight (Mv) is 55,000-medium molecular weight polyisobutylene.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com