An inorganic glass fiber reinforced plastic and magnesite technology, applied in the field of magnesite inorganic glass fiber reinforced plastic, can solve the problems of easy weathering on the surface of the product, decreased structural strength, pulverization and other problems, and achieves the effects of low moisture absorption rate, increased strength, and high product quality.
Inactive Publication Date: 2011-05-18
HAIMEN KANGDIXIN ENVIRONMENTAL PROTECTION EQUIP
View PDF0 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
The biggest disadvantage of magnesium chloride is that it will return to halogen when it encounters high temperature and humidity.
The main raw materials of magnesite products are magnesium oxide and magnesium chloride, but magnesium chloride contains a large amount of sodium chloride, and the sodium ions in the crystal voids can move, making the surface of the product easy to weather, deliquescence, and even lose luster, and pulverization occurs. Significant decrease in structural strength
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0016] Magnesite inorganic glass of the present invention is prepared in the following manner:
[0017] 1. Ingredients:
[0018] (1) Proportion: magnesia 50%-70% (magnesia Mgo active ingredient accounts for 85%)
[0019] Solid 10%-25% low alkali cement
[0020] Medical gypsum 20%-30% (hemihydrate gypsum)
[0021] Urea-formaldehyde glue 8%
[0022] Phosphoric acid 1%
[0023] Ammonium Chloride 1% (catalyst)
[0024] Mgcl 2 9% glass magnesium degree 28 or so
[0025] (2) Modulation: The above seven solids and liquids are strictly configured according to the ratio, and the pH value is controlled at about 7. Mgcl 2 The wave magnesium degree is controlled at about 28 (as the temperature changes, corresponding adjustments should be made, and the above-mentioned seven solids and liquids also have different adjustments), put it into a container and mechanically stir it evenly.
[0026] 2. Paste system:
[0027] Apply the prepared slurry on the glass fiber mesh cloth of the p...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention provides a magnesite fiber reinforced inorganic material. The magnesite fiber reinforced inorganic material is characterized by comprising the following raw materials in percentage by weight: 50 to 70 percent of magnesia, 10 to 25 percent of solid low-alkali cement, 20 to 30 percent of hemihydrate gypsum, 8 percent of urea-formaldehyde glue, 1 percent of phosphoric acid, 1 percent of ammonium chloride and 9 percent of magnesium chloride (MgCl2), and comprising a platinum clamp pot glass fiber grid cloth. The magnesite fiber reinforced inorganic material mainly has the following advantages: attractive appearance and modeling, no burr, smooth inside and outside, acid and alkali-resistance, corrosion resistance, high temperature resistance, freeze-tolerance, insolation resistance, aging resistance, no cracking, no toxicity, no pollution, no rust, no fracture, long service life, sound absorption, sound insulation, flame retardancy, fire resistance, capacity of being sawn, drilled, nailed, cut and scraped, simple preparation method, easily obtained raw materials, low cost, light weight, wide application, and capacity of being made into various products in different shapes, different specifications and different colors.
Description
technical field [0001] The invention relates to a magnesite inorganic glass steel, in particular to a ratio and a preparation method of the magnesite inorganic glass steel. Background technique [0002] Inorganic FRP, also known as FRIM (Fiber Reinforced Ionorganic Material), is a glass fiber reinforced magnesium oxychloride cement inorganic composite material. It is not made of organic resin but a composite material that uses inorganic materials as reinforcing materials. Its main materials are inorganic raw materials magnesia (the main component is magnesium oxide), brine (magnesium chloride aqueous solution), and medium-alkali glass fiber cloth. [0003] Inorganic FRP has various excellent properties, such as low cost, easy production and forming, fire prevention, waterproof, environmental protection, non-toxic, no peculiar smell, no deformation, no cracking, no broken, no paint peeling, no leakage, high and low temperature resistance, Inexpensive and widely used. Inorg...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.