Simple vanadium nitride production method

A production method and technology of vanadium nitride, applied in the direction of nitrogen-metal/silicon/boron binary compounds, etc., can solve the problems of low nitrogen content in products, low life of furnace lining, poor controllability, etc., and achieve wide source of raw materials, atmosphere The effect of convenient control and high productivity

Inactive Publication Date: 2011-09-07
河北钢辰冶金材料有限公司
View PDF2 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] The disadvantages of the above production method are: complex process,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0024] A simple and easy production method of vanadium nitride, the process steps are: 1. V 2 O 5 The powder and graphite powder are fully mixed on a dry mixer at a weight ratio of 4:1. ② Add a 4% polyvinyl alcohol aqueous solution to the above mixed powder at a weight ratio of 100:15, and mix in a wet mixer for 10 minutes. , ③ Press the wet mixed powder into balls, ④ Dry the mixed powder wet balls, ⑤ Load the dried mixed powder balls into the feeding truck, enter the furnace, and seal the furnace door in layers, ⑥ Evacuate to -0.02MPa, ⑦ Introduce nitrogen pressure to 0.04MPa, ⑧ heat to 800 ℃ and carry out pre-reduction at this temperature for about 5 hours, ⑨ then continue to heat up to 1350 ℃ for no less than 6 hours of deep reduction and carbonization, in the process of continuous charging Enter nitrogen with a purity of more than 99.99%, ⑩ heat up to 1600 °C for 6-10 hours of nitriding and sintering, the pressure in this process is controlled at 0.02Mpa, and the total ti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a simple vanadium nitride production method, which comprises the following steps of: (1) fully mixing vanadium pentoxide (V2O5) powder and graphite powder in a weight ratio of 4:1 on a dry mixer; (2) adding 4 percent of polyvinyl alcohol aqueous solution into mixed powder in a weight ratio of 100 to 15, and mixing the polyvinyl alcohol aqueous solution and the mixed powderin a wet mixer for 10 minutes; (3) carrying out ball pressing on the wet-mixed mixed powder; (4) drying wet balls of the mixed powder; (5) loading the dried balls of the mixed powder into a charging vehicle in a layered mode and then into a furnace, and sealing a furnace door; (6) vacuumizing until a pressure is equal to -0.02 megapascal (MPa); (7) introducing nitrogen until the pressure is equalto 0.04 MPa; (8) heating to 800 DEG C, and carrying out pre-reduction for about 5 hours at the temperature; (9) then keeping heating to 1,350 DEG C, continuing deep reduction and carbonization for atleast 6 hours, and continuously introducing the nitrogen with the purity of over 99.99 percent in process; and (10) carrying out nitridation sintering for 6 to 10 hours after the temperature rises to1,600 DEG C, controlling the pressure to 0.02 MPa in the process, cutting off power for cooling, and taking vanadium nitride out of the furnace until the temperature is equal to 150 DEG C.

Description

technical field [0001] The invention relates to a production method of vanadium nitride alloy, in particular to a simple and simple production method of vanadium nitride. Background technique [0002] The traditional preparation method of VN alloy is based on the oxide V of vanadium 2 o 3 , V 2 o 5 and vanadium compound ammonium vanadate (NH 4 VO 3 ), ammonium polyvanadate, etc. as raw materials, using carbonaceous, hydrogen, ammonia, CO, etc. as reducing agents, reducing at high temperature or vacuum, and then nitrogen or ammonia for nitriding. The method of preparing vanadium nitride can be divided into two categories: high-temperature vacuum method and high-temperature non-vacuum method according to the different preparation systems and conditions. In each category, it can be divided into C and V according to the different raw materials used. 2 o 3 , C and V 2 o 5 , NH 4 and VO 3 Process for preparing vanadium nitride for solid reactants. [0003] The United S...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C01B21/06
Inventor 王安仁卢世国张来顺
Owner 河北钢辰冶金材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap