Magnetic fluorescent difunctional nano material based on natural polymer and preparation method thereof
A technology of natural polymers and nanomaterials, applied in luminescent materials, nanotechnology for materials and surface science, and magnetism of organic materials/organic magnetic materials, etc., can solve the problem of poor biocompatibility of magnetic fluorescent nanomaterials, magnetic fluorescence The application of nanomaterials is limited, the preparation process is complicated and difficult, etc., to achieve good biocompatibility and degradability, renewable raw material sources, and good biocompatibility.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0039] Example 1:
[0040] The magnetic fluorescent dual-function nanomaterial based on natural polymer and its preparation method, the specific steps are as follows:
[0041] 1) Magnetic fluid nano Fe 3 O 4 Synthesis
[0042] Using co-precipitation method, weigh out 1.5g FeCl 3 ·6H 2 O, 0.6gFeSO 4 ·4H 2 O, dissolved in deionized water degassed by nitrogen beforehand, and pass N 2 Protect, heat to 70℃, then quickly stir and slowly add 5ml ammonia water. After reacting for 1 hour, the resulting precipitate was separated from the reaction medium by an external magnetic field, and washed three times with secondary water to obtain nano-Fe 3 O 4 Suspension, ultrasonic 15min, the black solution obtained is nano Fe 3 O 4 Magnetic fluid.
[0043] 2) Chitosan-Fe 3 O 4 Preparation of nanospheres
[0044] Take 0.15gFe 3 O 4 The magnetic fluid was mixed with 20 mL of 7.5 mg / mL chitosan (CS) acetic acid solution, and ultrasonically dispersed for 20 minutes. Under stirring, slowly add to the mixtur...
Example Embodiment
[0050] Example 2:
[0051] The magnetic fluorescent dual-function nanomaterial based on natural polymer and its preparation method, the specific steps are as follows:
[0052] 1) Magnetic fluid nano Fe 3 O 4 Synthesis
[0053] Using co-precipitation method, weigh 1.3g FeCl 3 ·6H 2 O, 0.5gFeSO 4 ·4H 2 O, dissolved in deionized water degassed by nitrogen beforehand, and pass N 2 Protect, heat to 69°C, then quickly stir and slowly add 6mL ammonia. After reacting for 1 hour, the resulting precipitate was separated from the reaction medium by an external magnetic field, and washed three times with secondary water to obtain nano-Fe 3 O 4 Suspension, ultrasonic for 20min, the black solution obtained is nano Fe 3 O 4 Magnetic fluid.
[0054] 2) Chitosan-Fe 3 O 4 Preparation of nanospheres
[0055] Take 0.15gFe 3 O 4 The magnetic fluid was mixed with 12 mL of 12 mg / mL chitosan (CS) acetic acid solution, and ultrasonically dispersed for 15 minutes. Under stirring, slowly add to the mixture of 5...
Example Embodiment
[0061] Example 3:
[0062] The magnetic fluorescent dual-function nanomaterial based on natural polymer and its preparation method, the specific steps are as follows:
[0063] 1) Magnetic fluid nano Fe 3 O 4 Synthesis
[0064] Using the co-precipitation method, weigh 1.4g FeCl 3 ·6H 2 O, 0.5gFeSO 4 ·4H 2 O, dissolved in deionized water degassed by nitrogen beforehand, and pass N 2 Protect, heat to 70℃, then quickly stir and slowly add 6ml ammonia water. After reacting for 1.5h, the resulting precipitate was separated from the reaction medium by an external magnetic field, and washed three times with secondary water to obtain nano-Fe 3 O 4 Suspension, ultrasonic for 25min, the black solution obtained is nano Fe 3 O 4 Magnetic fluid.
[0065] 2) Chitosan-Fe 3 O 4 Preparation of nanospheres
[0066] Take 0.13gFe 3 O 4 The magnetic fluid was mixed with 24 mL of 5 mg / mL chitosan (CS) acetic acid solution, and ultrasonically dispersed for 20 minutes. Under stirring, slowly add to the mixtur...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Saturation magnetic strength | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap