Environment-friendly type urea-formaldehyde resin adhesive and production method thereof

A technology of urea-formaldehyde resin and production method, which is applied in the directions of adhesives, aldehyde/ketone condensation polymer adhesives, adhesive types, etc. High strength, excellent water resistance, versatile effect

Inactive Publication Date: 2011-11-02
王喆
View PDF3 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] But the biggest disadvantage of UF adhesives is the high content of free formaldehyde, which not only pollutes the environment but also endangers people's health.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0022] Take 175 grams of glyoxal with a content of 40% and place it in a 1000 ml three-neck flask, add 45 grams of urea and 15 grams of 10% polyvinyl alcohol 2088 solution under stirring, raise the temperature to 50°C to stop heating, and pass through the methyl alcohol in six times. Tetramine to adjust pH value 7.5~8.5 , and react for 40 minutes when the temperature is raised to 80~90°C. Then 15 grams of the remaining 25% urea was added, and the reaction was continued for 40 minutes, and then the pH was adjusted with formic acid to 5.5~6.5 And in 70~80 The end point is when a milky white thick liquid appears in the reaction at ℃ or when a drop of the reaction solution is added to a cup of water at 40 ℃ and stirred to form a cloud. Adjust the pH with NaOH to 7.0~8.0 , After cooling to below 40°C, it will be finished product after being packaged.

[0023] Relevant performance indicators of urea glyoxal resin adhesive:

[0024] Name Indicator

[0025] Appearance Brown-yell...

example 2

[0031] Take 200 grams of 40% glyoxal and place it in a 1000 ml three-necked bottle, add 54 grams of urea and 35 grams of 10% polyvinyl alcohol 2099 solution under stirring, stop heating after raising the temperature to 50 ° C, adjust with hexamethylenetetramine PH value 7.5~8.5 Then warm up to 80~90 ℃ for 40 minutes, the remaining 30% of urea 23 grams continued to add, after 40 minutes of reaction, use 1:1 hydrochloric acid to adjust the pH to 5.5~6.5 , and at 70~80 The end point is when a milky white thick liquid appears in the reaction at ℃ or when a drop of the reaction solution is added to a cup of 40 ℃ water and stirred to appear cloudy. Adjust the pH with sodium hydroxide to 7.0~8.0 , After cooling to below 40°C, it will be the finished product after being packaged.

[0032] The method of use and relevant technical parameters are the same as those of the previous photobook, so they are omitted.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

An environment-friendly type urea-formaldehyde resin adhesive and a production method thereof. The method comprises the following steps: mixing glyoxal with urea in a container according to a certain mol ratio; adding a 10% polyvinyl alcoholic solution prepared in advance and urea under agitation, adjusting the pH value of the solution to be 7.5 to 8.5, and heating the solution to a temperature of 80 to 90 DEG C for reaction; adding a proper amount of urea for reaction for 40 minutes, adjusting the pH value of the solution to be 5 to 6, subjecting the solution to reaction at a temperature of 70 to 80 DEG C, and stopping the reaction when opacified sticky liquid appears or when cloudy sticky liquid appears under the condition that a droplet of the reaction solution is added into a glass with water at a temperature of 40 DEG C; cooling the solution to a temperature less than 40 DEG C and packaging the discharged products so as to obtain finished products. The adhesive provided in the invention belongs to excellent environment-friendly decoration materials, has remarkable adhesive properties, little smell, great initial adhesion, high final strength, good endurance and appropriate viscosity, is easy to paint and stable to store, and enables a glue film to be tough and tensile. Woodwork glued by the adhesive has no obvious glue lines, has excellent water tolerance, and produces no cracking in long-term usage.

Description

technical field [0001] The invention relates to the technical field of adhesives, in particular to an environment-friendly urea-formaldehyde resin adhesive and a production method thereof. It is mainly used for bonding woodworking furniture, various wood-based panels, glulam processing, advanced solid wood composite floor bonding, decoration and many other aspects, and has a wide range of applications. Background technique [0002] With the rapid development of my country's wood industry, it has become the world's largest wood-based panel production country. At present, most of the glue used in the domestic wood industry uses urea-formaldehyde glue, phenolic glue, melamine-formaldehyde glue and polyvinyl acetate glue. Their bonding strength is poor, the bonding surface is hard, brittle, non-tough, not waterproof, not durable, etc., and they are also poisonous. Pollution environment, hot eyes and pungent smell. Among all kinds of adhesives, urea-formaldehyde resin adhesives...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J161/32C08G12/40
Inventor 王喆王越王学谦
Owner 王喆
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com