Environmentally-friendly acid-etching and descaling conditioning fluid used for bimetal composite wire processing

A composite wire, environment-friendly technology, applied in the field of metal surface treatment, can solve the problems of excessive fluoride ions, operator hazards, environmental pollution, etc., and achieve the effects of promoting the acid etching process, reducing release, and reasonable compatibility

Inactive Publication Date: 2011-11-09
HANGZHOU ZHENDA HARDWARE MACHINERY
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the commonly used acid etching solutions in the prior art all contain high concentrations of fluoride, which will release a certain concentration of hydrogen fluoride in the operating environment, and excessive fluoride ions will be generated in the waste liquid produced
Not only will it cause environmental pollution, but it will also cause harm to operators.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0008] The environment-friendly acid etching and descaling treatment solution for bimetallic composite wire processing includes the following components: HNO with a concentration of 68% 3 Solution: 500-600ml / L; H 3 PO 4 : 300-350ml / L; inorganic ammonium salt: 10-15g / L; organic amine-containing compound 15-25g / L; surfactant: 5-10g / L; the balance is water. The optimized components of this treatment solution are as follows: the concentration is 68% HNO 3 Solution: 550-580ml / L; H 3 PO 4 : 320-340ml / L; inorganic ammonium salt: 12-14g / L; organic amine-containing compound 18-22g / L; surfactant: 7-9g / L; the balance is water.

[0009] In the present embodiment, the concentration is 68% HNO 3 Solution: 550ml / L; H 3 PO 4 : 320ml / L; inorganic ammonium salt: 12g / L; organic amine-containing compound 20g / L; surfactant: 8g / L; the balance is water.

[0010] The treatment solution does not contain high concentration of fluoride ions, and adding suitable surfactants promotes the acid etch...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of metal surface treatment, relates to aluminium magnesium alloy material surface treatment, and in particular relates to an environmentally-friendly acid-etching and descaling conditioning fluid used for bimetal composite wire processing. According to the conditioning fluid, the technical problems of unreasonable prior art and the like can be solved. The conditioning fluid comprises the following components: 500-600ml / L of 68% HNO3 solution, 300-350ml / L of H3PO4, 10-15g / L of inorganic ammonium salt, 15-25g / L of organic amido-contained compound, 5-10g / L of surfactant and the balance of water. The conditioning fluid has the advantage of reasonable compatibility, a surface oxidation film on the surface of the aluminium magnesium alloy can be effectively removed in the acid etching and descaling process, and the aluminium magnesium alloy can be protected from excess corrosion. In comparison with the traditional technology, nitric oxide pollutant amount is reduced by above 90%, thereby greatly improving production and operation environment.

Description

technical field [0001] The invention belongs to the technical field of metal surface treatment, and relates to the surface treatment of aluminum-magnesium alloy materials, in particular to an environment-friendly acid etching and descaling treatment solution for bimetal composite wire processing. Background technique [0002] The electroplating method is a traditional bimetallic composite wire production process. Since an oxide film is easily formed on the surface of the aluminum-magnesium alloy wire, the quality of the copper plating layer is poor, and the bonding force is not strong. It cannot meet the needs of the wire and cable industry, and has not been able to form an industrialization. For this reason, someone invented the salt electroplating copper process, which continuously plated copper on the aluminum-magnesium alloy wire, and then obtained the copper-clad aluminum conductor with the required wire diameter through the drawing process. This process solves the prob...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23G1/02C23G1/12C25D5/42
Inventor 张正良
Owner HANGZHOU ZHENDA HARDWARE MACHINERY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap