Degradable material for preparing outside sleeve of disposable injector
A technology for degrading materials and syringes, applied in the field of degradable materials, can solve the problems of slow crystallization, low strength, large molecular weight, etc., and achieve the effects of solving pollution, stable performance and reasonable formula
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0016] Weigh 100kg of poly-3-hydroxybutyrate, 10kg of polyglycol adipate, 0.07kg of antioxidant 1010, 0.14kg of antioxidant 168, 0.3kg of ethylene bisstearamide, two (3,4-Dimethylbenzylidene) sorbitol 0.2kg, acetyl tributyl citrate 20kg, POE (ethylene-octene copolymer) 5kg, the above weighed raw materials in a high-speed mixer Mix for 5 to 7 minutes to fully disperse the raw materials to obtain a mixture; place the mixed mixture in a parallel twin-screw extruder for melt extrusion and granulation; in this process: temperature control starts from the feeding section, Respectively 185℃, 190℃, 195℃, 195℃, 190℃, 180℃; the main engine speed is 380r / min, the feeding speed is 200r / min; the water-cooled pellets are used to obtain the degradable material for preparing disposable syringe jacket .
Embodiment 2
[0018] Weigh 100kg of poly-3-hydroxybutyrate, 13kg of polydiethylene adipate, 0.1kg of antioxidant 1010, 0.2kg of antioxidant 168, 0.5kg of ethylene bisstearamide, two (3,4-Dimethylbenzylidene)sorbitol 0.25kg, acetyl tributyl citrate 25kg, POE (ethylene-octene copolymer) 8kg, and then prepared according to the preparation method described in Example 1 for The biodegradable material for preparing disposable syringe jacket.
Embodiment 3
[0020] Weigh 100kg of poly-3-hydroxybutyrate, 15kg of polydiethylene adipate, 0.15kg of antioxidant 1010, 0.3kg of antioxidant 168, 0.8kg of ethylene bisstearamide, two (3,4-Dimethylbenzylidene)sorbitol 0.3kg, acetyl tributyl citrate 30kg, POE (ethylene-octene copolymer) 10kg, and then prepared according to the preparation method described in Example 1 for The biodegradable material for preparing disposable syringe jacket.
[0021] Corresponding tests were made between the material of the present invention and the commonly used syringe jacket material (polypropylene material), and the following data was obtained (see Table 1).
[0022] Table 1 Comparison table of the performance of the material of the present invention and the performance test data of commonly used polypropylene materials
[0023] Test items The degradable material of the present invention Commonly used polypropylene materials transparency(%)83.6~84.585.7 Haze (%)27.3~28.526.5 Izod impact strength (J / m)89~941...
PUM
Property | Measurement | Unit |
---|---|---|
elongation at break | aaaaa | aaaaa |
tensile strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com