Ceramic-imitated plastic composite material and preparation method thereof

A composite material and imitating ceramic technology, which is applied in the field of imitating ceramic polymer composite materials and its preparation, can solve the problems of high processing energy consumption, complicated process, and difficult to recycle, and achieves high impact resistance, high thermal conductivity, good thermal conductivity, etc. The effect of processability

Active Publication Date: 2013-09-18
XIAMEN RUNNER IND CORP
View PDF1 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a combination of the advantages of plastic and ceramics, which has the advantages of impact resistance, easy molding, easy recycling, and high surface quality, in view of the defects of existing ceramic materials such as complex process, high processing energy consumption, difficult recycling, and fragility. Glossy ceramic-plastic composite material and preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramic-imitated plastic composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Add 40% by weight of zinc oxide and 30% of ferrite into the mixer and stir for 30 minutes, then evenly spray 1% by weight of coupling agent on the stirring zinc oxide and ferrite, stir for 20 minutes, and then add 1% by weight of Ethylene bis stearamide, ethylene-octene copolymer grafted with 1% by weight of maleic anhydride, and 27% by weight of polyamide were added together into the mixer and stirred for 20 minutes to obtain a mixed raw material. Finally, the obtained mixed raw materials are put into a twin-screw extrusion granulator, melted and extruded into a line, cooled, and pelletized to obtain imitation ceramic-plastic composite material pellets. The process parameters are: use the auxiliary feeding system to add mixed For raw materials, the feeding speed is 80r / min; the screw speed of the main engine is 300r / min; The temperature is 245°C, the temperature of the seventh zone is 245°C, the temperature of the eighth zone is 250°C, the temperature of the ninth zone...

Embodiment 2

[0040] Add 60% zinc oxide and 15% iron powder by weight into the mixer and stir for 20 minutes. Then, 1% by weight of the coupling agent is evenly sprayed onto the stirring zinc oxide and iron powder, and then stirred for 25 minutes. Then add 1% by weight of ethylene bis stearamide, 1% by weight of maleic anhydride grafted ethylene-octene copolymer, and 22% by weight of polyamide into the mixer and stir for 20 minutes to obtain a mixed raw material. Finally, the obtained mixed raw materials are put into a twin-screw extrusion granulator, melted and extruded into a line, cooled, and pelletized to obtain imitation ceramic-plastic composite material pellets. The process parameters are: use the auxiliary feeding system to add mixed For raw materials, the feeding speed is 80r / min; the screw speed of the main engine is 300r / min; The temperature is 245°C, the temperature of the seventh zone is 245°C, the temperature of the eighth zone is 250°C, the temperature of the ninth zone is 2...

Embodiment 3

[0043]Add 65% by weight of zinc oxide and 5% by weight of iron powder into the mixer and stir for 20 minutes. Then, 0.8% by weight of the coupling agent is evenly sprayed on the stirring zinc oxide and iron powder, and then stirred for 20 minutes. Then add 0.7% by weight of ethylene bis stearamide, 5% by weight of maleic anhydride grafted ethylene-octene copolymer, and 23.5% by weight of polyamide into the mixer and stir for 15 minutes to obtain a mixed raw material. Finally, the obtained mixed raw materials are put into a twin-screw extrusion granulator, melted and extruded into a line, cooled, and pelletized to obtain imitation ceramic-plastic composite material pellets. The process parameters are: use the auxiliary feeding system to add mixed For raw materials, the feeding speed is 90r / min; the screw speed of the main engine is 330r / min; The temperature is 245°C, the temperature in the seventh zone is 245°C, the temperature in the eighth zone is 250°C, the temperature in t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a ceramic-imitated plastic composite material and a preparation method thereof, relates to a high molecular composite material, and provides the imitative ceramic plastic composite material which has the combined advantages of plastic and ceramic, is impact-resistant, easy to form and recover and has high surface glossiness and the preparation method thereof. The imitative ceramic plastic composite material comprises the following components: a plastic material, zinc oxide, a coupling agent, a lubricant, a weighing filler, a toughening agent and fiber. The preparation method comprises the following steps of: adding the zinc oxide and the weighing filler into a mixer; spraying the coupling agent; adding the lubricant, the toughening agent and the plastic material into the mixer to obtain mixed raw materials; throwing the obtained mixed raw materials into a double-screw extrusion granulator; performing melt extrusion to form wires; cooling; and granulating to obtain the imitative ceramic plastic composite material. If the fiber is available in the formula, the fiber is fed from a side feed port of the double-screw granulator during extrusion granulation.

Description

technical field [0001] The invention relates to a polymer composite material, in particular to a ceramic-like polymer composite material and a preparation method thereof. Background technique [0002] Ceramic products are deeply loved by people because of their natural, beautiful, durable, and low-cost characteristics, and can be seen everywhere in life. However, ceramics also have disadvantages such as high firing energy consumption, poor toughness and brittleness. It has become a trend to develop new materials with simple production process, easy recycling, and superior mechanical properties to replace existing ceramic materials. [0003] Because ceramics have the above advantages, people have long hoped to use plastics with better processing properties to imitate the appearance of ceramics. For example, adding a few percent of toner to the plastic material can adjust the appearance of the plastic material to various The appearance of ceramics, or the appearance of ceram...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L77/00C08L23/12C08L67/02C08L51/06C08K9/06C08K3/22C08K3/08C08K7/14
Inventor 陈明辉黄贤明李明仁
Owner XIAMEN RUNNER IND CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com