Washable polyaniline/terylene composite conductive fabric and manufacture method thereof

A technology of composite conduction and manufacturing method, which is applied in the direction of textiles and papermaking, fiber type, fiber treatment, etc., can solve the problems of fabrics not resistant to washing, weak polyaniline binding force, poor fastness, etc., and achieve excellent electrical conductivity and durability Washing performance, improving washing fastness, and increasing water resistance

Active Publication Date: 2012-02-01
深圳市新纶超净科技有限公司
View PDF5 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem to be solved by the present invention is to provide a water-resistant fabric for the conductive fabric obtained by compounding...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Washable polyaniline/terylene composite conductive fabric and manufacture method thereof
  • Washable polyaniline/terylene composite conductive fabric and manufacture method thereof
  • Washable polyaniline/terylene composite conductive fabric and manufacture method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Embodiment 1: a kind of manufacturing method of washable polyaniline / polyester composite conductive fabric, comprises the following steps:

[0035] (1) Alkali weight reduction pretreatment: first, the polyester base fabric is treated with 20g / L caustic soda solution, treated at 90°C for 90min, washed with water and dried.

[0036] (2) Hydrochloric acid solution of padding oxidant: then the polyester base cloth treated in step (1) is padded in the hydrochloric acid solution of ammonium persulfate at a temperature of 0°C, wherein the concentration of ammonium persulfate in the solution is 0.2mol / L, the concentration of hydrochloric acid is 0.5mol / L. Control the liquid-carrying rate to about 40%. drying;

[0037] (3) Padding reaction solution: dissolve N-methyl-N-hydroxyethylaniline monomer and p-toluenesulfonic acid in water, and add water-based isocyanate to form a reaction solution, stir evenly, N-methyl-N-hydroxyethylaniline The concentration of ethylaniline monome...

Embodiment 2

[0039] Embodiment 2: a kind of manufacturing method of washable polyaniline / polyester composite conductive fabric, comprises the following steps:

[0040] (1) Alkali decrement pretreatment: first, treat the polyester base fabric with 30g / L caustic soda solution, treat it at 85°C for 80min, wash and dry it with water;

[0041] (2) the hydrochloric acid solution of padding oxidant: then the dacron base cloth that step (1) will be processed is padded in the hydrochloric acid solution of the iron trichloride that temperature is 1 ℃, and the concentration of ferric chloride is 0.4mol / L, The concentration of hydrochloric acid is 0.8mol / L, and the liquid carrying rate is controlled at about 50%. drying;

[0042] (3) padding reaction solution: N, N-dihydroxyethylaniline and camphorsulfonic acid are dissolved in ethanol solution, and add aqueous isocyanate to form reaction solution, stir, N, N-dihydroxyethylaniline concentration is 0.2mol / L, the concentration of camphorsulfonic acid ...

Embodiment 3

[0044] Embodiment 3: a kind of manufacturing method of washable polyaniline / polyester composite conductive fabric, comprises the following steps:

[0045] (1) Alkali weight reduction pretreatment: first, treat the polyester base fabric with 40g / L caustic soda solution, treat it at 90°C for 70min, and then wash and dry it with water.

[0046] (2) Padding the hydrochloric acid solution of the oxidizing agent: then pad the treated polyester base cloth in a perchloric acid solution with a temperature of 2° C., wherein the concentration of the perchloric acid solution is 0.5 mol / L, and the liquid retention rate is controlled to be about 60%. drying;

[0047] (3) padding reaction solution: dissolve o-hydroxyaniline and dodecylbenzenesulfonic acid in isopropanol solution, and add water-based isocyanate to form a reaction solution, stir well, o-hydroxyaniline concentration is 0.15mol / L, ten The concentration of dialkylbenzenesulfonic acid is 0.07mol / L, and the addition amount (mass p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Surface resistanceaaaaaaaaaa
Login to view more

Abstract

The invention discloses a washable polyaniline/terylene composite conductive fabric and a manufacture method thereof. The conductive fabric comprises a terylene base cloth which has undergone alkali decrement treatment, wherein, a polyaniline conducting polymer layer is compounded on the terylene base cloth, and the polyaniline conducting polymer layer is prepared by reacting doped polyaniline containing active substituent and aqueous isocyanate. The manufacturing method comprises a step of alkali decrement pretreatment, a step of padding in a hydrochloric acid solution of an oxidizing agent,a step of padding in a reaction solution and low temperature reaction and a step of rinsing. The invention provides the washable polyaniline/terylene composite conductive fabric which is capable of maintaining good conductivity performance for a long time; the invention also provides the manufacture method for polyaniline/terylene composite conductive fabric, and the method has the advantage of asimple process and enables polyaniline to have a strong bonding force on the terylene base cloth.

Description

technical field [0001] The invention belongs to the technical field of conductive fabrics, in particular to a washable polyaniline / polyester composite conductive fabric and a manufacturing method thereof. Background technique [0002] Polyaniline is a conjugated conductive polymer with excellent conductivity, simple synthesis and low price, and has a very wide application prospect. In recent years, researchers have begun to study the compounding of polyaniline on fabrics to endow the fabrics with good electrical conductivity. However, polyaniline is highly polar and difficult to dissolve in common solvents, resulting in processing difficulties, which greatly limits the wide application of polyaniline. [0003] The self-assembly of polyaniline on the substrate solves the problem of polyphenylene in processing. The patent number is ZL200810202711.1 Chinese invention patent discloses "a preparation method of self-assembled multifunctional polyaniline / pure cotton composite con...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06M11/38D06M15/61D06M15/568D06M101/32
Inventor 张强管映亭郭海涛
Owner 深圳市新纶超净科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap