Slag pot carrier cable sheath material and manufacturing method thereof
The invention relates to a cable sheathing material and a manufacturing method technology, which are applied in the manufacture of cable sheathing materials for slag tank trucks and the field of cable sheathing materials for slag tanker trucks. problems such as short service life of cables, to achieve the effects of superior mechanical properties, high tensile strength and high elongation at break
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0016] Raw materials are prepared according to the following components and weight content: neoprene rubber CR 3221: 23 parts; active agent zinc oxide: 1.2 parts; active agent magnesium oxide: 1 part; methyl thiuram disulfide TMTD: 0.1 part; ethylene sulfide Urea ETU: 0.2 parts; Dioctyl sebacate DOS: 1.0 parts; Dioctyl phthalate DOP: 0.45 parts; Stearic acid SA: 0.1 parts; Microcrystalline paraffin: 1.2 parts; Ester ODA: 0.9 parts; N-N-phenyl-p-phenylenediamine TPPD: 0.1 parts; 4,4-bis( --Dimethylbenzyl) diphenylamine HS-911: 0.2 parts; High wear-resistant carbon black: 5 parts; Semi-reinforcing carbon black: 4.5 parts; Vaseline: 0.5 parts; Calcined clay: 8 parts; Calcium carbonate: 3 parts share.
[0017] The production includes the following steps in turn: first mix the neoprene CR 3221 in the internal mixer for 5 minutes; then add the active agent magnesium oxide, active agent zinc oxide, microcrystalline paraffin, stearic acid SA, calcium carbonate, plasticizer Agent DO...
Embodiment 2
[0019] Prepare raw materials according to the following components and weight content: CR 3221 neoprene: 23 parts; active agent zinc oxide: 1.3 parts; active agent magnesium oxide: 1.2 parts; methyl thiuram disulfide TMTD: 0.2 parts; ethylene sulfide Urea ETU: 0.25 parts; Dioctyl sebacate DOS: 1.2 parts; Dioctyl phthalate DOP: 0.5 parts; Stearic acid SA: 0.13 parts; Microcrystalline paraffin: 1.3 parts; Ester ODA: 1.1 parts; N-N-phenyl-p-phenylenediamine TPPD: 0.12 parts; 4,4-bis( --Dimethylbenzyl) diphenylamine HS-911: 0.3 parts; high wear-resistant carbon black: 6 parts; semi-reinforcing carbon black: 5 parts; vaseline: 0.6 parts; calcined clay: 9 parts; calcium carbonate: 3.5 parts share.
[0020] The production includes the following steps in turn: first mix the neoprene CR 3221 in the internal mixer for 6 minutes; then add the active agent magnesium oxide, active agent zinc oxide, microcrystalline paraffin, stearic acid SA, calcium carbonate, plasticizer Agent DOP (dioc...
Embodiment 3
[0022] Prepare raw materials according to the following components and weight content: CR 3221 neoprene: 23 parts; active agent zinc oxide: 1.5 parts; active agent magnesium oxide: 1.5 parts; methyl thiuram disulfide TMTD: 0.3 parts; ethylene sulfide Urea ETU: 0.3 parts; Dioctyl sebacate DOS: 1.3 parts; Dioctyl phthalate DOP: 0.6 parts; Stearic acid SA: 0.15 parts; Microcrystalline paraffin: 1.4 parts; Ester ODA: 1.2 parts; N-N-phenyl-p-phenylenediamine TPPD: 0.15 parts; 4,4-bis( --Dimethylbenzyl) diphenylamine HS-911: 0.4 parts; High wear-resistant carbon black: 8 parts; Semi-reinforcing carbon black: 6 parts; Vaseline: 0.7 parts; Calcined clay: 10 parts; Calcium carbonate: 4 parts share.
[0023] The production includes the following steps in turn: first mix the neoprene CR 3221 in the internal mixer for 7 minutes; then add the active agent magnesium oxide, active agent zinc oxide, microcrystalline paraffin, stearic acid SA, calcium carbonate, plasticizer The agent DOP (d...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap