Permanently antistatic masterbatch, permanently antistatic PA66/PA 6/POE (Polymide 66/Polymide 6/ Polyethylene Octene Elastomer) alloy and preparation method

An antistatic masterbatch, PA66 technology, applied in the field of antistatic masterbatch and alloy materials, can solve problems such as low conductivity, achieve low cost, improve comprehensive performance, and reduce the amount of addition

Inactive Publication Date: 2013-06-12
SHANGHAI SUNNY
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, PA66 / PA6 / POE alloy has good electrical insulation like most polymer materials, and its surface resistivity is generally 10 13 -10 15 Ω.m, the conductivity is much smaller than that of metal materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Permanently antistatic masterbatch, permanently antistatic PA66/PA 6/POE (Polymide 66/Polymide 6/ Polyethylene Octene Elastomer) alloy and preparation method
  • Permanently antistatic masterbatch, permanently antistatic PA66/PA 6/POE (Polymide 66/Polymide 6/ Polyethylene Octene Elastomer) alloy and preparation method
  • Permanently antistatic masterbatch, permanently antistatic PA66/PA 6/POE (Polymide 66/Polymide 6/ Polyethylene Octene Elastomer) alloy and preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-5

[0027] Embodiment 1-5 A kind of permanent antistatic masterbatch and preparation method

Embodiment 1

[0029] The composition ratio of the antistatic masterbatch is shown in Table 1. Alkali metal is LiClO 4 , the antioxidant is a compound of phenothiazine and phosphite (s9228) in a mass ratio of 1:1, and the heat stabilizer is an organotin heat stabilizer, calcium stearate, zinc stearate in a mass ratio of 2:1:1 The ratio of the compound, the auxiliary antistatic agent is silicon dioxide, and the polymer material containing polyether block is the compound of polyethylene oxide and polyether ester acetamide in a mass ratio of 5:1.

[0030] The antistatic masterbatch raw material formula of table 1 embodiment 1-5

[0031]

[0032] Put the above components into a high mixer according to the proportion and mix them for 2-5 minutes, discharge the material, and then use a screw extruder to extrude and granulate. The processing temperature is 150-200°C, and the screw speed is 25-35HZ. The specific process is shown in Table 2.

[0033] Table 2 Processing parameters of antistatic ...

Embodiment 2

[0040] The composition ratio of the antistatic masterbatch is shown in Table 1. The alkali metal is LiCl, the antioxidant is a compound of phenothiazine and phosphite (s9228) in a mass ratio of 1:1.5, and the heat stabilizer is an organotin heat stabilizer, calcium stearate, zinc stearate according to 2: A compound with a mass ratio of 1:0.8, the auxiliary antistatic agent is silicon dioxide, and the polymer material containing polyether blocks is a compound of polyethylene oxide and polyether ester acetamide in a mass ratio of 5:1.

[0041] The components were mixed in a high mixer for 8 minutes. The processing parameters are shown in Table 2, and the surface resistivity test data of the obtained antistatic masterbatch are shown in Table 3. Others are the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an antistatic masterbatch, which comprises the following components: 1-15 wt% of alkaline metal salt, 0.1-2 wt% of antioxidant, 0.1-2 wt% of heat stabilizer, 0.01-10 wt% of assistant antistatic agent and 71-95 wt% of high polymer material with polyether blocks. The invention also provides antistatic alloy prepared from the masterbatch, which comprises the following components: 2-8 wt% of antistatic masterbatch, 20-50 wt% of PA66 (Polymide 66), 20-50 wt% of PA6 (Polymide 6), 15-25 wt% of POE (Polyethylene Octene Elastomer) and 1-5 wt% of compatilizer. The invention also provides a preparation method of the masterbatch and a preparation method of the alloy, which respectively comprise the following steps of: mixing the components for 1-10 minutes; discharging; extruding; pelleting; and obtaining the product. The antistatic masterbatch has the surface resistivity being 102-103 ohm m, a lasting antistatic effect, less additive amount, and good compatibility with many kinds of resin. The antistatic alloy has the surface resistivity being 106-108 ohm m, higher comprehensive mechanical property, low cost and good heat resistance.

Description

technical field [0001] The invention relates to the field of antistatic materials, in particular to an antistatic master batch, an alloy material made of the same and a preparation method for the two. Background technique [0002] Due to its good comprehensive mechanical properties, high heat resistance, good wear resistance, self-lubricating properties, good flame retardancy, excellent chemical corrosion resistance, excellent barrier properties and other properties, nylon has become the most suitable for current applications. Wide range of engineering plastics. POE is non-toxic, odorless, low density, low price, and has excellent properties such as aging resistance, ozone resistance, and chemical medium resistance. POE can be used as an impact modifier for engineering plastics, used to make mechanical parts with impact resistance requirements, corrosion-resistant parts, automobiles, electrical parts and other products. Adding POE to nylon can effectively improve its hygro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L71/02C08K13/02C08K3/24C08K5/524C08K5/46C08K5/098C08K3/36C08J3/22C08L77/06C08L77/02C08L23/08
Inventor 郭建鹏苏吉英孟成铭杨涛
Owner SHANGHAI SUNNY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com