Production method of automobile skylight slide plate made of paper honeycomb-shape core material

A technology of automobile sunroof and production method, which is applied in the field of automobile interior parts, can solve the problems such as the heavy weight of the sunroof slide plate, and achieve the effects of reducing the weight of the car, environmental protection, weather resistance, and high rigidity

Inactive Publication Date: 2012-04-18
WUXI GISSING AUTO PARTS CO LTD
View PDF4 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a production process for car sunroof slides with paper honeycomb core materia...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Fiat 343 sunroof skateboard, its specification is: L564.5×W774mm.

[0020] Including the following production process steps:

[0021] (1) Material placement: Lay the materials on the workbench in the order of glass fiber, paper honeycomb core material, and glass fiber;

[0022] (2) Polyurethane spraying: Fix the paved material on the manipulator, send it to the spraying room for AB material spraying until the material is fully infiltrated;

[0023] (3) Compression molding: Place the infiltrated material in a molding machine for positioning, molding, and punching to obtain a molding material; the molding temperature of the upper mold of the mold is 120°C, the molding temperature of the lower mold is 125°C, and the molding pressure is 7.5MPa. Time: 130s;

[0024] (4) Cooling and shaping: Take the molding material out of the mold, put it on the cooling fixture for cooling and shaping at room temperature, the cooling time is 45s, after cooling and shaping, remove the surr...

Embodiment 2

[0031] 353 sunroof slide plate, its specification is: L1120×W850mm.

[0032] Including the following production process steps:

[0033] (1) Material placement: Lay the materials on the workbench in the order of glass fiber, paper honeycomb core material, and glass fiber;

[0034] (2) Polyurethane spraying: Fix the paved material on the manipulator, send it to the spraying room for AB material spraying until the material is fully infiltrated;

[0035] (3) Compression molding: Place the infiltrated material in a molding machine for positioning, forming and punching to obtain a molding material; the molding temperature of the upper mold of the mold is 130°C, the molding temperature of the lower mold is 145°C, and the molding pressure is 8.5MPa. Time: 140s;

[0036] (4) Cooling and shaping: Take the molding material out of the mold, put it on the cooling fixture for cooling and shaping at room temperature, the cooling time is 50s, after cooling and shaping, remove the surroundin...

Embodiment 3

[0043] 464 sunroof slide plate, its specification is: L1100×W820mm.

[0044] Including the following production process steps:

[0045] (1) Material placement: Lay the materials on the workbench in the order of glass fiber, paper honeycomb core material, and glass fiber;

[0046] (2) Polyurethane spraying: Fix the paved material on the manipulator, send it to the spraying room for AB material spraying until the material is fully infiltrated;

[0047] (3) Compression molding: place the infiltrated material in a molding machine for positioning, forming and punching to obtain a molding material; the molding temperature of the upper mold of the mold is 120°C, the molding temperature of the lower mold is 135°C, the molding pressure is 8MPa, and the molding time : 130s;

[0048] (4) Cooling and shaping: Take the molding material out of the mold, put it on the cooling fixture for cooling and shaping at room temperature, the cooling time is 50s, after cooling and shaping, remove the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a production method of an automobile skylight slide plate made of a paper honeycomb-shape core material, and belongs to the technical field of automobile interior trim part. A lightweight, vibration resistant, heat insulating and sound insulating automobile skylight slide plate with high specific strength, high stiffness-to-density ratio and good weatherability is prepared. The skylight slide plate is prepared by selecting the paper honeycomb-shape core material as a base material, placing a layer of honeycomb paper board between two layers of glass fiber mats, carrying out double face polyurethane spraying and moulding. The preparation steps comprise paving materials, spraying polyurethane, compacting for moulding, cooling for fixing, installing silica gel pads, applying back glue fabrics and assembling accessories. The method of the invention solves defect of heavy weight of a traditional skylight slide plate and satisfies design requirement of lightweighting automobile; a product has high rigidity and will not break or deform; the whole production process adopts an automatic production line for one-time production, so as to substantially reduce worker labor intensity and increase working efficiency; the whole production process generates no harmful substance, therefore, the method is an environment-friendly method for producing the automobile skylight slide plate.

Description

technical field [0001] The invention relates to a method for producing a car sunroof skateboard with a paper honeycomb core material, and prepares a car sunroof skateboard with light weight, high specific strength, high specific stiffness, good vibration resistance, heat insulation, sound insulation and weather resistance, which belongs to the automobile The field of interior technology. Background technique [0002] With the rapid development of China's auto industry, lightweight, low fuel consumption, high safety, reduced environmental pollution and reduced overall cost of automobile manufacturing and use have increasingly become the consensus of the automobile industry. Studies have shown that reducing vehicle weight is critical to improving fuel efficiency and reducing emissions. The weight of the vehicle is reduced by 56.69kg, and the mileage of the same 1L fuel vehicle can be increased by 0.09~0.21kg; at the same time, the mass of the vehicle is reduced by 50%, and th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B3/12B32B29/02B32B17/02B32B37/06B32B37/10B60J7/02
Inventor 李倩
Owner WUXI GISSING AUTO PARTS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap