Preparation method of liquid rubber asphalt water-proof paint

A technology of asphalt waterproof coating and liquid rubber, which is applied in the direction of asphalt coating, recycled rubber coating, anti-corrosion coating, etc. It can solve the problems affecting stability and achieve good stability, excellent bonding performance and less foam

Active Publication Date: 2012-06-13
天津四十二站检测技术有限公司
View PDF2 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this emulsion can affect stability if diluted with water

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of liquid rubber asphalt water-proof paint
  • Preparation method of liquid rubber asphalt water-proof paint
  • Preparation method of liquid rubber asphalt water-proof paint

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0053] Preparation of nonionic regenerated rubber emulsion:

[0054] Taking the total weight of regenerated rubber as the basic amount, the ingredients are formulated according to the following weight ratio:

[0055]

[0056] After the above-mentioned regenerated tread rubber is plasticized for 8-10 times at a temperature of 70±5°C, the above-mentioned stabilizer-polyvinyl alcohol and non-ionic emulsifier 2-sorbitan fatty acid sugar are added After mixing evenly, place the lower piece in a shearing machine, keep the temperature of 80-120°C, add the above-mentioned nonionic emulsifier 1-nonylphenol polyoxyethylene ether and water, and cut 20 at a speed of 450 rpm Minutes, turn to high speed 960 rpm and cut for 3 minutes, that is, non-ionic regenerated rubber emulsion;

[0057] Preparation of nonionic asphalt emulsion:

[0058] Take the weight of asphalt as the basic amount, and mix according to the following weight ratio:

[0059]

[0060]Melt and dehydrate the above-m...

Embodiment 2

[0073] Preparation of nonionic regenerated rubber emulsion:

[0074] Taking the total weight of regenerated rubber as the basic amount, the ingredients are formulated according to the following weight:

[0075]

[0076] Make nonionic regenerated rubber emulsion with the method for example 1;

[0077] Preparation of nonionic asphalt emulsion:

[0078] Take the weight of asphalt as the basic amount, and mix according to the following weight ratio:

[0079]

[0080] Obtain non-ionic asphalt emulsion with the method for embodiment 1;

[0081] Preparation of liquid rubber asphalt waterproof coating:

[0082]

[0083]

[0084] The liquid rubber asphalt waterproof paint 200kg is obtained with the method for embodiment 1.

[0085] Its physical properties reach the JC / T 975-2005 standard index,

[0086] Tensile strength, MPa 1.1,

[0087] Elongation at break, % 820,

[0088] Low temperature flexibility, ℃ -25,

[0089] Water impermeability, (0.3MPa, 30min) no leakag...

Embodiment 3

[0092] 1. Preparation of nonionic regenerated rubber emulsion

[0093] Taking the total weight of regenerated rubber as the basic amount, the ingredients are formulated according to the following weight:

[0094]

[0095] Make nonionic regenerated rubber emulsion with the method for example 1;

[0096] 2. Preparation of non-ionic asphalt emulsion

[0097]

[0098] Obtain non-ionic asphalt emulsion with the method for embodiment 1;

[0099] 3. Preparation of liquid rubber asphalt waterproof coating

[0100]

[0101] The liquid rubber asphalt waterproof paint 200kg is obtained with the method for embodiment 1.

[0102] Its physical performance index meets the index of JC / T 975-2005 standard:

[0103] Tensile strength, MPa 1.0

[0104] Elongation at break, % 850

[0105] Low temperature flexibility, ℃ -25

[0106] Water impermeability (0.3MPa, 30min) no leakage

[0107] The emulsion prepared by it is delicate and the particle size is 2-3μ.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a preparation method of liquid rubber asphalt water-proof paint and relates to a preparation method of water-proof paint. The preparation method provided by the invention is a preparation method of a rubber asphalt emulsion by taking a non-ionic surfactant as an emulsifying agent. The preparation method comprises the following steps: 1, preparing a non-ionic reclaimed rubber emulsion from the following components in parts by weight: 100 parts of reclaimed rubber, 0-2 parts of stabilizing agent, 0-8 parts of non-ionic emulsifying agent 1, 0-2 parts of non-ionic emulsifying agent 2 and 100 parts of water; 2, preparing a non-ionic asphalt emulsion from the following components in parts by weight: 100 parts of 70# petroleum asphalt, 0-2 parts of non-ionic emulsifying agent 1, 0-1 part of non-ionic emulsifying agent 2, 0-1 part of stabilizing agent and 100 parts of water; and 3, preparing the liquid rubber asphalt water-proof paint from the following components in parts by weight: 70-80 parts of non-ionic reclaimed rubber emulsion, 20-30 parts of chloroprene rubber latex and 100 parts of non-ionic asphalt emulsion. The liquid rubber asphalt water-proof paint prepared by using the method can be widely used in projects with high thermal resistance requirement and railway, highway, municipal bridges and building waterproof and anticorrosive projects which have high crack resistance requirements.

Description

Technical field: [0001] The invention relates to a preparation method of waterproof paint. Especially the preparation method of liquid rubber asphalt waterproof coating. It is a manufacturing method of rubber asphalt emulsion with non-ionic surfactant as emulsifier. Background technique: [0002] Mixing various rubbers in asphalt can overcome the shortcomings of high-temperature softening and low-temperature embrittlement of asphalt itself, and improve the tear resistance in winter, and no cracks will appear at low temperature -25°C; the anti-melt performance in summer is also improved. It is improved and does not soften at high temperature. For this reason, it is necessary to modify the petroleum asphalt in order to meet the needs of construction and municipal engineering. [0003] There are many ways to modify asphalt. At present, rubber, resin and mineral fillers are commonly used for modification. Among them, rubber is an important modified material for asphalt. [0...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D195/00C09D117/00C09D111/00C09D5/08C08J3/03C08L17/00C08L95/00
Inventor 郑健红李子安于勇梁中艳魏申莉
Owner 天津四十二站检测技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap