Production process for spunlace composite high temperature-resisting and corrosion-resisting filtering material

A filter material and production process technology, which is applied in the field of spunlace composite high temperature and corrosion resistant filter materials, can solve the problems of filter material mechanical strength decline, affecting the service life of filter bags, and expensive imports, so as to improve the entanglement effect and uniform Better performance and better filtration efficiency

Active Publication Date: 2014-03-26
ZHEJIANG BAOREN NONWOVEN CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Studies have shown that in the needle punching process, steel needles with hooks puncture the fiber web for entanglement and compounding, which will cut off a large number of fibers and reinforce the filaments of the base fabric, resulting in inevitable damage to the base fabric, which will eventually cause a decrease in the mechanical strength of the filter material and affect the final filter. Lifespan of the bag
At the same time, due to the influence of the level of industrial development in China, high-temperature resistant filter mats imported from abroad are generally used. The import price is expensive, and restricted by the current economic development conditions, the popularization and use are limited.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production process for spunlace composite high temperature-resisting and corrosion-resisting filtering material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0030] The production process of the spunlace composite high-temperature-resistant and corrosion-resistant filter material of the present invention uses polyphenylene sulfide fiber and glass fiber base cloth as raw materials; the polyphenylene sulfide fiber is first inspected, weighed and fed, and then fed into the long curtain in sequence , horizontal opener, large warehouse mixing box, fine opener, and then carding machine 1 and carding machine 2 perform layered carding, and then enter the cross-lapper 1 and cross-lapper 2 respectively for laying Then the glass fiber base cloth is sandwiched between the raw materials conveyed by the first cross-lapper and the second cross-lapper and laminated, and then enters the pre-wet process, spunlace process, dehydration process, and drying process in sequence. Drying process, coiling process.

[0031] Among them, carding machine one, the main cylinder work roll is 110m / min, the main cylinder stripping roll is 150m / min, the main cylinde...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a production process for a spunlace composite high temperature-resisting and corrosion-resisting filtering material and belongs to the technical field of a textile filtering material. The production process comprises the following steps that: taking polyphenylene sulfide fibers and fiberglass fabrics as raw materials; checking, weighing and charging the polyphenylene sulfide fibers; charging the polyphenylene sulfide fibers into a long curtain, a horizontal opener, a big-cabin cotton blending box and a refined opener successively; and then carding by using a carding machine I and a carding machine II in a layering mode; placing into a cross lapping machine I and a cross lapping machine II to lap; clamping the fiberglass fabrics between the raw materials delivered by the cross lapping machine I and the cross lapping machine II and performing superposition; and performing the processes of pre-wetting, hydroentangling, dehydrating, drying and taking-up. The production process for the spunlace composite high temperature-resisting and corrosion-resisting filtering material provided by the invention has the advantages of excellent mechanical performance, filtration performance, high temperature-resisting performance, and chemical corrosion-resisting performance and size stability.

Description

technical field [0001] The invention relates to a production process of a spunlace composite high-temperature-resistant and corrosion-resistant filter material, which belongs to the technical field of textile filter materials. Background technique [0002] With the progress of society, people's living standards have been significantly improved. However, while high-tech brings wealth and a more convenient and comfortable life, it also brings many problems to the natural environment on which human beings depend. The environmental pollution caused by high-temperature dusty waste gas discharged from coal-fired power plants, steel industry, cement chemical industry, etc. has brought more and more harm to human survival and health. China's "Eleventh Five-Year Plan" puts forward the idea of ​​greatly increasing power generation capacity. It is necessary to increase the installed capacity of power generation to 910 million kilowatts by 2020, including thermal power generation of 60...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01D39/14D04H1/4326D04H18/04B32B27/02B32B27/28
Inventor 洪桂焕徐寿明韩旭
Owner ZHEJIANG BAOREN NONWOVEN CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products