Solar battery back plate adopting ultraviolet (UV) curing weather-proof coating and manufacture method of solar battery back plate

A technology for solar cells and manufacturing methods, applied in coatings, circuits, photovoltaic power generation, etc., can solve the problems of low curing efficiency of coatings and coatings, high production equipment investment, large production sites, etc., and achieve high coating curing efficiency, improve Excellent production efficiency and weather resistance

Active Publication Date: 2012-07-25
ZHEJIANG WAZAM NEW MATERIAL CO LTD
View PDF4 Cites 45 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the presence of easily hydrolyzable adhesives on both sides of the PET substrate inside the compound-adhesive backsheet, the fluorine film (PVF or PVDF, etc.) is easily peeled off from the PET substrate, resulting in product defects
However, the current coating-type bac

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0047] Example 1:

[0048] The materials and specific gravity of UV-curable weather-resistant coating: 70wt% fluorocarbon resin, 10wt% trimethylolpropane triacrylate, 4wt% initiator Irgacure 184, 10wt% titanium dioxide (particle size 0.5μm), 1wt% dispersant DISPERBYK -111, 2wt% antioxidant 1010, 1.5wt% anti-hydrolysis agent Stabaxol-1, 1.5wt% hindered amine anti-aging agent.

[0049] First, add 50% fluorocarbon resin and all titanium dioxide to a vertical sand mill, use glass beads with a particle size of 1.5 mm as the sanding medium, and sand for 3 hours at a peripheral speed of 10 m / sec. Mother liquor. Then, the mother liquor and the remaining raw materials are mixed uniformly on a high-speed mixer to obtain a coating. The coating was applied to both sides of the PET substrate treated with plasma through the machine head, and the UV curing machine with a wavelength of 365nm was used for curing. The curing time was 10s to obtain a solar cell backsheet material with a thickness o...

Example Embodiment

[0051] Example 2:

[0052] The materials and specific gravity of UV-curable weathering coating: 60wt% epoxy resin, 15wt% 1,6-hexanediol diacrylate, 5wt% Jiangsu Huati 201 initiator, 15wt% silica (particle size 1μm), 1.5wt% dispersant DISPERBYK-112, 1.5wt% antioxidant 1076, 1wt% anti-hydrolysis agent Stabaxol-P100, 1wt% phenylpropazole anti-aging agent.

[0053] First, add 40% fluorocarbon resin and silica to a vertical sand mill, use glass beads with a particle size of 2 mm as the sanding medium, and sand for 4 hours at a peripheral speed of 12 m / sec. Mother liquor. Then, the mother liquor and the remaining raw materials are mixed uniformly on a high-speed mixer to obtain a coating. The coating was applied to both sides of the plasma-treated PBT substrate through the machine head, and the UV curing machine with a wavelength of 365nm was used for curing, and the curing time was 50s to obtain a solar battery backsheet material with a thickness of 300μm.

[0054] After testing: the p...

Example Embodiment

[0055] Example 3:

[0056] The materials and specific gravity of UV curable weather-resistant coating: 80wt% acrylic resin, 10wt% glycidyl methacrylate, 3wt% initiator Irgacure 1173, 5wt% alumina (particle size 2μm), 0.5wt% dispersant DISPERBYK-112 , 0.5wt% antioxidant 168, 0.5wt% anti-hydrolysis agent Stabaxol-P100, 0.5wt% benzophenone anti-aging agent.

[0057] First, 60% acrylic resin and alumina are added to a vertical sand mill, and glass beads with a particle size of 3 mm are used as the sanding medium, and the peripheral speed is 8 m / sec for 5 hours to prepare the mother liquor. Then, the mother liquor and the remaining raw materials are mixed uniformly on a high-speed mixer to obtain a coating. The coating was applied to one side of the corona-treated PNT substrate through the machine head, and a 365nm wavelength UV curing machine was used for curing. The curing time was 30s to obtain a solar battery backsheet material with a thickness of 200μm.

[0058] After testing: the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Water vapor transmission rateaaaaaaaaaa
Login to view more

Abstract

The invention discloses a solar battery back plate adopting an ultraviolet (UV) curing weather-proof coating and a manufacture method of the solar battery back plate. The solar battery back plate comprises a substrate, wherein at least one side of the substrate is coated with the UV curing weather-proof coating, the UV curing weather-proof coating is prepared from the following materials: 50 to 80 weight percent of weather-proof photosensitive resin, 10 to 20 weight percent of reactive diluent, 2 to 15 weight percent of initiating agent, 5 to 30 weight percent of filling material, 0.5 to 2 weight percent of dispersing agent, 0.5 to 2 weight percent of antioxidant, 0.5 to 2 weight percent of hydrolysis-resistant agent and 0.5 to 2 weight percent of anti-aging agent. The UV curing weather-proof coating is adopted and directly coated onto the substrate, the coating curing efficiency is high, the production efficiency of the solar battery back plate is improved, and meanwhile, the use of organic solvents causing serious pollution to the environment is avoided, so the organic solvent volatilization is avoided in the whole production process, and the solar battery back plate conforms to the green and environmental friendly standard.

Description

technical field [0001] The invention belongs to the technical field of solar battery backplane manufacturing, and in particular relates to a solar battery backplane coated with a UV-cured weather-resistant coating on at least one side and a manufacturing method thereof. Background technique [0002] The back sheet is one of the important components of the solar cell, which mainly plays the role of insulation, anti-water vapor penetration, protection of the cell and support. At present, the mainstream solar cell module backsheet materials mostly use double-sided fluorine-containing compound adhesive backsheets and coated backsheets. Due to the presence of easily hydrolyzed adhesives on both sides of the internal PET substrate of the compound-adhesive backsheet, the fluorine film (PVF or PVDF, etc.) is easily peeled off from the PET substrate, resulting in product defects. However, the current coating-type backplane has the problem of low curing efficiency of the coating (it ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01L31/048H01L31/18C09D4/00C09D4/02C09D4/06C09D7/12H01L31/049
CPCY02E10/50
Inventor 沈宗华董辉龚春林
Owner ZHEJIANG WAZAM NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap