Antistatic radiating safety-protective tooling fabric and production method thereof

A safety protection and anti-static technology, which is applied in the manufacture of conductive/antistatic filaments, textiles and paper, and single-component polyester artificial filaments. Achieve the effects of reducing carbon emissions, strong anti-static performance, and saving electricity costs

Inactive Publication Date: 2012-08-15
ZHEJIANG LANTIANHAI FAB TECHNOLAGY CO LTD
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the coolness of the patented fabric mainly refers to moisture absorption and perspiration, which cannot serve the purpose of cooling and heat dissipation. Moreover, the fabric is thick and heavy, which is not suitable for light and thin sum

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] An anti-static and heat-dissipating safety protection tooling fabric, the warp and weft yarns are made of the following raw materials in weight percentage: 50% cotton fiber, 50% nylon fiber containing nano-composite ore powder accounting for 6% of the total amount of nylon fiber, wherein nano The composite ore powder is a mixed powder of zirconium silicate and medical stone with a particle size of 30nm, and a commercially available conductive thread is embedded at an interval of 0.5cm between the warp and weft yarns. The warp density of the fabric is 128 threads / inch, and the weft density is 65 threads / inch, the weave is two up and one down twill.

Embodiment 2

[0025] An anti-static and heat-dissipating safety protective tooling fabric, the warp and weft of which are made of the following raw materials in weight percentage: 60% cotton fiber, 40% nylon fiber containing nano-composite ore powder accounting for 25% of the total amount of nylon fiber, wherein nano The composite ore powder is a mixed powder of zirconium silicate and dolomite with a particle size of 80nm, and three composite polyester conductive filaments of 20D carbon black and metal oxide are embedded at an interval of 1.2cm between the warp and weft yarns. The density of the fabric is 132 threads / inch, weft density 75 threads / inch, the weave is two up and one down twill.

Embodiment 3

[0027] An anti-static and heat-dissipating safety protective tooling fabric, the warp and weft of which are made of the following raw materials in weight percentage: 50% cotton fiber, 55% nylon fiber containing nano-composite ore powder accounting for 15% of the total amount of nylon fiber, wherein nano The composite ore powder is a mixed powder of zirconium silicate, dolomite, and magnesium silicate with a particle size of 50nm, and a 20D carbon black and metal oxide composite polyester conductive wire is embedded at an interval of 0.8cm between the warp and weft yarns. The warp density is 130 threads / inch, the weft density is 70 threads / inch, and the weave is two up and one down twill.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses an antistatic radiating safety-protective tooling fabric. Warps and wefts of the fabric are made of, by weight percentage, 50-60% of cotton fiber, and 40-50% of polyamide fiber containing nano composite mineral powder, wherein the nano mineral powder accounts for, by weight percentage, 6-25% of the total weight of the polyamide fiber, one to three conductive wires are inserted between the warps and the wefts every other 0.5-1.2cm, warp density is 128-132/inch, weft density is 65-75/inch, and fabric weave is 2/1 twill. The invention further provides a production method of the fabric, which includes component matching, semi-finished product weaving and dyeing and finishing. The obtained fabric is fast in radiating speed, can create instant cool feel in contact with human skin, and has the advantages of electrostatic prevention, lightness, thinness, environmental friendliness and energy conservation.

Description

technical field [0001] The invention relates to an antistatic heat dissipation safety protective tooling fabric and a manufacturing method thereof. Background technique [0002] In the production of petroleum, petrochemical, chemical, coal, aviation, aerospace, electronics, electric power, medicine, automobile, sanitation, public transportation, cement and other industries, the losses caused by static electricity accidents are very large, which has to arouse people's attention. Pay attention to. There are three main aspects of electrostatic hazards, that is, electrostatic discharge can cause fires and explosions, give people electric shocks and hinder production. Among them, electrostatic discharge causes fire and explosion is the most serious hazard of static electricity. In order to prevent fires and explosions caused by static electricity, we can take the following measures, such as: 1) For factories with fire and explosion hazards, local exhaust or full ventilation can...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D03D15/00D03D13/00D02G3/04D01F6/92D01F1/09D03D15/217D03D15/283D03D15/47D03D15/50D03D15/533
Inventor 陈兆祥
Owner ZHEJIANG LANTIANHAI FAB TECHNOLAGY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap