Manufacturing method of titanium copper compound pot

A production method and composite pot technology, which can be applied in applications, coatings, kitchen utensils, etc., can solve the problems of poor thermal conductivity of titanium, and achieve the effects of strong titanium rigidity, concentrated heat source, and convenient use

Active Publication Date: 2015-04-08
NORTHWEST INSTITUTE FOR NON-FERROUS METAL RESEARCH
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the thermal conductivity of titanium is relatively poor, so it is not ideal to use titanium alone to make pots

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method of titanium copper compound pot
  • Manufacturing method of titanium copper compound pot
  • Manufacturing method of titanium copper compound pot

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] The structure of the titanium-copper composite pot that present embodiment makes is as follows figure 1 As shown, its production method is:

[0039] Step 1. Polish the surface of a pure titanium plate with a thickness of 3mm, and then punch the polished titanium plate to form a pot body 1, and use a conventional metal cleaning agent (purchased from Feitian, Longcheng Chemical Factory, Yantan District, Zigong City, Sichuan Province brand 702 metal cleaning agent) to clean and degrease the pot body 1;

[0040] Step 2. Sandblasting the lower part of the outer surface of the pot body 1 after cleaning and degreasing in step 1 to remove the surface scale, and then paint the outer surface of the pot body 1 and the inner surface of the pot body 1 Conventional insulating glue (purchased from Xi'an Guoyuze Chemical Technology Co., Ltd. S-1 electroplating special peelable protective coating) for insulation protection; The outer surface of the pot body 1, wherein the ratio of the...

Embodiment 2

[0048] The structure of the titanium-copper composite pot that present embodiment makes is as follows figure 2 As shown, its production method is:

[0049] Step 1. Polish the surface of a pure titanium plate with a thickness of 2 mm, and then stamp the polished pure titanium plate to form a pot body 1. Use a conventional metal cleaning agent (purchased from Shanghai Arrow Chemical Co., Ltd. 664 metal cleaning agent) to clean the pot body. Body 1 is cleaned and degreased;

[0050] Step 2. Sandblasting the lower part of the outer surface of the pot body 1 after cleaning and degreasing in step 1 to remove the surface scale, and then paint the outer surface of the pot body 1 and the inner surface of the pot body 1 Conventional insulating glue (plastic electroplating insulating oil 9901) for insulation protection; the lower part of the outer surface of the pot body 1 and the upper part of the outer surface of the pot body 1 constitute the outer surface of the entire pot body 1, w...

Embodiment 3

[0058] The structure of the titanium-copper composite pot that present embodiment makes is as follows image 3 As shown, its production method is:

[0059] Step 1. Polish the surface of a pure titanium plate with a thickness of 1mm, and then punch the polished titanium plate to form a pot body 1, and use a conventional metal cleaning agent (purchased from Feitian, Longcheng Chemical Factory, Yantan District, Zigong City, Sichuan Province brand 702 metal cleaning agent) to clean and degrease the pot body 1;

[0060] Step 2. Sandblasting the lower part of the outer surface of the pot body 1 after cleaning and degreasing in step 1 to remove the surface scale, and then paint the outer surface of the pot body 1 and the inner surface of the pot body 1 Conventional insulating glue (purchased from Xi'an Guoyuze Chemical Technology Co., Ltd. S-1 electroplating special peelable protective coating) for insulation protection; The outer surface of the pot body 1, wherein the ratio of the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a manufacturing method of a titanium copper compound pot; the method comprises the following steps: 1, punching a pure titanium plate to make a pot body; 2, sand blasting the lower part of the outer surface of the pot body and coating insulating gel at the upper part of the outer surface and the inner surface for protection; 3, etching treatment; 4, presoaking nick plating treatment; 5, plating a copper layer; 6, placing the pot body plated with a copper layer in after-treatment solution for soaking treatment; and 7, removing the insulating gel after cleaning, and then mounting a pot handle to obtain the titanium copper compound pot. The invention further discloses another manufacturing method of a titanium copper compound pot; the method comprises the following steps: 1, punching a pure titanium plate to make a pot body; 2, sand blasting the lower part of the outer surface of the pot body and protecting the upper part of the outer surface and the inner surface with a steel die; 3, spraying a copper layer through low-pressure plasma; and 4, polishing, cleaning and mounting a pot handle to obtain the titanium copper compound pot. The titanium copper compound pot manufactured through the methods is firm and durable, can resist corrosion, is light in weight, does not contain nickel, ferrum, aluminium or other undesirable allergic elements, and is suitable for popularization and universalization.

Description

technical field [0001] The invention belongs to the technical field of kitchen cookware, and in particular relates to a manufacturing method of a titanium-copper composite pot. Background technique [0002] A pot is a utensil for cooking food. Since the pot with a single-layer material structure is deformed after being heated, a kitchen utensil with a multi-layer composite material structure has been developed. During the use of the pot, the outer layer of the pot is in contact with high temperature, and the inner layer of the pot is in contact with food. The preparation of the pot is usually made of metal materials. The metal materials used require high strength, good rigidity, good thermal conductivity, high temperature resistance, corrosion resistance, beautiful appearance, and no substances that affect human health when used. Present pot has metal materials such as pig iron, cast iron, steel, stainless steel, aluminum to make, and the physical and chemical properties of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A47J27/00A47J36/02C25D3/38C25D5/38C23C4/12C23C4/08C23C4/134
Inventor 李争显骆瑞雪慕伟意杜继红
Owner NORTHWEST INSTITUTE FOR NON-FERROUS METAL RESEARCH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com