Steam-cured high-performance foam concrete block, production method and application thereof

A foam concrete, high-performance technology, applied in the field of lightweight energy-saving building wall materials, can solve the problems of easy pulverization, low strength, large shrinkage, etc., and achieve the effect of simple production process, good durability and weight reduction

Active Publication Date: 2012-10-24
罗云峰 +2
View PDF1 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to overcome the defects of traditional ordinary foam concrete blocks such as easy pulverization, low strength and large shrinkage, the primary purpose of the present invention is to provide a steam-cured high-performance foam concrete block

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Steam-cured high-performance foam concrete block, production method and application thereof
  • Steam-cured high-performance foam concrete block, production method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A steam-cured high-performance foam concrete block is prepared by the following steps:

[0038] 1) Weigh 1 kg of Henan Huatai HTQ-1 composite foaming agent, add it to the foaming machine, add 40 kg of tap water, and then fully foam with compressed air;

[0039] 2) At the same time, weigh 510kg of cement (P.O42.5R; the same below), 75kg of S95 slag powder, 45kg of sand, 6.3kg of non-slow coagulation carboxylic acid superplasticizer (Guangdong Yuehe HPG-R type; the same below), Add 190kg of water into the mixer and mix and stir, first stir slowly for 0.5min, then stir rapidly for about 1.5min, then add 8kg of curing agent (5.6kg of sodium chloride, 2.4kg of calcium hydroxide), and stir rapidly for 2min to make the slurry uniform;

[0040] 3) Blow the foam that has been foamed in step 1) into the uniformly stirred slurry through compressed air to mix with the slurry, and then stir at a slow speed for about 1.5 minutes to make the slurry a uniform high-performance foam conc...

Embodiment 2

[0044] A steam-cured high-performance foam concrete block is prepared by the following steps:

[0045] 1) Weigh 0.8kg of Henan Huatai HTQ-1 composite foaming agent, add it to the foaming machine, add 35kg of tap water, and then fully foam it with compressed air;

[0046] 2) At the same time, weigh 582kg of cement, 86kg of S95 slag powder, 51kg of sand, 7.3kg of non-slow coagulation carboxylic acid superplasticizer, and 220kg of water, and add them to the mixer for mixing and stirring. First, stir slowly for 0.5 minutes, and then stir rapidly for about 1.5 minutes. Then add 9kg of curing agent (sodium chloride 6.3kg, calcium hydroxide 2.7kg), and then stir rapidly for 2 minutes to make the slurry uniform;

[0047] The remaining steps are the same as Steps 3)-5) of Example 1. The dry density of the obtained steam-cured high-performance foam concrete block is 800kg / m 3 .

Embodiment 3

[0049] A steam-cured high-performance foam concrete block is prepared by the following steps:

[0050] 1) Weigh 0.7kg of Henan Huatai HTQ-1 composite foaming agent, add it to the foaming machine, and add 30kg of tap water to fully foam with compressed air;

[0051] 2) At the same time, weigh 655kg of cement, 96kg of S95 slag powder, 58kg of sand, 8.3kg of non-slow coagulation carboxylic acid superplasticizer, and 250kg of water, and add them to the mixer for mixing and stirring. First, stir slowly for 0.5 minutes, then stir quickly for about 1.5 minutes. Then add 10.0kg of curing agent (sodium chloride 7.0kg, calcium hydroxide 3.0kg), and then stir rapidly for 2 minutes to make the slurry uniform;

[0052] The remaining steps are the same as Steps 3)-5) of Example 1. The dry density of the obtained steam-cured high-performance foam concrete block is 900kg / m 3 .

[0053] Referring to the requirements of "Foam Concrete Block" (JC / T1062-2007), the specific performance indicato...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a steam-cured high-performance foam concrete block which comprises 55-60% of cement, 7-9% of slag powder, 5-8% of sand, 0.5-1.0% of a water reducing agent, 0.88-3% of a curing agent, 0.06-0.3% of a foaming agent and 24-26% of water, wherein the mass of the slag powder is less than 20% of that of the cement which is P.O42.5R cement. According to the foam concrete block, the curing agent is used, so that structural pulverization, collapse of dies and the like are avoided, and the steam-curing effect is improved; water-proof, heat preservation and thermal insulation effects of products are good, and building energy saving is facilitated; the products have good durability and the same service life with a main construction; and the problems of low strength, pulverization, large shrinkage, collapse of dies and the like of low-density foam concrete are solved.

Description

technical field [0001] The invention belongs to the field of lightweight energy-saving building wall materials, and in particular relates to a steam-cured high-performance foam concrete block and its production method and application. Background technique [0002] Traditional ordinary foam concrete blocks generally have defects such as low strength, large shrinkage, and structural pulverization. The main reasons are: (1) The cement grade used in traditional ordinary foam concrete blocks is relatively low, generally 32.5, making Its strength is low, and its shrinkage is also large; (2) Traditional ordinary foam concrete blocks generally do not use high-efficiency water reducers, which makes their water consumption too large, and the water gel is relatively large, resulting in low strength; (3) Traditional Ordinary foam concrete blocks have lower quality requirements for the admixtures used. For example, fly ash is generally required to be grade 3 or lower. The activity of adm...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00
Inventor 罗云峰王劲松肖涛
Owner 罗云峰
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com