Seam binding agent with modified fatty amine as epoxy curing agent resin

An epoxy curing agent, epoxy resin technology, applied in epoxy resin glue, epoxy resin coating, adhesive additive and other directions, can solve the pungent ammonia odor of polyamide, corrosion and yellowing of tank wall, wettability It is not easy to sag, easy to construct, and has strong chemical resistance.

Active Publication Date: 2012-12-12
SKSHU PAINT
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the existing jointing agent, polyamide epoxy resin is generally used as the curing agent, its wettability is not high, and it has a st

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0073] Example 1:

[0074] Component one:

[0075] Component Weight ratio %

[0076] 1. Epoxy resin 35

[0077] 2. Environmentally friendly solvent 2

[0078] 3. Wetting and dispersing agent 0.3

[0079] 4. Quartz sand 15

[0080] 5. Bentonite 3

[0081] 6. Heavy calcium 44.6

[0082] 7. Synthetic fiber 0.1

[0083] Component two:

[0084] 1. Modified fatty amine curing agent 30

[0085] 2. Wetting and dispersing agent 0.3

[0086] 3. Quartz sand 15

[0087] 4. Bentonite 5

[0088] 5. Heavy calcium 49.6

[0089] 6. Synthetic fiber 0.1

[0090] The above-mentioned component one and component two are proportioned by weight as follows:

[0091] Component 1: Component 2 = 2:1.

[0092] The preparation method of the joint agent:

[0093] Disperse the above-mentioned resin, auxiliary agent and environmental protection solvent at medium speed for 5-10 minutes until uniform, then add quartz sand, heavy calcium and bentonite into each powder in turn, and disperse at med...

Example Embodiment

[0095] Embodiment 2:

[0096] Component one:

[0097] Component Weight ratio %

[0098] 1. Epoxy resin 40

[0099] 2. Environmentally friendly solvent 1

[0100] 3. Wetting and dispersing agent 0.3

[0101] 4. Quartz sand 15

[0102] 5. Bentonite 3

[0103] 6. Heavy calcium 40

[0104] 7. Synthetic fiber 0.2

[0105] Component two:

[0106] 1. Modified fatty amine curing agent 32

[0107] 2. Wetting and dispersing agent 0.3

[0108] 3. Quartz sand 15

[0109] 4. Bentonite 5

[0110] 5. Heavy calcium 47.5

[0111] 6. Synthetic fiber 0.2

[0112] The above-mentioned component one and component two are proportioned by weight as follows:

[0113] Component 1: Component 2 = 2:1.

[0114] The preparation method of this imitation metal fluorocarbon paint:

[0115] Disperse the above-mentioned resin, auxiliary agent and environmental protection solvent at medium speed for 5-10 minutes until uniform, then add quartz sand, heavy calcium and bentonite into each powder in ...

Example Embodiment

[0117] Embodiment three:

[0118] Component one:

[0119] Component Weight ratio %

[0120] 1. Epoxy resin 35

[0121] 2. Environmentally friendly solvent 2

[0122] 3. Wetting and dispersing agent 0.3

[0123] 4. Quartz sand 15

[0124] 5. Bentonite 3

[0125] 6. Heavy calcium 44.6

[0126] 7. Synthetic fiber 0.1

[0127] Component two:

[0128] 1. Polyamide curing agent 30

[0129] 2. Wetting and dispersing agent 0.3

[0130] 3. Quartz sand 15

[0131] 4. Bentonite 5

[0132] 5. Heavy calcium 49.6

[0133] 6. Synthetic fiber 0.1

[0134] The above-mentioned component one and component two are proportioned by weight as follows:

[0135] Component 1: Component 2 = 2:1.

[0136] The preparation method of the joint agent:

[0137] Disperse the above-mentioned resin, auxiliary agent and environmental protection solvent at medium speed for 5-10 minutes until uniform, then add quartz sand, heavy calcium and bentonite into each powder in turn, and disperse at medium ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a seam binding agent with modified fatty amine as epoxy curing agent resin. The agent is suitable for easy-cracking positions in indoor and outdoor decorations. The agent is filled into seams of same or different materials such as wood, brick and stone, gypsum board, calcium silicate, and the like, for providing an excellent anti-cracking effect. The agent can also be used as a binding agent for roof leakage repairing, wood, and plastic. The agent can be used in crack sealing and water proofing of various grouting projects, bridges, and tunnels. According to the invention, a novel nano fiber binding technology is adopted. When the product is cured, nano fibers in the product form a high-molecular high-density net-shaped film at a seam position, wherein the physical density of the film is close to that of wood board or gypsum board. The film can expand or contract synchronically with the board when weather is changed, and has good cracking resistance, adhesive force, and flexibility. The seam binding agent is advantaged in fast shaping, easy construction, and low sagging.

Description

technical field [0001] The invention relates to a coating auxiliary material, in particular to an epoxy series auxiliary material using modified aliphatic amine as an epoxy curing agent resin. Background technique [0002] Joint compound is a kind of paint, which is a kind of coating product when decorating objects. As the name suggests, the joint agent is a new type of coating that connects the gaps between objects. The joint agent has strong crack resistance and adhesion, flexibility, strong wear resistance, good water resistance, corrosion resistance, yellowing resistance, color impermeability, It is safe and environmentally friendly, and has excellent accumulation performance, simple construction, and can be quickly shaped after a moderate drying time. It can be dried within 2 hours at room temperature at 20-25°C, and hard-dried for 24 hours. It will reach the best hardness in three days. After drying, a high-density, high-strength mesh coating is formed on the seams. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D163/02C09D7/12C09J163/02C09J11/04C08G59/50
Inventor 刘中华
Owner SKSHU PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap